Thermal Inspection for the Assessment of Adhesively Bonded Metal Adherents

Joseph N Zalameda; Peter W Spaeth; Marc Genest; Matthew Webster; Richard G Cole

Home/Archive/NASA NTRS

NASA NTRS · 20260003245

Thermal Inspection for the Assessment of Adhesively Bonded Metal Adherents

Joseph N Zalameda·Peter W Spaeth·Marc Genest·Matthew Webster·Richard G Cole

View original source ↗Read source document ↗Export metadata ↓

Abstract

Certification of adhesively bonded structures is currently a challenge for aircraft manufacturers. The ability to certify bonds in primary structure can reduce dependence on fasteners and this will enable more efficient manufacturing. For example, drilling holes and installing fasteners in bonded joints can be a potentially significant bottleneck in airframe manufacturing. In addition, fasteners increase the airframe weight and can add stress concentration areas. Reducing fastener count can accelerate manufacturing and improve aircraft performance. NASA is currently investigating nondestructive evaluation (NDE) techniques to assess bond integrity. For example, bond thickness influences bond strength and therefore NDE techniques are being investigated to determine bond thickness. For bonded metal structures, there is a large difference in the thermal diffusivity between the 7075 aluminum alloy metal adherends and aircraft grade adhesive. Multi-layered thermal models show a large variation in the thermal response for bondline adhesive thicknesses that vary from 100 to 300 microns for adherend thicknesses of 0.163 cm. Experimental through-transmission thermal measurements reveal promise to quantitatively characterize the bondline thickness. Results were validated with X-ray computed tomography and optical microscopy measurements, and influence of porosity on the thermal model and measurements are investigated.

Explore related subjects

bondline thickness optical microscopy thermal nondestructive evaluation thermal diffusivity bonded metal adherents porosity X-ray computed tomography

Keep this discovery

BibTeX RIS

Joseph N Zalameda, Peter W Spaeth, Marc Genest, Matthew Webster, Richard G Cole. 2026-04-29. Thermal Inspection for the Assessment of Adhesively Bonded Metal Adherents. https://ntrs.nasa.gov/citations/20260003245

Cite the original work for its findings. Save a collection to share your selection of sources.

Discover connections

Porosity subject Thermal diffusivity subject X-ray computed tomography subject

Connections use source metadata and explicit phrase matches, not verified experimental comparisons.

KEEP EXPLORING

Related reports

NASA NTRS2026

Thermal Inspection for the Assessment of Adhesively Bonded Metal Adherends

X-ray computed tomography↗

NASA NTRS1985

Nondestructive Evaluation of Composites By Optical Time Domain Reflectometry

Results in the measurement of slowly varying mechanical loading functions on composites using optical time domain reflectometry (OTDR) in imbedded optical fiber during both simulated manufacture and use are reviewed. First, the basic theoretical and experimental principles of the OTDR system are described. Next, the mechanical system of the composite and the imbedded fiber is analyzed. Results of measurement obtained for various loading functions applied to material specimens are then described and system limitations on spatial resolution, strain amplitude sensitivity, and frequency response are explained in terms of the range and resolution limits of the OTDR system.

R O Claus↗

NASA NTRS2025

Improving Adhesive Bondline Time of Flight Predictions During Autoclave Cure Utilizing Machine Learning

Composite materials are increasingly being used in aerospace applications due to their superior strength-to-weight ratio compared to commonly used metals. A current limitation to widespread adoption is the certification of adhesively bonded joints. One approach to improving adhesive bonding in composites is accurately measuring the thickness of adhesive bondlines in composite laminates. Precise bondline thickness control is essential for aerospace applications where adhesive layer thickness directly affects joint fracture properties and structural performance. This study focused on implementing machine learning techniques to determine the ultrasonic time of flight (directly correlated to thickness) in adhesive bondlines throughout autoclave cure cycles. A high-temperature (use up to 180°C) ultrasonic scanning system was deployed in an autoclave to provide time of flight data through composite panels. Three experiments were conducted on the curing of 305 mm × 305 mm unidirectional composite panels. In the first experiment, a piecewise function was fit for the temperature correction factor to account for changing autoclave temperatures. Due to deficiencies in the first calibration experiment, a second experiment was run, and the results were used to train a machine learning model. The revised experiment, in combination with the machine learning model, significantly increased the accuracy of the bondline time of flight predictions (~14% error reduced to <1%). Data was processed using the Regression Learner Application in MATLAB®, with a Support Vector Machine selected for the model. The result was a machine learning algorithm capable of reliably quantifying ultrasonic time of flight through adhesive bondlines. The third experiment provided independent test data for the machine learning model, demonstrating that the model produces accurate predictions from data beyond its training set.

Machine Learning↗