Evaluations of Additively Manufactured Superalloy Lattice Blocks

Abstract

Cast lattice block structures made up of high-temperature superalloys were previously shown to offer advantages in density, efficiency, and tailored properties. However, inconsistencies in casting die-fill, composition, and microstructure were identified as persistent issues with the casting process path. Three candidate lattice designs were screened through additive manufacturing of a superalloy. Laser powder bed fusion was applied with superalloy powder to produce lattice blocks for three-dimensional octahedral unit-cell designs of three heights. Properties of the structural designs versus additively manufactured lattices were compared, including structural dimensions, densities, defects, grain structures, crystallographic texture, and surface residual stresses. Findings indicate this concept could produce useful superalloy structures for high-temperature-capable static components requiring tailored density, and thermophysical and mechanical properties.

Explore related subjects

Keep this discovery

BibTeXRIS

Timothy P Gabb, Aaron C Thompson, Christopher A Kantzos, Timothy M Smith, Richard B Rogers, Richard W Rauser, Richard E Martin. Evaluations of Additively Manufactured Superalloy Lattice Blocks. https://ntrs.nasa.gov/citations/20260003085

Cite the original work for its findings. Save a collection to share your selection of sources.

Discover connections

Connections use source metadata and explicit phrase matches, not verified experimental comparisons.

KEEP EXPLORING

Related reports

Evaluation of Superalloy 718 Additively Manufactured Lattice Blocks

Lattice block structures made up of high temperature superalloys could offer advantages in density, efficiency, and tailored properties. Three candidate lattice designs were screened through additive manufacturing of superalloy 718. Laser powder bed fusion was applied with 718 powder to produce lattice blocks for three-dimensional octahedral unit cell designs of three heights. As-designed versus additively manufactured 718 lattices were compared, including structural dimensions, densities, defects, grain structures, crystallographic texture, and surface residual stresses. Manufactured lattice I diverged the most from its design, with both corner and center nodes merged into continuous columns. Manufactured lattice III came closest to its design, though the actual nodes and struts were still larger in cross section than in the design. Only modest grain coarsening and negligible chemical segregation were observed for all three designs, suggesting uniform thermo-physical and mechanical properties are possible. Significant tensile residual stresses were present at the surface of the manufactured blocks, with highest stresses in the building direction. Current findings indicate this concept could produce useful superalloy structures for high-temperature-capable static components requiring tailored density, and thermo-physical/mechanical properties.

super alloys

Influences of Introduced Yttrium Oxide Particles on Superalloy 718

Additive manufacturing has proven useful for introducing oxide particles into superalloys, to provide oxide dispersion strengthening (ODS) at high temperatures. This study screened how such an approach can influence microstructure and failure modes for superalloy 718. The objective of this study was to compare tensile and creep failure modes for additively manufactured superalloy 718 having introduced oxide particles. Fine yttrium-oxide (yttria) particles were introduced into 718 powder using two different powder mixing methods. Additive manufacturing by laser powder bed fusion was then used to prepare specimen blanks for each case, oriented parallel and transverse to the building direction. These were subsequently given consistent stress relief, hot isostatic pressurization, and final heat treatments, then subjected to tensile and creep tests at varied temperatures. Additively manufactured 718 without ODS (“no-ODS”) had nearly equiaxed grains at 50 μm in width. Roll-mixed ODS material had a bimodal grain size distribution, with fine grains at 9 μm and coarse grains at 66 μm in average width. The fine grains were elongated about 5x in the building direction. Acoustic-mixed ODS materials had grains at 10 μm in width that were elongated about 10x in the build direction. Compared to no-ODS, roll-mixed and acoustic mixed ODS materials did not show improved tensile strengths at room temperature, 760 °C, and 1093 °C. The tensile failure strains parallel to the building direction of roll-mixed ODS material were lowest in these tests. Flattened clumps of yttria had formed transverse to the building direction in roll-mixed material, which were easily cracked. Creep rupture response at 760 °C in the building direction was highest for acoustic-mixed material test. Creep tests at 1093 °C showed varied results, with low rupture lives associated with enhanced cavitation at grain boundaries and surface oxidation. Transverse to the building direction, all three materials had low failure strains in tests at 760 °C. The elongated grain boundaries failed readily in all transverse specimens tested at 760 °C and 1093 °C.

oxide dispersion strengthening

Microstructural Evolution and Mechanical Properties of LP-DED NASA HR-1 – A Hydrogen Resistant AM Superalloy for Space Propulsion Applications

The National Aeronautics and Space Administration (NASA) has actively pursued metal additive manufacturing (AM) technologies for spaceflight applications since the late 2000s. AM offers transformative advantages in cost, schedule, part consolidation, and design flexibility. Among the various AM techniques, laser powder directed energy deposition (LP-DED) is particularly well suited for fabricating complex geometries with fine feature resolution. In propulsion systems that utilize high-pressure gaseous hydrogen—such as liquid hydrogen rocket engines—hydrogen environment embrittlement (HEE) presents a serious threat to material performance 1,2 . Mechanical property degradation under these conditions can compromise component reliability, especially under cyclic loading. To address this challenge, NASA developed NASA HR-1 (Hydrogen Resistant-1) as a solution for liquid rocket engine components operating in hydrogen-rich environments, using the LP-DED technique 3-9 . A key component in a liquid rocket engine is the exhaust nozzle, which is typically regeneratively cooled (regen) due to the high heat flux. NASA HR-1 was specifically developed for regen nozzle applications using hydrogen as a propellant, providing resistance to HEE, a critical issue for many materials. The AM version of NASA HR-1 was also formulated to achieve high ultimate tensile strength, along with high yield strength and ductility in this environment 5,6 . Low-cycle fatigue (LCF) is another important consideration in nozzle design, as components are expected to endure multiple starts and missions. Additionally, the LP-DED version of the alloy exhibits improved thermal conductivity compared to its wrought counterpart, which benefits nozzle cooling. Overall, NASA HR-1 offers an excellent balance of high strength, HEE resistance, LCF performance, thermal conductivity, and ductility to meet the demanding requirements of channel-cooled nozzles and other components used with hydrogen and other propellants. The LP-DED–processed NASA HR-1 requires several post-processing heat treatment steps to achieve the material properties desirable for its intended application 6 . These steps include stress relief, homogenization, solution annealing, and aging for precipitation hardening. The stress relief treatment mitigates residual stresses accumulated during the LP-DED process and minimizes the potential for distortion. Homogenization, a common step for AM materials, reduces elemental segregation and promotes recrystallization to develop a more equiaxed grain structure. The subsequent solution annealing treatment heats the part to a solid solution temperature to dissolve the undesirable η-phase that forms during cooling from homogenization, followed by rapid cooling to retain an η-phase–free microstructure. Finally, aging promotes precipitation of the strengthening γ′ phase in the alloy. The integration of compositional design and optimized thermal processing enables high-quality LP-DED NASA HR-1 components with excellent microstructural and mechanical stability. Improved chemical and microstructure homogeneity enhances ductility and fatigue resistance—both critical for safe and reliable operation in high-pressure hydrogen environments. NASA has successfully fabricated and hot-fire tested multiple subscale and full-scale channel wall nozzles using LP-DED NASA HR-1 5,6, 9-14 . These efforts included process refinements to support thin-wall construction and various channel geometries. Throughout development, several key observations emerged. After homogenization, the as-built columnar grain structure transforms into a fully equiaxed microstructure. However, subsequent treatments—such as solution annealing and aging—result in changes that are more difficult to track. The grain structure remains largely unchanged, and the γ′ precipitates, typically 5–10 nm in diameter, are beyond the resolution of scanning electron microscopy (SEM). While transmission electron microscopy (TEM) can resolve these fine precipitates, TEM sample preparation is time-consuming and difficult for LP-DED material. As an alternative, differential scanning calorimetry (DSC) offers a useful, qualitative approach to monitor precipitate evolution throughout different stages of heat treatment. The overall goal is to improve the understanding of how heat treatment affects the microstructure and mechanical performance of LP-DED NASA HR-1. This paper presents heat treatment design considerations, microstructural characterization, mechanical testing – including tensile and LCF testing in both air and hydrogen environments.

Superalloy