Fatigue Life of Flow-Formed Aluminum 2195 and 6061 Alloys

Andrew Boddorff·John Newman·Wesley Tayon·Elizabeth Urig
View original source ↗Read source document ↗Export metadata ↓

Abstract

The successful design and fabrication of metallic cryotanks for commercial aviation applications require lightweight, durable materials capable of withstanding high pressures and cryogenic temperatures through tens of thousands of thermomechanical refueling cycles. Flow forming is an advanced manufacturing technique that offers high-rate production and scalability for fabricating integrally stiffened cylinders suitable for cryotank applications. This work establishes the durability of flow-formed aluminum alloys by characterizing their fatigue life performance under conditions that mimic cryotank refueling cycles. Residual stresses in flow-formed aluminum-lithium (Al-Li) 2195-T6 cylinders were assessed using the contour method and found to be minimal. Fatigue life testing was conducted on flow-formed Al-Li 2195-T6 at room temperature and cryogenic temperatures (-321°F [-196°C]), with wrought Al-Li 2195-T6 serving as a baseline for comparison. Results showed that flow-formed materials exhibited fatigue performance comparable to or better than wrought materials, with no statistically significant differences observed between different specimen orientations relative to processing directions. Fractography revealed reduced delaminations in the flow-formed Al-Li 2195 samples as compared to wrought, indicating potential improvement to the microstructure that could result in improved service properties. Texture analysis using electron backscattered diffraction (EBSD) indicated recrystallization during heat treatment, potentially contributing to reduced delamination susceptibility. These findings demonstrating flow-formed material durability coupled with the high manufacturing efficiency of flow forming, makes flow forming an attractive process to produce aircraft cryotanks.

Explore related subjects

EBF3Additive ManufacturingAutomated Inspection Detection and RepairLaser-wire DED

Keep this discovery

BibTeXRIS

Andrew Boddorff, John Newman, Wesley Tayon, Elizabeth Urig. 2026-03-01. Fatigue Life of Flow-Formed Aluminum 2195 and 6061 Alloys. https://ntrs.nasa.gov/citations/20260001601

Cite the original work for its findings. Save a collection to share your selection of sources.

Discover connections

Additive Manufacturing subjectEBF3 subject

Connections use source metadata and explicit phrase matches, not verified experimental comparisons.

KEEP EXPLORING

Related reports

DOE OSTI2026

Deep Learning and Photogrammetric Reconstruction for Automated Crack Detection and Dimensional Measurement in Mining Operations

Surface crack detection and dimensional measurement at active mining sites present significant safety and operational challenges. Manual inspection methods are labor-intensive, spatially incomplete, and expose personnel to hazardous environments, while existing automated approaches have been developed primarily for concrete civil infrastructure and have not been validated on the complex, variable surfaces characteristic of mining environments. This dissertation presents an automated pipeline that integrates deep learning semantic segmentation with Structure-from-Motion photogrammetry to detect surface cracks and measure their aperture, length, and vertical displacement from standard RGB imagery acquired during routine Uncrewed Aerial Vehicle (UAV) survey operations, without requiring additional sensor hardware or manual measurement. The pipeline combines a U-Net architecture with an EfficientNet-B0 encoder, pretrained on the SDNET2018 concrete crack dataset and fine-tuned on a mining-specific dataset spanning laboratory concrete specimens, coal refuse impoundment embankments, and post-blast limestone quarry benches. Photogrammetric reconstruction is performed using COLMAP Structure-from-Motion and Multi-View Stereo, with crack segmentation masks projected into the reconstructed point cloud to enable three-dimensional vertical displacement measurement through local plane fitting and bimodal surface detection. The pipeline was validated across 36 controlled laboratory specimens at three imaging distances and four vertical displacement levels, achieving aperture measurement RMSE of 0.047 cm and R² of 0.954, and vertical displacement RMSE of 0.140 cm and R² of 0.966, against independent caliper measurements. Field application at a coal refuse impoundment in southwestern Pennsylvania detected 71 crack components across the embankment crest, with a dominant longitudinal crack exhibiting aperture values reaching 28 cm and a 95th percentile vertical displacement of 35.53 cm, consistent in magnitude and spatial distribution with simultaneously acquired LiDAR-derived estimates. Application across four post-blast limestone quarry bench datasets in California successfully characterized blast-induced fracture networks at ground sampling distances ranging from 0.59 to 1.23 cm/pixel, with detected crack geometries physically consistent with observable surface conditions at each site. The results demonstrate that deep learning-based crack detection and photogrammetric measurement can be integrated into routine UAV inspection workflows at mining sites, providing repeatable, scalable, and quantitative crack characterization across surface types, crack scales, and displacement magnitudes not previously addressed in the literature. The pipeline requires no dedicated surveying equipment beyond the UAV platforms already deployed at mine sites for survey and monitoring purposes, supporting practical adoption within existing operational workflows.

Crack detection, Dimensional Measurement↗
NASA NTRS2026

Smart Process Planning for Automated Fiber Placement

Many industries, including aerospace, automotive, wind energy, maritime, and sporting goods, rely on strong, lightweight materials called composites. These materials are made by layering fibers, which can come in the form of narrow strips or wider sheets, and setting them in a polymer matrix. One of the most advanced ways to make these parts is through automated fiber placement, where a machine lays down the fibers in precise patterns. This method can create very efficient and strong designs, but it is complex, expensive, and often depends heavily on the experience of skilled engineers. Today, the design, manufacturing, and inspection stages of composite production are usually handled separately. This separation means that important information, such as how a part will be built or what defects might occur, is not always shared between stages. As a result, parts may not be as lightweight, strong, or defect-free as possible, and the process can take longer and cost more. This research develops a smart process planning system that connects design, manufacturing, and inspection into one continuous process. Built as software that works with existing tools, the system can automatically plan how the fibers are placed, predicting and reducing defects while improving both manufacturability and strength. The system optimizes not only individual layers but also how defects are distributed across all layers, preventing them from stacking up in ways that weaken the final part. It also uses inspection results from completed parts to improve future designs, creating a feedback loop where each stage informs the others. The system was tested by designing a composite panel using this new approach and comparing it to a panel made with state-of-the-art manual planning methods. The results showed that the system could intentionally control where defects appeared and increase the efficiency of the planning process. By unifying design, manufacturing, and inspection, this research shows a way to make advanced composite manufacturing more efficient, consistent, and cost-effective. This approach lowers the barrier to using automated fiber placement and opens the door for its wider adoption not only in aerospace but also in industries such as automotive, wind energy, maritime, and sporting goods, where strong and lightweight structures are essential.

Computer-Aided Process Planning↗