Highly Porous Polyimide Gel for Use as Battery Separator with Room Temperature Ionic Liquid Electrolytes

Abstract

Advanced aerospace vehicular concepts require advances in many existing technologies, including space power and energy storage systems. Batteries represent one of the major areas in need of improvement, both in terms of energy density and safety, with growing concerns over the fire safety of commercial lithium-ion batteries. This has prompted efforts to develop nonflammable battery components, namely the electrolyte and separator. Existing commercial lithium-ion batteries utilize polyolefin microporous membranes as separators with an electrolyte consisting of a lithium salt dissolved in a mixture of cyclic carbonate solvents. This separator/electrolyte combination has ionic conductivities in the range of 10 −2 to 10 −3 S/cm. However, the cyclic carbonate solvents are inherently flammable. Room-temperature ionic liquids (RTILs) appear to be a safer alternative. They offer good ionic conductivities and are inherently nonvolatile and nonflammable, giving them a safety advantage. However, many promising RTILs for battery electrolytes are not compatible with commercial polyolefin separator materials. Alternative separator materials, such as polyimides, are non-flammable and are capable of accepting RTILs into their structure. Polyimide gels, with a composition of 4,4′-oxydianiline, 3,3′,4,4′-tetracarboxylic dianhydride and cross-linked with Desmodur N3300A, possess an open-porous, fibrillar network architecture which offers a high degree of porosity (typically greater than 85% porosity) for lithium-ion transport and conduction, as well as good mechanical properties. Furthermore, these polyimide gels are compatible with selected imidazolium-based RTILs. Nonflammable separator/electrolyte systems with room-temperature conductivities in the range of 10 −3 S/cm have been evaluated. It has been demonstrated that 1-ethyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide was the most promising among six RTILs screened, in terms of both ionic conductivity and constant current cycling.