NASA NTRS · 20200010261
The source did not provide an abstract. Follow the original record for more information.
Cecilia Stoner, Marcia Domack, Eric Hoffman. Characterization of Al Parts Fabricated by Additive Friction Stir (AFS) Manufacturing. https://ntrs.nasa.gov/citations/20200010261
Cite the original work for its findings. Save a collection to share your selection of sources.
KEEP EXPLORING
Friction stir welded (FSW) aluminum blanks offer larger preform sizes than available from the mill in single width plates. Large blanks made from aerospace-grade aluminum alloys are essential for making large domes and cones for launch vehicles and crew vehicles. Previous research efforts have demonstrated >5m FSW blanks can be formed into large domes or cones using spin forming, but the subsequent solution heat treatment consistently led to abnormal grain growth (AGG). The AGG phenomenon occurs because the FSW blanks must be spin formed in the -O annealed temper to withstand the high strain process without cracking. Subsequently, the solution heat treatment process leads to the onset of AGG, whereby a small number of grains grow much larger than the surrounding matrix. Ultimately, the large grains and bimodal grain-size distribution leads to unacceptable ductility in the short-transverse direction of the part. Alternatively, explosive hydroforming is a nascent process that can be applied to large and thick aerospace-grade aluminum alloy blanks in the -T3 temper and only require a post-forming artificial aging process to a -T8. Avoiding the solution heat treatment (SHT) process mitigates AGG, and also eliminates the need for very rare drop-furnace quench baths that can accommodate a part size larger than 5m in diameter. This presentation summarizes a Lockheed Martin-led effort that demonstrated explosive hydroforming of a 1.9m diameter, 39mm thick 2050 aluminum lithium FSW blank. Details will be provided on the process flow, mechanical properties, and metallographic analyses. This work was performed in partnership with NASA Langley Research Center (LaRC) under a NASA Announcement of Collaboration Opportunities program.
Explore the source record for details and available documents.
Friction stir welding and processing (FSW/P) has emerged as an effective solid-state joining technique for fabricating metal matrix composites (MMCs), offering improved mechanical properties through refined microstructural evolution. In this study, an aluminum-boron nitride nanoparticle (Al-BNNP) composite was synthesized via FSW, and its indentation-based mechanical properties were systematically evaluated. Microhardness mapping across the weld cross-section revealed a progressive increase in hardness toward the stir zone (SZ), attributed to severe plastic deformation, dynamic recrystallization (DRX), and the reinforcing effect of BNNPs. Profilometry-based indentation plastometry (PIP) inferred yield strength (YS) demonstrates a 47.8% increase compared to the base metal (BM) and a 75% improvement compared to FSP pure aluminum reported in literature. This enhancement is attributed to strengthening mechanisms, including grain boundary pinning, load transfer, and increased dislocation density. The strain rate sensitivity (SRS) measurements at the nanoscale demonstrated a substantial decrease in the SZ, correlated with ultrafine grain structures and strong BNNP-matrix interactions. Activation volume analysis revealed a significant reduction in the SZ, suggesting that dislocation motion is increasingly restricted by dislocation-dislocation and dislocation-particle interactions. These findings suggest that incorporating BNNPs in FSW/P enables tailoring the microstructure without thermal degradation of the secondary particles, thereby significantly enhancing the mechanical performance of aluminum composites, particularly for structural applications in aerospace and automotive industries.