NASA NTRS · 20140010325
No abstract available
Explore connections, maps & timelines
Calle, Luz Marina, Russell, Rick, Li, Wenyan, Buhrow, Jerry, Jolley, Scott. 2014-06-16. A Multifunctional Smart Coating for Autonomous Corrosion Control. https://ntrs.nasa.gov/citations/20140010325
Cite the original work for its findings. Save a collection to share your selection of sources.
KEEP EXPLORING
Environmental barrier coatings (EBC) are an enabling technology for the successful application of ceramic matrix composites (CMCs) in air-breathing gas turbine engines. EBCs are susceptible to several failure modes including oxidation/delamination, recession, chemical attack and dissolution, thermomechanical degradation, erosion, and foreign object impact damage in a combustion environment. Spallation of environmental barrier coating (EBC), induced by a thermally grown oxide (TGO) layer, is a key EBC failure mode. The TGO layer, resulting from steam oxidation, grows either from a silicon bond coat layer (if present) or from a silicon carbide (SiC) based substrate itself. The TGO layer evolves (i.e., thickness increases with time) as water vapor and oxygen gradually diffuse through the EBC, and the EBC spalls off once the TGO layer reaches some critical thickness. The critical thickness of the TGO layer for failure is in the range of 20-30 microns, with the actual value depending upon exposure temperature, microstructure, etc. Current work at NASA Glenn Research Center, under the Transformative Tools and Technology (TTT) subproject is aimed at addressing associated failure modes in EBC systems and developing robust analysis tools to aid in the design/analysis of these systems. The objective of the current work is to conduct a sensitivity study to examine the influence of uniformly and non-uniformly grown oxide layers on the associated driving forces leading to spallation of the EBC when subjected to isothermal loading. The effect of damage in the TGO layer on the resulting stress states is also assessed both in uniform and non-uniform TGO layers.
Materials for advanced turbine engines are expected to have temperature capabilities in the range of 1370-1500C. At these temperatures the ingestion of sand and dust particulate can result in the formation of corrosive glass deposits referred to as CMAS. The presence of this glass can both thermomechanically and thermochemically significantly degrade protective coatings on metallic and ceramic components. Plasma Spray- Physical Vapor Deposition (PS-PVD) was used to deposit advanced environmental barrier coating (EBC) systems for investigation on their interaction with CMAS compositions. Coatings were exposed to CMAS and furnace tested in air from 1 to 50 hours at temperatures ranging from 1200-1500C. Coating composition and crystal structure were tracked with X-ray diffraction and microstructure with electron microscopy.