Processing Robustness for A Phenylethynyl Terminated Polyimide Composite

Abstract

The processability of a phenylethynyl terminated imide resin matrix (designated as PETI-5) composite is investigated. Unidirectional prepregs are made by coating an N-methylpyrrolidone solution of the amide acid oligomer (designated as PETAA-5/NMP) onto unsized IM7 fibers. Two batches of prepregs are used: one is made by NASA in-house, and the other is from an industrial source. The composite processing robustness is investigated with respect to the prepreg shelf life, the effect of B-staging conditions, and the optimal processing window. Prepreg rheology and open hole compression (OHC) strengths are found not to be affected by prolonged (i.e., up to 60 days) ambient storage. Rheological measurements indicate that the PETAA-5/NMP processability is only slightly affected over a wide range of B-stage temperatures from 250 deg C to 300 deg C. The OHC strength values are statistically indistinguishable among laminates consolidated using various B-staging conditions. An optimal processing window is established by means of the response surface methodology. IM7/PETAA-5/NMP prepreg is more sensitive to consolidation temperature than to pressure. A good consolidation is achievable at 371 deg C (700 deg F)/100 Psi, which yields an RT OHC strength of 62 Ksi. However, processability declines dramatically at temperatures below 350 deg C (662 deg F), as evidenced by the OHC strength values. The processability of the IM7/LARC(TM) PETI-5 prepreg was found to be robust.