NASA NTRS · 20060039552
A novel method of forming nested fullerenes by irradiation of carbon soot using the high energy beam in a 300-kV electron microscope.
Explore connections, maps & timelines
Anderson, M.. 1993-01-01. Nested Fullerenes on Graphite. https://ntrs.nasa.gov/citations/20060039552
Cite the original work for its findings. Save a collection to share your selection of sources.
KEEP EXPLORING
The large mass, low first ionization potential and large electron impact ionization cross-section make Buckminsterfullerene (carbon 60) potentially attractive as an ion engine propellant. It has the potential for significant increases in engine efficiency over that obtained with xenon at specific impulses less than 3 000 s. One problem encountered in fullerene ion engines has been dissociation of the propellant. Previously this was attributed to thermal decomposition due to operation of the ion engine at temperatures greater than 1073 K. However, during tests conducted at temperatures lower than 1073 K fullerene fragmentation was still observed. This prompted an investigation to determine if the dissociation was still due to thermal effects or if it was due to collisional processes in the discharge chamber.
Several reports of successful operation of DC discharges using fullerene vapor have been made. However, degradation of the propellant molecules in the vapor source and in contact with the filament cathode was observed in each case. Because disintegration of the fullerene cage could result in poor performance or thruster failure, we have developed an RF ion thruster for use with C 60 propellant to avoid the presence of electrodes inside the discharge chamber. Also, we conducted a series of experiments to ascertain the stability of fullerenes at high temperatures. We find that when C 60 and C 70 are maintained at temperatures above 1073 K, or are exposed to hot metal surfaces, significant degradation occurs. We find an activation energy of 261.5 kJ/mol for this process. At temperatures below 873 K, no breakdown of fullerenes can be detected, even after heating for 6 hours. The effect of these findings on C 60 ion thruster design is discussed.
Because vapor phase fullerene molecules collide with high temperature surfaces at both the cathode in DC discharges and at the walls of vapor sources, knowledge of the thermal stability and material compatibility of fullerenes is important for ion thruster applications. Here, we present a study of the high temperature behavior of fullerenes. We find that when C 60 and C 7O are maintained at temperatures above 1073 K, or are wxposed to hot metal surfaces, significant degradation occurs. We find an activation energy of 261.5 kJ/mol for this process. At temperatures below 873 K, no breakdown of fullerenes can be detected, even after heating for 6 hours. The effect of these findings on C 60 ion thruster design is discussed. Our present C 60 ion thruster experiment is also described.