A High Temperature Cyclic Oxidation Data Base for Selected Materials Tested at NASA Glenn Research Center

Charles A Barrett

Home/Archive/NASA NTRS

NASA NTRS · 20030093726

A High Temperature Cyclic Oxidation Data Base for Selected Materials Tested at NASA Glenn Research Center

Charles A Barrett

View original source ↗Read source document ↗Export metadata ↓

Abstract

The cyclic oxidation test results for some 1000 high temperature commercial and experimental alloys have been collected in an EXCEL database. This database represents over thirty years of research at NASA Glenn Research Center in Cleveland, Ohio. The data is in the form of a series of runs of specific weight change versus time values for a set of samples tested at a given temperature, cycle time, and exposure time. Included on each run is a set of embedded plots of the critical data. The nature of the data is discussed along with analysis of the cyclic oxidation process. In addition examples are given as to how a set of results can be analyzed. The data is assembled on a read-only compact disk which is available on request from Materials Durability Branch, NASA Glenn Research Center, Cleveland, Ohio.

Explore related subjects

Scale Spalling Models Data Base Cyclic Oxidation High Temperature Alloys

Keep this discovery

BibTeX RIS

Charles A Barrett. 2003-09-01. A High Temperature Cyclic Oxidation Data Base for Selected Materials Tested at NASA Glenn Research Center. https://ntrs.nasa.gov/citations/20030093726

Cite the original work for its findings. Save a collection to share your selection of sources.

Discover connections

Cyclic Oxidation subject Data Base subject Scale Spalling Models subject

Connections use source metadata and explicit phrase matches, not verified experimental comparisons.

KEEP EXPLORING

Related reports

NASA NTRS2000

Chalcogenide-Based Non-Volatile Memory Technology

Chalcogenide is a proven phase change material used in re-writeable CDs and DVDs. This material changes phases, reversibly and quickly, between an amorphous state that is dull in appearance and electrically high in resistance, and a polycrystalline state that is highly reflective and low in resistance. The application of this commercially proven technology to create dense, high-speed, non-volatile semiconductor memories is discussed.

J Maimon↗

NASA NTRS1995

Effect of Turbulence Models on Criticality Conditions in Swirling Flows

The critical state of vortex cores downstream of vortex breakdown has been studied. Base vortical flows were computed using the Reynolds-averaged, axisymmetric Navier-Stokes equations. Standard K - epsilon , RNG and second-order Reynolds stress models were employed. Results indicate that the return to supercriticality is highly dependent on the turbulence model. The K - epsilon model predicted a rapid return of the vortex to supercritical conditions, the location of which showed little sensitivity to changes in the swirl ratio. The Reynolds stress model predicted that the vortex remains subcritical to the end of the domain for each of the swirl ratios employed, and provided results in qualitative agreement with experimental work. The RNG model produced intermediate results, with a downstream movement in the critical location with increasing swirl. Calculations for which area reductions were introduced at the exit in a subcritical flow were also performed using the Reynolds stress model. The structure of the resulting recirculation zone was altered significantly. However, when area reductions were employed within supercritical flows as predicted using the two-equation models, no significant influence on the recirculation zone was noted.

Robert E Spall↗

NASA NTRS1994

Thermal Testing of High Performance: Thermal Barrier Coatings for Turbine Blades

A 350 micron thick 7 wt.% Y 2 O 3 -ZrO 2 (7YSZ) ceramic Thermal Barrier Coating (TBC) was manufactured in an argon atmosphere and with a strictly controlled substrate temperature on flat IN 600 samples and on IN 100 aircraft turbine blades. This new atmosphere and temperature controlled spraying (ATCS) allows the reduction of the residual stresses and an improvement in the microstructure and in the mechanical properties of the coating. The good performance of these new TBC's was assessed in thermal fatigue and in thermal shock tests carried out in air at 1100°C and at 1280°C respectively. The oxidation rate of the metal-ceramic interface was measured at 1100°C. Failure of the TBC's was induced only by the deterioration (like oxidation, cracking, ...) of the uncoated parts of the samples, as testing temperature was too severe for the base metals. Spalling was thereafter driven by compressive stresses near the aluminum oxide layer at the metal-ceramic interface. The results of these tests underline the good quality of the ceramic coating manufactured by the new ATCS technology.

L Bertamini↗