X-Ray Absorption Spectroscopy in High Temperature Oxidation of Metals and Alloys

Daniele Gozzi·Massimo Tomellini
View original source ↗Export metadata ↓

Abstract

An experimental technique is described that allows for the joint study of the kinetics and of the oxide structure during the high temperature oxidation of metal surfaces. Oxygen is supplied at the metal through an electrochemical oxygen pump and the oxygen pressure, at the metal surface, is measured during oxidation by a YSZ (yttria stabilized zirconia) oxygen sensor. XAS (x-ray absorption spectroscopy) is performed in fluorescence mode at the cation K edge and after each oxidation step. An appropriate analysis of the XAS spectra could provide information on both the oxidation kinetics and oxide structure. Experimental data on the high temperature oxidation of nickel, cobalt, and Fe(64%)Ni(36%) alloy, at low oxygen pressure, are reported and analyzed according to the proposed data reduction. These results indicate the presented technique to be particularly suitable for studying the hot corrosion of oxide film too thick for common surface spectroscopy (AUGER, ESCA) and too thin for conventional thermogravimetric technique.

Keep this discovery

BibTeXRIS

Daniele Gozzi, Massimo Tomellini. 1994-11-01. X-Ray Absorption Spectroscopy in High Temperature Oxidation of Metals and Alloys. https://ntrs.nasa.gov/citations/19950013266

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

DOE OSTI2023

Speciation of Transition Metal Dissolution in Electrolyte from Common Cathode Materials

Significant capacity loss has been observed across extended cycling of lithium-ion batteries cycled to high potential. One of the sources of capacity fade is transition metal dissolution from the cathode active material, ion migration through the electrolyte, and deposition on the solid-electrolyte interphase on the anode. While much research has been conducted on the oxidation state of the transition metal in the cathode active material or deposited on the anode, there have been limited investigations of the oxidation state of the transition metal ions dissolved in the electrolyte. Here, in this work, X-ray absorption spectroscopy has been performed on electrolytes extracted from cells built with four different cathode active materials (LiMn 2 O 4 (LMO), LiNi 0.5 Mn 1.5 O 4 (LNMO), LiNi 0.8 Mn 0.1 Co 0.1 O 2 (NMC811), and (x Li 2 MnO 3 *(1-x) LiNi a Mn b Co c O 2 , with a+b+c=1) (LMRNMC)) that were cycled at either high or standard potentials to determine the oxidation state of Mn and Ni in solution. Inductively coupled plasma-mass spectrometry has been performed on the anodes from these cells to determine the concentration of deposited transition metal ions. While transition metal ions were found dissolved in all electrolytes, the oxidation state(s) of Mn and Ni were determined to be dependent on the cathode material and independent of cycling potential.

25 ENERGY STORAGE↗
DOE OSTI2024

Lanthanum-Promoted Electrocatalyst for the Oxygen Evolution Reaction: Unique Catalyst or Oxide Deconstruction?

A conventional performance metric for electrocatalysts that promote the oxygen evolution reaction (OER) is the current density at a given overpotential. However, the assumption that increased current density at lower overpotentials indicates superior catalyst design is precarious for OER catalysts in the working environment, as the crystalline lattice is prone to deconstruction and amorphization, thus greatly increasing the concentration of catalytic active sites. We show this to be the case for La 3+ incorporation into Co 3 O 4 . Powder X-ray diffraction (PXRD), Raman spectroscopy and extended X-ray absorption fine structure (EXAFS) reveal smaller domain sizes with decreased long-range order and increased amorphization for La-modified Co 3 O 4 . This lattice deconstruction is exacerbated under the conditions of OER as indicated by operando spectroscopies. The overpotential for OER decreases with increasing La 3+ concentration, with maximum activity achieved at 17% La incorporation. HRTEM images and electron diffraction patterns clearly show the formation of an amorphous overlayer during OER catalysis that is accelerated with La 3+ addition. O 1s XPS spectra after OER show the loss of lattice-oxide and an increase in peak intensities associated with hydroxylated or defective O-atom environments, consistent with Co(O) x (OH) y species in an amorphous overlayer. Furthermore, our results suggest that improved catalytic activity of oxides incorporated with La 3+ ions (and likely other metal ions) is due to an increase in the number of terminal octahedral Co(O) x (OH) y edge sites upon Co 3 O 4 lattice deconstruction, rather than enhanced intrinsic catalysis.

Catalysts↗