High Velocity Oxygen Fuel Spraying of Erosion and Wear Resistant Coatings on Jet Engine Parts

A T J Verbeek

View original source ↗Export metadata ↓

Abstract

High velocity oxygen fuel (HVOF) spraying is the most recent development in the field of thermal spraying. The importance of this technique for the repair and new part manufacturing of jet engine parts is rapidly increasing. The HVOF uses a supersonic oxygen-fuel flame to heat and accelerate the powder particles that form the coating. The high particle velocity results in a high density and a low porosity, a high bond strength, and a high macro and micro hardness of the coating. The high quality of the HVOF coatings makes it possible to use these coatings on high loaded, rotating parts in jet engines. This paper will highlight the use of HVOF processes to apply erosion resistant cermet coatings to high pressure compressor blades. These blades are exposed to severe erosion. Next to the D-gun process, HVOF spraying is the only nonproprietary technique that can be used to apply these high performance coatings. Also the use of the HVOF process to apply wear resistant coatings and superalloys to jet engine parts will be discussed. The difference between HVOF coatings and plasma sprayed coatings will be highlighted. During HVOF spraying, the parts are exposed to a high heat flow. Solutions to avoid overheating, especially of titanium parts, will be presented.

Keep this discovery

BibTeX RIS

A T J Verbeek. 1994-11-01. High Velocity Oxygen Fuel Spraying of Erosion and Wear Resistant Coatings on Jet Engine Parts. https://ntrs.nasa.gov/citations/19950013264

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

DOE OSTI2026

Feasibility of Nitrogen as a Carrier Gas for Inconel Cold Spray in Hydropower Application

Cold spray deposition of Inconel nickel alloys has emerged as a promising strategy for mitigating cavitation erosion in hydropower facilities. Most prior developments employ helium (He) as the carrier gas because it enables high particle velocities and the formation of dense coatings. However, He is nearly two orders of magnitude more expensive than nitrogen (N2), which limits its widespread adoption in the hydropower sector. Although He-based cold spray can be justified for high value repairs, the lower cost and broad availability of N2 make it an attractive alternative. This study assesses the feasibility of N2-based cold spray of Inconel 625 powders for hydropower applications. Cavitation erosion testing shows that He-based coating exhibits cavitation resistance of ~398% relative to the 304L stainless steel (SS304L) substrate. In contrast, N2-based coating shows substantially lower cavitation resistance, reaching only ~69% of the SS304L substrate, even when higher carrier gas temperature and pressure are applied. When the Inconel 625 powder size is reduced from 44 to 22 µm under N2-based cold spray conditions, cavitation resistance increases significantly to ~148% of the SS304L substrate. Additional improvement can be obtained by incorporating fine chromium carbide powders into the feedstock, resulting in cavitation resistance of ~172% of the SS304L substrate. Overall, with optimized feedstock design, N2-based cold spray offers a practical and cost-effective approach for producing cavitation resistant coatings on hydropower components, although He-based cold spray continues to deliver higher cavitation resistance.

Wang, Tianhao↗

NASA NTRS2025

Erosion Behavior of Ti-hBN Multifunctional Coatings in A Custom-Made Planetary Test Rig at Extreme Lunar Temperatures

Spacecraft landings and takeoffs on the lunar surface, along with extreme temperature variations between day and night (-196 to 150° C), cause high-velocity dust impacts and erosion, resulting in the premature failure of structures. Ti/2 vol% hBN coatings were deposited using atmospheric (APS) and vacuum plasma spray (VPS) using cryo-milled powder feedstock to protect the structural components. The erosion performance of coatings at extreme lunar temperature regimes (-150 to 150° C) was evaluated in a custom-made planetary erosion test rig (PETR) at low (50 mph) and high impact velocities (250 mph). The mass loss of VPS coatings was reduced by 50% compared to the APS coatings and 40% compared to the Ti6Al4V substrate. The cryogenic temperature induces brittleness in the material, rendering it susceptible to extreme conditions of material loss. The particle impact-deformation behavior was captured using a high-speed camera to study the erosion mechanism. This analysis revealed chipping in substrates and brittle APS coatings, while particles rebounding and embedding were observed in VPS coatings. Energy calculations, aided by particle trajectory tracking from the high-speed camera, have conclusively shown that VPS coatings absorb 5–10% more energy than APS coatings during erosion tests. A modified erosion index was developed incorporating the fracture toughness and temperatures. New erosion models for brittle and ductile target materials are proposed for developing erosion-resistant material systems.

Abhijith Kunneparambil Sukumaran↗

NASA NTRS2025

Radiation-Resistant Ti/BN Coatings: Insights From 171 Days Exposure to Space Radiation and Atomic Oxygen in Low Orbit

Atmospheric Plasma Spray (APS) and Vacuum Plasma Spray (VPS) techniques were used to develop Ti/2 vol.% hBN coatings, for extreme space environments and tested aboard the International Space Station as part of the MISSE-17 (Materials International Space Station Experiments) program. The coatings were exposed to atomic oxygen, space radiation, and low-orbit thermal cycling. VPS coatings showed a 56% increase in microhardness, a 26% rise in elastic modulus, minimal porosity and crack density changes compared to APS coatings. The change in mechanical properties is attributed to the formation of TiO, TiO₂ and TiN from nitrogen retention, alongside radiation-induced dislocations, which enhanced surface hardening. The oxidation of titanium led to the formation of TiO and TiO₂, while boron nitride was retained and underwent transmutation in VPS coatings. XPS and EDS analyses confirmed the enhanced space-environment resistance of VPS coatings, making them ideal for long-term spacecraft protection in lunar and Martian conditions.

Abhijith Kunneparambil Sukumaran↗