Mechanical properties of glasses impacted by debris or micrometeorites

Donald L. Kinser; David E. Wiedlocher

Home/Archive/NASA NTRS

NASA NTRS · 19920018004

Mechanical properties of glasses impacted by debris or micrometeorites

Donald L. Kinser·David E. Wiedlocher

View original source ↗Export metadata ↓

Abstract

Mechanical strength measurements on five glasses and one glass ceramic exposed on the Long Duration Exposure Facility (LDEF) have revealed no damage exceeding experimental limits of error after exposure. The measurement technique subjected less than 5 percent of the sample surface area to stresses above 90 percent of the failure strength. Seven micrometeorite or space debris impacts occurred at locations which were not in that portion of the sample subjected to greater than 90 percent of the applied stress. In consequence of this, the impact events on the sample were not detected in mechanical strength measurements. The physical form and structure of the impact sites was carefully examined to determine the influence of those events upon stress concentration associated with the impact and the resulting mechanical strength influence. The size of the impact site insofar as it determines flaw size for fracture purposes was examined. Surface topography of the impacts reveals that six of the seven sites display impact melting. The classical melt crater structure is surrounded by a zone of fractured glass. Residual stresses arising from shock compression and from cooling of the impact fused zone cannot be included in fracture mechanics analyses based on simple flaw size analyses. Strategies for refining estimates of mechanical strength degradation by impact events are presented.

Keep this discovery

BibTeX RIS

Donald L. Kinser, David E. Wiedlocher. 1992-06-01. Mechanical properties of glasses impacted by debris or micrometeorites. https://ntrs.nasa.gov/citations/19920018004

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

DOE OSTI2026

Boron Coordination in Multicomponent Glasses: Analytical Models and Machine Learning With Uncertainty

Borosilicate glasses are extensively used in a variety of applications from kitchenware to nuclear waste immobilization due to the strong network formed by the Si-O-B bond that makes it resistant to chemical corrosion and gives it a low thermal expansion. Boron, however, exists in both trigonal BO3 and tetrahedral BO4 bonds in glass systems, which impacts the chemical durability and thermal resistance of the glass, amongst other properties. Boron coordination (N4), or the ratio of the amount of BO4 to BO3 within a glass, may aid in predicting these properties but is difficult to derive without experimental data due to the complexity of impacts from varied glass compositions and processing factors. For this reason, compositional models have been developed to predict boron coordination, but the models typically include a limited number of glass components. To help fill this gap in the models, in this work, a diverse multicomponent glass dataset of 809 glasses is compiled from a literature search, and then a number of analytical and machine learning (ML) models are trained on the dataset. Previously developed modified Bernstein and modified Du Stebbins analytical models were fitted to update parameters with the new dataset. Then, partially Bayesian neural networks, Gaussian process regressor, and heteroskedastic deterministic neural networks were evaluated. The ML models examined all have different strategies to overcome the potential for overfitting as a result of a limited training dataset, and return results that account for model uncertainty, which can be valuable for understanding model reliability. For the first time, cooling rate is introduced as an input parameter for ML models, showing consistent improvements in performance and solidifying the importance of including parameters outside of composition alone for N4 prediction. The machine learning models examined here show promise in accurate predictions of boron coordination in borosilicate glasses, all achieving R2 values of 0.91.

boron coordination↗

NASA NTRS1992

LDEF experiment M0003 meteoroid and debris survey

A survey of the meteoroid and space debris impacts on LDEF experiment M0003 was performed. The purpose was to document impact phenomenology and to obtain impact crater data for comparison to current debris and micrometeoroid models. The survey consists of photomicrographs of significant impacts in a variety of material types, accurate measurements of impact crater coordinates and dimensions for selected experiment surfaces and data basing of the crater data for reduction, manipulation, and comparison models. Large area surfaces which were studied include the experiment power and data system sunshields, environment exposure control canister sunshields, and the M0003 signal conditioning unit covers. Crater diameters down to 25 microns were measured and catalogued. Both leading and trailing edge surfaces were studied and compared. The results shows the different response of materials to hypervelocity impacts. Comparison of the data to curves derived from the Kessler debris model and the Cour-Palais micrometeoroid model indicates a marked tendency for overprediction of small impacts and underprediction of large impacts with there being better agreement for the medium sized impacts. Representative impact data is presented.

M. J. Meshishnek↗

NASA NTRS1992

Analysis of LDEF micrometeoroid/debris data and damage to composite laminates

A nomogram based on the number/distribution of micrometeoroid/debris hits recorded on the Long Duration Exposure Facility (LDEF) is presented. The nomogram permits the user to estimate the total number of impacts that a space structure would encounter as a function of time in orbit, exposed area, and angular location associated with the LDEF. Examples are presented on the application of the nomogram to satellites and space structures of different cross-sections to that of the LDEF. The effects of altitude and orbit inclination are also discussed. To further demonstrate the usefulness of this nomogram, results are compared to impact data measured on the UTIAS polymer matrix composite experiment (AO180). The impact damage occurring on these composite materials is examined, and data on hole size, penetration depth, and delamination area are presented.

R. C. Tennyson↗