Thrust Chamber Thermal Barrier Coating Techniques

Richard J Quentmeyer
View original source ↗Export metadata ↓

Abstract

Methods for applying thermal barrier coatings to the hot-gas side wall of rocket thrust chambers in order to significantly reduce the heat transfer in high heat flux regions has been the focus of technology efforts for many years. A successful technique developed by NASA-Lewis that starts with the coating on a mandrel and then builds the thrust chamber around it by electroforming appropriate materials is described. This results in a smooth coating with exceptional adherence, as was demonstrated in hot fire rig tests. The low cycle fatigue life of chambers with coatings applied in this manner was increased dramatically compared to uncoated chambers.

Keep this discovery

BibTeXRIS

Richard J Quentmeyer. 1989-03-01. Thrust Chamber Thermal Barrier Coating Techniques. https://ntrs.nasa.gov/citations/19890013300

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

NASA NTRS1994

New Trends in Coatings Developments for Turbine Blades: Materials Processing and Repair

Turbine engines for aeronautic applications now have to face strenuous requirements concerning not only operating performances but also reliability and repairability. This evolution of the specifications induces important consequences regarding the choice and the design of turbine blade protective coatings. This paper presents several key features concerning the deposition techniques and the real-life behavior of such coatings: (1) complex aluminides well suited to the protection against high temperature oxidation and hot corrosion of directionally solidified nickel-base superalloy turbine blades; (2) ceramic coatings used as thermal barriers - they have to exhibit both high resistance to thermomechanical fatigue and adequate smoothness; (3) processing techniques for thermal barriers, including plasma spraying, electron beam physical vapor deposition and plasma enhanced chemical vapor deposition; and (4) blades and coatings repair techniques.

S Alpérine↗
NASA NTRS1994

Thermal Testing of High Performance: Thermal Barrier Coatings for Turbine Blades

A 350 micron thick 7 wt.% Y 2 O 3 -ZrO 2 (7YSZ) ceramic Thermal Barrier Coating (TBC) was manufactured in an argon atmosphere and with a strictly controlled substrate temperature on flat IN 600 samples and on IN 100 aircraft turbine blades. This new atmosphere and temperature controlled spraying (ATCS) allows the reduction of the residual stresses and an improvement in the microstructure and in the mechanical properties of the coating. The good performance of these new TBC's was assessed in thermal fatigue and in thermal shock tests carried out in air at 1100°C and at 1280°C respectively. The oxidation rate of the metal-ceramic interface was measured at 1100°C. Failure of the TBC's was induced only by the deterioration (like oxidation, cracking, ...) of the uncoated parts of the samples, as testing temperature was too severe for the base metals. Spalling was thereafter driven by compressive stresses near the aluminum oxide layer at the metal-ceramic interface. The results of these tests underline the good quality of the ceramic coating manufactured by the new ATCS technology.

L Bertamini↗