Improved processing of alpha-SiC

Abstract

Dry pressing/sintering, slurry pressing/sintering, and hot isostatic pressing have been investigated with a view to developing an optimum processing technique to produce high-strength SiC for high-temperature structural applications. A baseline strength of 348 MPa was achieved by dry pressing and sintering. When slurry pressing was used to minimize agglomerates in the powder, a baseline strength of 428 MPa was obtained. An additional improvement in strength (655 MPa) was obtained by hot isostatic pressing, which prevented the formation of critical flaws resulting from residual agglomerates in the powder. It is expected that surface finish, such as lapping, polishing, and heat treatment, may further improve the strength and Weibull modulus of hot isostatically pressed alpha-sic.