Strength optimization of alpha-SiC by improved processing

Abstract

Silicon carbide is of great interest for structural use in aircraft and automobile engines. This ceramic combines high thermal conductivity and low coefficient of thermal expansion, and consequently has good thermal shock resistance. However, like other ceramics, silicon carbide shows strength variability due to processing flaws such as large voids, shrinkage cracks, and inclusions. Agglomerates in the starting powder seem to be the predominant cause of such defects. Improved processing techniques such as slurry pressing and hot isostatic pressing (HIP) were employed to minimize these defects and to improve strength and reliability in the fabricated material. For this purpose 2-inch diameter disks were fabricated by various consolidation techniques. These include: dry pressing and sintering, slurry pressing and sintering, and slurry pressing and HIPing. The results are discussed.