J series thruster isolator failure analysis

Abstract

Three Hg propellant isolators (two cathode and one main) failed during testing in the Mission Profile Life Test. These failures involved contamination of the surface of the alumina insulating body which resulted in heating of the vaporizer by leakage current from the high voltage supply, with subsequent loss of propellant flow rate control. Failure analysis of the isolators showed the surface resistance was temperature dependent and that the alumina could be restored to its original insulating state by grit blasting the surface. The contaminant was identified as carbon and the most likely sources identified as ambient facility hydrocarbons, directed back-sputtered facility materials, and outgassing from organic insulating materials within the thruster envelope. Methods to eliminate contamination from each of these sources are described.