Space stable thermal control coatings

Abstract

A specification quality zinc orthotitanate coating was developed. This silicate-bonded Zn2TiO4 coating is discussed. The effects of precursor chemistry, precursor mixing procedures, stoichiometry variations, and of different heat treatments on the physical and optical properties of Zn2TiO4 are investigated. Inorganic silicates are compared to organic silicone binder systems. The effects of pigment to binder ratio, water content, and of different curing procedures on the optical and physical properties of Zn2TiO4 potassium silicate coatings are also studied. Environmental tests were conducted to determine the UV vacuum stability of coatings for durations up to 5000 equivalent Sun hours.