Intermetallics as alternative materials

Abstract

Aluminum containing intermetallics have B2 cubic crystal structures, exist over a wide range of composition, have large solubilities for third element alloying additions, are capable of both low and high temperature plastic flow, and have very high melting temperatures (approximately 1900 K) except for FeAl. The slow strain rate elevated temperature properties of Fe, Ni, and Co aluminides are investigated. Because of the reported difficulties with traditional melting/casting methods, sound polycrystalling materials are fabricated by hot extrusion of steel canned blended prealloyed powders. These binary aluminides are used to develop base line elevated temperature mechanical properties as well as an understanding of the factors which affect/control the strength and ductility.