Sintered plaque characteristics

Abstract

The structural transformations occurring during sintering, the fabrication of a slurry produced sintered plaque, are detailed. Degradation of the positive electrode in performance in cycling in a nickel hydrogen battery were traced to the quality of the sintered plaque. Electrode degradation was found to be a limiting factor in the battery cycle life. Details of microstructural characterization and distribution of pores, examination of plastic flow during shrinkage, and observations of the rounding of nickel powder particles during the slurry process are presented.