Shape of two-dimensional solidification interface during directional solidification by continuous casting

Abstract

An analysis was made of the two-dimensional solidification of an ingot being cooled and withdrawn vertically downward from a mold consisting of parallel walls of finite length. Heat transfer analysis shows how the flatness of the interface is related to the ingot thickness, the withdrawal rate, the heat addition from the superheated liquid metal, and the temperature difference available for cooling. This provides an understanding of the conditions that will yield a maximum rate of casting while achieving the desired flatness of the interface. The results are interpreted with respect to the conditions for obtaining an aligned eutectic structure by directional solidification. In this process an additional constraint must be included that relates the ingot withdrawal rate and the heat transfer rate from the liquid metal to the solidification interface.