Accommodating and cracking mechanisms in low-cycle fatigue

Abstract

The three main stages of fatigue life (accommodation, crack initiation and crack growth) are briefly reviewed. The cyclic behavior of annealed or predeformed face-centered cubic metals is described. Moreover, two types of alloys (Al-4-Cu and WASPALOY) are examined regarding the influence of the interactions between the precipitates and the dislocations on the cyclic behavior. Data on the percent of life to crack initiation (for a microcrack smaller than about 100 microns) are also given. Finally, experimental and theoretical results on crack growth rates in lowcycle fatigue are described.