Ordering Effects in NbC and TaC

Abstract

By means of transmission electron microscopy and electron diffraction, evidence has been obtained for the existence of long range carbon atom ordering in single-crystal niobium carbide that has a carbon-to-metal ratio close to the integral composition Nb6C5. The ordering, which gives rise to superlattice and domain structures similar to those observed in V6C5, appears, however, only in samples that have been cooled slowly through the order-disorder temperature of 1025 C. In TaC of similar composition, the ordering, although present, remains very imperfect even after the crystals are subjected to the same thermal treatment. The results are interpreted in terms of the electronic structure of the transition metal carbides as it is currently understood, and their relevance to the mechanical properties of NbC and TaC are discussed.