Explore NASA and DOE materials research. Search alloys, composites and material properties, then open the original technical report for test conditions and results.

Follow this topic with RSS

At least 1,207 records · Page 67

All sources NASA NTRS DOE OSTI

DOE OSTI2025

Final report on assessment of molten salt corrosion testing of unirradiated and ion irradiated advanced manufactured high entropy alloys

Generation IV reactors and future fusion reactor designs have led to more demanding materials performance requirements due to their increased operating temperatures, corrosive coolants, and increased radiation doses compared to the current light-water reactor fleet. Among the innovative nuclear technologies under development, molten salt reactors stand out for their potential to offer superior fuel utilization, intrinsic safety characteristics, and economic viability. Of the proposed Generation IV designs, the gas fast reactor operates at 450 to 850°C and the molten salt reactor operates at 565 to 850°C, with the molten salt reactor design needing molten salt corrosion resistant materials [1, 2]. These increased temperatures and more extreme corrosion environments necessitate higher material performance, such as creep strength, radiation-tolerant microstructures, corrosion resistance, and high-temperature tensile properties. Hastelloy-N, a nickel-based alloy with additions of molybdenum and chromium, has been successfully employed to contain molten fluoride salt at temperatures up to 705°C. However, Hastelloy-N becomes embrittled upon neutron irradiation, primarily due to the accumulation of helium produced by (n,a) transmutation reactions. Furthermore, the corrosive nature of molten fluoride and chloride salts presents a formidable challenge, as these salts can react with and dissolve alloying elements such as Cr, Mo, and Fe, leading to selective leaching, loss of protective oxide layers, and accelerated degradation. High entropy alloys (HEAs) and refractory high entropy alloys (RHEAs) have emerged as a prominent area of interest, due to their ability to achieve tailored chemical compositions for specific applications. Unlike conventional alloys, HEAs are characterized by having multiple principal elements in equimolar or near equimolar ratios, leading to an unconventional alloying strategy [3]. This alloying strategy is believed to promote unique properties, such as single-phase stabilization of chemically compatible elements, lattice distortion effects due to atomic radius differences, and proposed sluggish diffusion effects. For extreme-environment applications, RHEAs have garnered much research interest because of the possibility of creating relatively ductile materials that can operate in extremely high-temperature environments, beyond the operating temperatures where other Ni-based superalloys begin to lose strength [4-6]. Idaho National Laboratory (INL) initiated a joint international effort with the Czech Republic to explore the feasibility of manufacturing HEAs for high-temperature nuclear applications using advanced manufacturing. This effort was funded at INL by the United States Department of Energy's Office of Nuclear Energy under the Advanced Reactor Technologies and Advanced Materials and Manufacturing Technologies (AMMT) Program. The HEAs were specifically designed for the corrosive and irradiation environments experienced in gas-cooled fast reactors, molten salt reactors, and fusion power. These alloys have been manufactured by multiple processes to determine the impact of manufacturing processes on the performance of the alloys in corrosive and irradiation environments. Preliminary molten salt corrosion testing showed that equimolar MoNbTiV and MoNbTi alloys exhibit exceptional performance, with arc-melted variants demonstrating only minimal degradation after 1000 hours of exposure to molten chloride salt at 700°C. Conversely, Nb2TiVZr2 showed significant molten salt corrosion susceptibility and microstructural instability during high-temperature molten salt exposures, and was, therefore deemed unfit for molten salt reactor applications. The MoNbTiV, MoNbTi, and Nb2TiVZr2 alloys were further evaluated through ion irradiation experiments conducted at the Michigan Ion Beam Laboratory at the University of Michigan. The microstructural stability and the evolution of irradiation-induced defects were characterized to assess the irradiation resistance of each of these alloys.

36 - MATERIALS SCIENCE↗

DOE OSTI2022

Design considerations for high entropy alloys in advanced nuclear applications

The demanding operating environments of advanced nuclear reactors require the development of new nuclear materials that can withstand their increased physical, chemical, thermal, and radiation-related challenges. High-entropy alloys (HEAs) have shown often-impressive mechanical, thermomechanical, and corrosion-resistant properties, and offer a massive, unexplored compositional space which allows for the targeted development of application-specific materials. Furthermore, although still in a nascent stage, research has shown that HEAs may exhibit unique irradiation tolerance, including reduced defect production and resistance to irradiation-induced swelling and hardening. The mechanisms behind this increased tolerance are not yet well-understood, although the HEA-specific attributes of a complex energy landscape, reduced thermal conductivity, and shift in defect migration energies and pathways provide promising explanations. Here this work assesses the current and future challenges faced by structural nuclear materials, identifying the specific applications in which HEAs may provide a competitive advantage compared to industry-standard materials with the aid of Ashby material selection maps. Considerations are provided for the design of future nuclear HEAs, including calculations of nuclear-relevant properties to assist in the initial down-selection of elements depending on application requirements (e.g., low neutron capture for in-core applications), narrowing the existing compositional space of HEAs to a manageable scope.

36 MATERIALS SCIENCE↗

NASA NTRS2006

Improving Thermomechanical Properties of SiC/SiC Composites

Today, a major thrust toward improving the thermomechanical properties of engine components lies in the development of fiber-reinforced silicon carbide matrix composite materials, including SiC-fiber/SiC-matrix composites. These materials are lighter in weight and capable of withstanding higher temperatures, relative to state-of-the-art metallic alloys and oxide-matrix composites for which maximum use temperatures are in the vicinity of 1,100 C. In addition, the toughness or damage tolerance of the SiC-matrix composites is significantly greater than that of unreinforced silicon-based monolithic ceramics. For successful application in advanced engine systems, the SiC-matrix composites should be able to withstand component service stresses and temperatures for the desired component lifetimes. Inasmuch as the high-temperature structural lives of ceramic materials are typically limited by creep-induced growth of flaws, a key property required of such composite materials is high resistance to creep under conditions of use. Also, the thermal conductivity of the materials should be as high as possible so as to minimize component thermal gradients and thermal stresses. A state-of-the-art SiC-matrix composite is typically fabricated in a three-step process: (1) fabrication of a component-shaped architectural preform reinforced by thermally stable high-performance fibers, (2) chemical-vapor infiltration (CVI) of a fiber-coating material such as boron nitride (BN) into the preform, and (3) infiltration of an SiC-based matrix into the remaining porosity in the preform. Generally, the matrices of the highest-performing composites are fabricated by initial use of a CVI SiC matrix component that is typically more thermally stable and denser than matrix components formed by processes other than CVI. As such, the initial SiC matrix component made by CVI provides better environmental protection to the coated fibers embedded within it. Also, the denser CVI SiC imparts to the composite better resistance to propagation of cracks, enhanced thermal conductivity, and higher creep resistance.

DiCarlo, James A.↗

NASA NTRS1985

Tough composite materials: Recent developments

The present volume broadly considers topics in composite fracture toughness and impact behavior characterization, composite system constituent properties and their interrelationships, and matrix systems' synthesis and characterization. Attention is given to the characterization of interlaminar crack growth in composites by means of the double cantilever beam specimen, the characterization of delamination resistance in toughened resin composites, the effect of impact damage and open holes on the compressive strength of tough resin/high strain fiber laminates, the effect of matrix and fiber properties on compression failure mechanisms and impact resistance, the relation of toughened neat resin properties to advanced composite mechanical properties, and constituent and composite properties' relationships in thermosetting matrices. Also treated are the effect of cross-link density on the toughening mechanism of elastomer-modified epoxies, the chemistry of fiber/resin interfaces, novel carbon fibers and their properties, the development of a heterogeneous laminating resin, solvent-resistant thermoplastics, NASA Lewis research in advanced composites, and opportunities for the application of composites in commercial aircraft transport structures.

Vosteen, L. F.↗

NASA NTRS1996

NASA-UVa Light Aerospace Alloy and Structures Technology Program: Aluminum-Based Materials for High Speed Aircraft

This report is concerned with 'Aluminum-Based Materials for High Speed Aircraft' which was initiated to identify the technology needs associated with advanced, low-cost aluminum base materials for use as primary structural materials. Using a reference baseline aircraft, these materials concept will be further developed and evaluated both technically and economically to determine the most attractive combinations of designs, materials, and manufacturing techniques for major structural sections of an HSCT. Once this has been accomplished, the baseline aircraft will be resized, if applicable, and performance objectives and economic evaluations made to determine aircraft operating costs. The two primary objectives of this study are: (1) to identify the most promising aluminum-based materials with respect to major structural use on the HSCT and to further develop those materials, and (2) to assess these materials through detailed trade and evaluation studies with respect to their structural efficiency on the HSCT.

Starke, E. A., Jr.↗

NASA NTRSDate not supplied

Initial Results of the MISSE-Flight Facility Polymers and Composites Experiment 1-4 (PCE 1-4)

Spacecraft in low Earth orbit (LEO) are subjected to harsh environmental conditions, including radiation (cosmic rays, ultraviolet (UV), x-ray and charged particle radiation), micrometeoroids and orbital debris, temperature extremes, thermal cycling, and atomic oxygen (AO). These environmental exposures can result in erosion, embrittlement and optical property degradation of susceptible materials threatening spacecraft performance and durability. To increase our understanding of effects such as AO erosion and radiation induced embrittlement of spacecraft materials, NASA Glenn Research Center has developed a series of experiments that are flown as part of the Materials International Space Station Experiment (MISSE) missions on the exterior of the International Space Station (ISS). These experiments have provided critical space environmental durability data such as AO erosion data of polymers and composites, and radiation induced mechanical property degradation of spacecraft insulation materials, after long term space exposure. In continuing these studies, four Glenn experiments with 365 flight samples have been flown on ISS’s external MISSE-Flight Facility (MISSE-FF). These experiments are the Polymers and Composites Experiment-1 (PCE-1) flown as part of the inaugural MISSE-9 mission, the PCE-2 flown as part of the MISSE-10 mission, the PCE-3 flown as part of the MISSE-12 and MISSE-15 missions, and the PCE-4 flown as part of the MISSE-13 mission. The primary objective of the PCE 1-4 experiments is to determine the AO and radiation durability of spacecraft polymers and composites. In addition, each experiment has a wide variety of spacecraft materials and hence they each have numerous additional sample objectives. Each of the PCE 1-4 is designed to examine the consequences of AO interactions including AO erosion yield (Ey) and optical and thermal property characterization. Several polymers were flown in both ram and zenith flight orientations to determine the effect of varying solar to AO ratios on Ey. Common spacecraft materials including Teflon FEP, white Tedlar and Upilex-S were included on multiple MISSE missions so erosion dependence on environment exposure can be determined. The PCE-1 includes epoxy composite samples with varying ZnO levels to determine the effect of inorganic filler level on AO durability. And, a variety of samples were flown to characterize AO scattering and AO undercutting processes. All four PCE experiments include samples to provide better insight into radiation durability of polymers and composites. The MISSE-9 PCE-1 includes Teflon FEP tensile samples flown in the wake and zenith direction so variations in radiation exposure from the different flight directions can provide insight into radiation induced embrittlement of Teflon FEP. Teflon FEP tensile samples were also flown in the wake direction as part of the MISSE-13 PCE-4. In addition, shape memory alloys, shape memory composites, melanin based composites, stressed and unstressed gossamer sun shield materials, coated and uncoated docking seal samples, and new solar cell cover slides were flown for space radiation durability and/or shielding assessment. This paper provides an overview of Glenn’s PCE 1-4 MISSE-FF experiments and provides initial post-flight observations and results.

atomic oxygen↗

DOE OSTI2025

Alloying multiple halide perovskites on the same sublattice in search of stability and target band gaps

Single-component halide perovskites (HPs) rarely satisfy all the necessary criteria for optoelectronic applications, such as achieving an optimal band gap while maintaining high chemical and structural stability. Alloying halide perovskites has emerged as a promising strategy, not only to enhance stability but also to fine-tune their electronic and optical properties. In this work, we explore multiple degrees of freedom in alloy design, considering different substitution sublattices sites (A, B, or X in ABX3 perovskites), various chemical species (isovalent and hetero-valent elements), and multi-component compositions on a given sublattice. Using first-principles calculations based on density functional theory (DFT), we investigate how compositional variations influence the electronic (band gap) and structural properties (mixing enthalpy) of HP alloys. Our approach employs the polymorphous cell model, allowing full local relaxation which breaks local symmetry while preserving global cubic symmetry—an essential framework for accurately modeling HPs. Our results reveal that X-site mixing (halogen substitution) primarily affects the valence band maximum, allowing target band gap engineering. Additionally, variations in halogen radii introduce internal strain through octahedral distortions, influencing the mixing enthalpy. A-site substitution, while not directly contributing to the band edge states, modifies structural stability via volume effects, indirectly impacting the band gap. B-site alloying plays a dominant role in band gap modulation, leading to either positive or negative band gap bowing. Specifically, isovalent B-site mixing (Sn–Pb) induces strong positive bowing, where the alloy band gap is smaller than the average gap of parent compounds, whereas hetero-valent mixing (Cd–Pb) results in pronounced negative bowing. As an aside, we investigate the competition between the excess energy of disordered alloys vs. that of long-range ordered double perovskites of the same compositions, seeking examples of ordered phases emerging from disordered alloys. Furthermore, our findings provide fundamental insights into the electronic and structural behavior of HP alloys, offering valuable design principles for the development of stable and efficient materials for next-generation photovoltaic and optoelectronic devices.

14 SOLAR ENERGY↗

DOE OSTI2023

THE IMPACT OF OXIDATION-INDUCED DEGRADATION ON MATERIALS USED IN HYDROGEN-FIRED MICROTURBINES

Hydrogen-fueled microturbines are being considered as part of the future green microgrid. However, the use of hydrogen as a fuel presents new challenges for selection and development of suitable high temperature materials for hydrogen combustion. The burning of hydrogen is expected to result in higher operating temperatures and higher than typically observed water vapor contents in exhaust gases than after burning natural gas. In the present work, foil specimens of various Fe- and Ni-based alloys were oxidized in air + 10vol.% H2O and air + 60vol.% H2O for up to 5,000 h at 700 °C to simulate the exhaust atmosphere of natural gas and hydrogen-fueled microturbines. The impact of alloy composition and water vapor content on the oxidation/ volatilization induced loss of wall thickness was experimentally evaluated. Enhanced external oxidation and volatilization of Cr¬2O3 and Ti-doped Cr2O3 scales was observed in 60 % H2O compared to 10% H2O. No significant impact of the higher water vapor content was observed on Al2O3 scales formed on Fe-based alumina forming alloys. Lifetime modeling was employed to predict the combined effects of water vapor content, gas flow rates, temperature and alloy composition on the oxidation-induced lifetime of the investigated materials

Romedenne, Marie↗

NASA NTRS1996

NASA-UVA Light Aerospace Alloy and Structures Technology Program (LA2ST)

The NASA-UVA Light Aerospace Alloy and Structures Technology (LA2ST) Program was initiated in 1986 and continues with a high level of activity. The objective of the LA2ST Program is to conduct interdisciplinary graduate student research on the performance of next generation, light-weight aerospace alloys, composites and thermal gradient structures in collaboration with NASA-Langley researchers. Specific technical objectives are presented for each research project. We generally aim to produce relevant data and basic understanding of material mechanical response, environmental/corrosion behavior, and microstructure; new monolithic and composite alloys; advanced processing methods; new solid and fluid mechanics analyses; measurement and modeling advances; and a pool of educated graduate students for aerospace technologies. Three research areas are being actively investigated, including: (1) Mechanical and environmental degradation mechanisms in advanced light metals, (2) Aerospace materials science, and (3) Mechanics of materials for light aerospace structures.

Scully, John R.↗

NASA NTRS1997

NASA-UVA Light Aerospace Alloy and Structures Technology Program (LA2ST)

The NASA-UVA Light Aerospace Alloy and Structures Technology (LA2ST) Program was initiated in 1986 and continues with a high level of activity. Here, we report on progress achieved between July I and December 31, 1996. The objective of the LA2ST Program is to conduct interdisciplinary graduate student research on the performance of next generation, light-weight aerospace alloys, composites and thermal gradient structures in collaboration with NASA-Langley researchers. Specific technical objectives are presented for each research project. We generally aim to produce relevant data and basic understanding of material mechanical response, environmental/corrosion behavior, and microstructure; new monolithic and composite alloys; advanced processing methods; new solid and fluid mechanics analyses; measurement and modeling advances; and a pool of educated graduate students for aerospace technologies. The accomplishments presented in this report are summarized as follows. Three research areas are being actively investigated, including: (1) Mechanical and Environmental Degradation Mechanisms in Advanced Light Metals, (2) Aerospace Materials Science, and (3) Mechanics of Materials for Light Aerospace Structures.

Gangloff, Richard P.↗

NASA NTRS1999

Crystal Growth of II-VI Semiconducting Alloys by Directional Solidification

This research study is investigating the effects of a microgravity environment during the crystal growth of selected II-VI semiconducting alloys on their compositional, metallurgical, electrical and optical properties. The on-going work includes both Bridgman-Stockbarger and solvent growth methods, as well as growth in a magnetic field. The materials investigated are II-VI, Hg(1-x)Zn(x)Te, and Hg(1-x)Zn(x)Se, where x is between 0 and 1 inclusive, with particular emphasis on x-values appropriate for infrared detection and imaging in the 5 to 30 micron wavelength region. Wide separation between the liquidus and solidus of the phase diagrams with consequent segregation during solidification and problems associated with the high volatility of one of the components (Hg), make the preparation of homogeneous, high-quality, bulk crystals of the alloys an extremely difficult nearly an impossible task in a gravitational environment. The three-fold objectives of the on-going investigation are as follows: (1) To determine the relative contributions of gravitationally-driven fluid flows to the compositional redistribution observed during the unidirectional crystal growth of selected semiconducting solid solution alloys having large separation between the liquidus and solidus of the constitutional phase diagram; (2) To ascertain the potential role of irregular fluid flows and hydrostatic pressure effects in generation of extended crystal defects and second-phase inclusions in the crystals; and, (3) To obtain a limited amount of "high quality" materials needed for bulk crystal property characterizations and for the fabrication of various device structures needed to establish ultimate material performance limits. The flight portion of the study was to be accomplished by performing growth experiments using the Crystal Growth Furnace (CGF) manifested to fly on various Spacelab missions.

Lehoczky, Sandor L.↗

NASA NTRS2013

Fracture Analysis of Particulate Reinforced Metal Matrix Composites

A fracture analysis of highly loaded particulate reinforced composites was performed using laser moire interferometry to measure the displacements within the plastic zone at the tip of an advancing crack. Ten castings were made of five different particulate reinforcement-aluminum alloy combinations. Each casting included net-shape specimens which were used for the evaluation of fracture toughness, tensile properties, and flexure properties resulting in an extensive materials properties data. Measured fracture toughness range from 14.1 MPa for an alumina reinforced 356 aluminum alloy to 23.9 MPa for a silicon carbide reinforced 2214 aluminum alloy. For the combination of these K(sub Ic) values and the measured tensile strengths, the compact tension specimens were too thin to yield true plane strain K(sub Ic) values. All materials exhibited brittle behavior characterized by very small tensile ductility suggesting that successful application of these materials requires that the design stresses be below the elastic limit. Probabilistic design principles similar to those used with ceramics are recommended when using these materials. Such principles would include the use of experimentally determined design allowables. In the absence of thorough testing, a design allowable stress of 60 percent of the measured ultimate tensile stress is recommended.

Min, James B.↗

NASA NTRSDate not supplied

A Machine Learning Approach to Predict Martensitic Transition Temperatures for Shape Memory Alloys

Shape memory alloys (SMAs) are a unique class of materials with several remarkable properties including shape recovery, superelasticity, etc. Especially important for many NASA applications is the ability to tune the martensitic phase transition temperature by varying the alloy composition. Nickel-titanium (NiTi) based alloys are the most widely studied of this class, with compositions involving ternary, quaternary, or higher additions being considered. Over the past several years, a significant database of SMA properties has been assembled by NASA researchers. Such a database is ideal for data science-based approaches including machine learning. We present results from a developed machine learning model capable of accurately predicting the transition temperature of SMAs across a wide range of compositions. Our model has the added benefit of interpretability and even provides confidence intervals for our predictions. This model will make rapid screening and design of new SMA materials possible. Predictions from the machine learning model can be validated by empirical and/or atomistic scale modeling.

Shreyas Honrao↗

DOE OSTI2023

A high-strength precipitation hardened cobalt-free high-entropy alloy

Recent studies on precipitation-hardened high-entropy alloys (HEAs) demonstrate their high strength and thermal stability, making them promising materials for high-temperature structural applications such as nuclear reactors. However, many existing HEAs contain cobalt (Co), which is unsuitable for nuclear applications because of the long-term activation issue of Co. Co is also expensive and considered a critical material for other applications. Therefore, it is desired to exclude Co from the composition. A Co-free (Fe 0.3 Ni 0.3 Mn 0.3 Cr 0.1 ) 88 Ti 4 Al 8 HEA was developed and studied in this work. In contrast to previous Co-free HEAs, this alloy is close to equiatomic in its composition and promises a more pronounced high-entropy effect. Scanning electron microscopy, transmission electron microscopy, atom probe tomography, and synchrotron-based, high-energy X-ray diffraction were used to characterize this alloy and revealed a complex four-phase structure, with an FCC matrix, γ’ precipitates, and a network of B2 and χ phase particles. This structure granted 2151 MPa compressive strength and good thermal stability, but with limited ductility and slow precipitation kinetics. A strengthening analysis of the alloy shows that the B2 and χ provided the most significant strengthening contribution, adding 312 MPa and 788 MPa respectively. Furthermore the strengthening effect from the nanoscale γ' is also considerable, adding 608 MPa in total. This study lays the foundation for the continued development of high-strength Co-free HEAs with improved and satisfactory ductility.

36 MATERIALS SCIENCE↗

NASA NTRS1988

A study of surface tension driven segregation in monotectic alloy systems

The compatibilities of various monotectic alloy systems with several different crucible materials were evaluated. The study was carried out using small candidate alloy samples of compositions that produced fifty volume percent of each liquid phase at the monotectic temperature. Compatibility was based on the evaluation of the wetting tendency of the two immiscible phases with the crucible material in a one-g solidified sample. Three types of wetting phenomena were observed during the evaluation. Type 1 indicates an alloy-crucible combination where the L2 phase preferentially wets the crucible material. Since L2 is usually the minority phase in desirable alloys, this material combination would be difficult to process and is therefore considered incompatible. Type 2 behavior indicates an alloy-crucible combination where the L1 phase preferentially wets the crucible material. This type of combination is considered compatible since surface tension effects should aid in processing the alloy to a useful form. Type 3 indicates any combination that leads to major reactions between the alloy and crucible material, gas entrapment, or separation of the metal from the crucible wall. Additional compatibility evaluations would have to be carried out on combinations of this category. The five alloy systems studied included aluminum-bismuth, copper-lead, aluminum-indium, aluminum-lead and cadmium-gallium. The systems were combined with crucibles of alumina, boron nitride, mullite, quartz, silicon carbide and zirconia.

Andrews, J. Barry↗

DOE OSTI2024

Elucidating the mechanical and thermal response of nanotwinned Ni alloys

Transformative advances in nanoscale materials synthesis, characterization and modeling are enabling the synthesis of materials with unprecedent properties and greater understanding of the nanoscale mechanisms that underpin these properties. Nanotwinned Cu alloys have received considerable attention due to their impressive balance of strength and ductility, but they have limited microstructural stability. Recent instantiation of nanotwins in sputter deposited Ni-Mo-W, and several commercial Ni-based superalloys, point to the potential development of a new class of high temperature materials with a very beneficial suite of mechanical and physical properties. The experimental study described in this report was undertaken to elucidate the nanoscale origins of the thermal and mechanical behavior of nanotwinned Ni alloys. Micropillar compression experiments have shown nanotwinned Ni 85 Mo 15-x W x alloys to possess unusually high strengths above 3.5GPa and enhanced microstructural stability. The strength of these nanotwinned alloys is determined by the abrupt formation of shear bands. This study focused on identifying the nanoscale trigger, or triggers, for shear banding in nanotwinned materials using in situ experiments and atomic-scale postmortem analysis. Contrasting and comparing the mechanical response and postmortem nanostructures of “Mo-rich” and “W-rich” nanotwinned specimens elucidated the importance of the lateral motion of easy glide defects that results in erasure of twins and local coarsening of the nanotwinned microstructure. This twin coarsening was then associated with very localized plasticity, strain softening, and shear band formation. The difference between alloys was further studied by considering the role of various material factors: stacking fault energy, coherent twin boundary spacing and flatness, grain size, and the interactions of solute atoms with twin and grain boundaries. The effect of alloy composition and sputtering power and temperature were also investigated and used to control twin spacing and geometry. Combined with atomic-scale simulations, these experiments insights should allow us to identify strategies for achieving concomitant ultrahigh strength and ductility in nanotwinned Ni alloys. In parallel but synergistic studies, our work was buoyed by collaborative state-of-the-art nanoscale orientation and strain mapping at the DOE National Center for Electron Microscopy (NCEM). For example, novel 4D-STEM techniques were used to acquire nanoscale strain maps. The extremely fine twin spacing limited our measurements of atomic-scale thermal expansion within twins, but recent results from NCEM suggest that it will soon be possible to conduct such measurements and to unravel the origins of the novel thermal expansion characteristics of nanotwinned Ni alloys.

36 MATERIALS SCIENCE↗

NASA NTRS1974

Immiscible materials and alloys

Only immiscible materials which involve a fluid phase have a potential advantage when considered for space processing. Processing of such systems at low gravity can lead to a material which is very homogeneous and contains a finely dispersed mixture of phases. Materials with such structures may exhibit potentially useful properties for such applications as superconductors, dispersion-strengthened materials, superplastic materials, permanent magnets, etc. These conclusions have resulted from review of past efforts in the field of low-g processing of materials containing a liquid phase miscibility gap and from present efforts dealing with such systems. These studies have concentrated on precipitation of liquid droplets in a host liquid during cooling through the miscibility gap. This effort has been to study the agglomeration of the droplets both experimentally and through computer simulation in order to understand the mechansism involved and to deduce the effect of gravity on the droplet distribution and resulting structure of the solidified material. The agglomeration mechanisms treated in detail are those due to diffusional growth and collision processes caused by Stokes on convection current-induced droplet migration.

Markworth, A. J.↗

NASA NTRSDate not supplied

High Energy Dynamic Impact Testing of APC AS4D/PEKK-FC and TC1225 LMPAEK T700G Thermoplastic Composite Materials

High energy dynamic impact tests were conducted on AS4/PEKK and TC1225 LMPAEK T700G thermoplastic quasi-isotropic laminated tape composite panels. The primary objective was to provide data for evaluation of computational composite impact models. Measurements include transient deformations, pre- and post-test characterization of delamination and energy threshold for onset of delamination and onset of penetration. Empirical results indicate an approximately 50% increase in penetration threshold velocity and over 100% increase in penetration energy threshold for the TC1225 LMPAEK T700G composite compared to the AS4/PEKK composite. The velocity required to produce NDE-detectable delamination in the TC1225 LMPAEK T700G composite was roughly twice that for the AS4/PEKK composite. Results will be compared with those from a thermoset composite system with a similar architecture. Because of differences in the chemical structure of the two resins, differences in the impact response are to be expected.

Impact↗