Small Co-doping induced magnetic and electrical transitions in single crystal CaFe 0.95 Co 0.05 O 3
CaFeO 3 and CaFe 0.95 Co 0.05 O 3 single crystals were grown by combing floating-zone method with high oxygen pressure treatment. Both crystals show charge disproportionation of Fe (Fe 4+ → Fe 3+ + Fe 5+ ) accompanied by a metal-to-insulator transition as well as a crystal structural transformation from Pbnm to 𝑃2 1 /𝑛. However, the slight introduction of Co significantly suppresses the critical temperature of charge disproportionation from 290 K in CaFeO 3 to 260 K in CaFe 0.95 Co 0.05 O 3 . Different from the single antiferromagnetic phase transition as observed in the polycrystalline CaFeO 3 , two sequential antiferromagnetic transitions are found to occur in these two single crystals with the Néel temperatures around 119 and 112 K for CaFeO 3 crystal and 109 and 98 K for CaFe 0.95 Co 0.05 O 3 crystal, respectively. Neutron diffraction illustrates the formation of a spiral antiferromagnetic structure. Moreover, as the temperature further decreases to 65 K, a third magnetic transition accompanied by a second electrical transition is observed in the slightly Co-doped CaFe 0.95 Co 0.05 O 3 crystal. In conclusion, first-principles calculations suggest that the introduction of a moderate amount of Co and the peculiar spiral spin texture play an important role in the presence of such new magnetic and electrical transitions.