DOE OSTI2023

From Femtoseconds to Gigaseconds: The SolDeg Project to Analyze and Mitigate the Performance Degradation of a-Si:H/c-Si Heterojunction Solar Cells

We pursued two major projects. In the first, we studied the degradation of a-Si/c-Si Heterojunction cells. We substantially expanded our previously developed SolDeg platform, and incorporated hydrogen into it. We also expanded the capabilities of SolDeg by developing a three channel model for a very efficient way to determine long term junction dynamics. The first main result was that we identified hydrogen drifting away from the interface as a key degradation channel. The second was that we developed and proposed the concept of a “reverse silicon density gradient” in the a-Si layer that had the promise of reducing degradation by up to 80%. In the second project, we studied the degradation of TOPCon solar cells. We again identified a key degradation channel, which in these cells was the formation of pinholes across the oxide layer. We then again were able to develop and to propose a way to dramatically reduce degradation by discovering that tuning the hydrogen concentration forms a sharp and deep minimum of the recombination current.

14 SOLAR ENERGY↗

DOE OSTI2022

High-Mobility Hole Transport in Single-Grain PbSe Quantum Dot Superlattice Transistors

Epitaxially-fused superlattices of colloidal quantum dots (QD epi-SLs) may exhibit electronic minibands and high-mobility charge transport, but electrical measurements of epi-SLs have been limited to large-area, polycrystalline samples in which superlattice grain boundaries and intragrain defects suppress/obscure miniband effects. Systematic measurements of charge transport in individual, highly-ordered epi-SL grains would facilitate the study of minibands in QD films. Here, we demonstrate the air-free fabrication of microscale field-effect transistors (μ-FETs) with channels consisting of single PbSe QD epi-SL grains (2–7 μm channel dimensions) and analyze charge transport in these single-grain devices. The eight devices studied show p-channel or ambipolar transport with a hole mobility as high as 3.5 cm 2 V –1 s –1 at 290 K and 6.5 cm 2 V –1 s –1 at 170–220 K, one order of magnitude larger than that of previous QD solids. The mobility peaks at 150–220 K, but device hysteresis at higher temperatures makes the true mobility–temperature curve uncertain and evidence for miniband transport inconclusive.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2021

From Femtoseconds to Gigaseconds: The SolDeg Platform for the Performance Degradation Analysis of Silicon Heterojunction Solar Cells

Heterojunction Si solar cells exhibit notable performance degradation. Here, we modeled this degradation by electronic defects getting generated by thermal activation across energy barriers over time. To analyze the physics of this degradation, we developed the SolDeg platform to simulate the dynamics of electronic defect generation. First, femtosecond molecular dynamics simulations were performed to create a-Si/c-Si stacks, using the machine learning-based Gaussian approximation potential. Second, we created shocked clusters by a cluster blaster method. Third, the shocked clusters were analyzed to identify which of them supported electronic defects. Fourth, the distribution of energy barriers that control the generation of these electronic defects was determined. Fifth, an accelerated Monte Carlo method was developed to simulate the thermally activated time-dependent defect generation across the barriers. Our main conclusions are as follows. (1) The degradation of a-Si/c-Si heterojunction solar cells via defect generation is controlled by a broad distribution of energy barriers. (2) We developed the SolDeg platform to track the microscopic dynamics of defect generation across this wide barrier distribution and determined the time-dependent defect density N(t) from femtoseconds to gigaseconds, over 24 orders of magnitude in time. (3) We have shown that a stretched exponential analytical form can successfully describe the defect generation N(t) over at least 10 orders of magnitude in time. (4) We found that in relative terms, Voc degrades at a rate of 0.2%/year over the first year, slowing with advancing time. (5) We developed the time correspondence curve to calibrate and validate the accelerated testing of solar cells. We found a compellingly simple scaling relationship between accelerated and normal times t normal ∝ t accel T(accel)/T(normal) . (6) We also carried out experimental studies of defect generation in a-Si:H/c-Si stacks. We found a relatively high degradation rate at early times that slowed considerably at longer time scales.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2020

Commensuration Effects in Layered Nanoparticle Solids.

We have developed a hierarchical nanoparticle transport simulator (HINTS) and adapted it to study commensuration effects in two classes of nanoparticle (NP) solids: (1) a bilayer NP solid (BNS) with an energy offset and (2) a BNS as part of a field effect transistor (FET). HINTS integrates the ab initio characterization of single NPs with the phonon-assisted tunneling transition model of the NP-NP transitions into a kinetic Monte Carlo based simulation of the charge transport in NP solids. First, we studied a BNS with an interlayer energy offset Delta, possibly caused by a fixed electric field. Our results include the following. First, in the independent energy-offset model, we observed the emergence of commensuration effects when scanning the electron filling factor (FF) across integer values. These commensuration effects were profound as they reduced the mobility by several orders of magnitude. We analyzed these commensuration effects in a five-dimensional parameter space, as a function of the on-site charging energy E-C, energy offset Delta, disorder D, the electron FF, and temperature k(B)T. We demonstrated the complexity of our model by showing that at integer FFs commensuration effects are present in some regions of the parameter space, while they vanish in other regions, thus defining distinct dynamical phases of the model. We determined the phase boundaries between these dynamical phases. Second, using these results as a foundation, we shifted our focus to the experimentally much-studied NP-FETs. NP-FETs are also characterized by an interlayer energy offset Delta, which, in contrast to our first model, is set by the gate voltage V-G and thereby related to the electron FF. We repeated many of our simulations and again demonstrated the emergence of commensuration effects and distinct dynamical phases in these NP-FETs. Notably, the commensuration effects in the NP-FETs showed many similarities to those in the independent energy-offset BNS.

Qu, Luman↗