Solid electrolyte interphase (SEI) has been widely perceived to play a critical role in the stable cycling of rechargeable batteries. However, associated with the fragile and air-sensitive nature of the SEI layer, delineation of the formation process and the nature of SEI remains a big challenge. Here, we use in situ liquid time-of-flight secondary ion mass spectroscopy (TOF-SIMS), cryo- transmission electron microscope (TEM) and density functional theory (DFT) calculation to delineate molecular process on the formation of SEI layer under the dynamic operating condition. We discover that the onset potential for SEI layer formation and the thickness of the SEI show dependence on the solvation shell structure. Using LiCoO 2 as a cathode and Cu film as an anode, the SEI is noticed to start to form at around 2.0 V and reach its final thickness (irreversible part, ~ 40-50 nm) at about 3.0 V in the 1 M LiPF 6 –EC/DMC electrolyte, while for the case of 1 M LiFSI–DME, the SEI starts to form at around 1.5 V and reaches its final thickness (~ 20 nm) at about 2.0 V. The in situ TOF-SIMS clearly indicates the outer SEI layer formation and dissipation upon charging and discharging, implying a continued evolution of electrolyte structure with extended cycling. In conclusion, the present work establishes a direct correlation between the molecular signature of SEI layer with solvation feature of electrolytes in lithium batteries, providing insights for tailoring SEI layer toward improved electrochemical properties of lithium batteries.

25 ENERGY STORAGE↗

DOE OSTI2023

Visualizing oxygen transport pathways during intergranular oxidation in Ni-Cr

The transport paths of O during intergranular oxidation in binary Ni-Cr were investigated. To isolate the selective oxidation of Cr, oxidation was performed with a CO/CO 2 gas mixture in which the oxygen partial pressure was kept under the NiO dissociation pressure. A combination of electron microscopy and atom probe tomography (APT) was used to study the nanometer-scale details of the passivation and penetrative intergranular oxidation processes at high-energy grain boundaries. Oxygen transport towards the terminating oxidation front is elucidated with dedicated usage of oxygen tracer exchange experiments. Secondary ion mass spectroscopy and APT support classical theories of internal oxidation, revealing preferred transport paths at the oxide/alloy interface with sub-nanometer resolution.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Data for EMSL Project 60413 from August 2023

Explore the source record for details and available documents.

Hu, Dehong↗