Zhang, Yanwen

Publications and source records attributed to Zhang, Yanwen.

At least 19 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2024

Effects of irradiation damage on the hardness and elastic properties of quaternary and high entropy transition metal diborides

Multi-principal component transition metal (TM) diborides represent a class of high-entropy ceramics (HECs) that have received considerable interest in recent years owing to their promising properties for extreme environment applications that include thermal/ environmental barriers, hypersonic vehicles, turbine engines, and next-generation nuclear reactors. While the addition of chemical disorder through the random distribution of TM elements on the cation sublattice has offered opportunities to tailor elastic stiffness and hardness, the effects of irradiation-induced structural damage on the physical properties of these complex materials have remained largely unexplored. To this end, changes in the hardness and elastic moduli of a high-entropy TM diboride (Hf 0.2 Nb 0.2 Ta 0.2 Ti 0.2 Zr 0.2 )B 2 and three of its quaternary subsets following irradiation with 10 MeV gold (Au) ions to fluences of up to 6 × 10 15 Au cm -2 are investigated at the micrometer and sub-micrometer length-scales via the dispersion of laser-generated surface acoustic waves (SAW) and nanoindentation, respectively. The nanoindentation measurements show that the TM diborides exhibit an initial increase in hardness following irradiation with energetic Au ions, with a subsequent decrease in hardness following further irradiation. One quaternary composition, (Hf 1/3 Ta 1/3 Ti 1/3 )B 2 , exhibits a notable exception to the trend and continues to exhibit an increase in hardness with ion irradiation fluence. Although differences in the absolute values of the effective elastic moduli obtained from the measured SAW dispersion and nanoindentation are observed (and attributed to microstructural variations at the measurement length-scale), both techniques yield similar trends in the form of an initial reduction and subsequent saturation in the elastic modulus with increasing ion irradiation fluence. The quaternary TM diboride (Hf 1/3 Ta 1/3 Ti 1/3 )B 2 again exhibits a departure from this trend. The high-entropy TM diboride (Hf 0.2 Nb 0.2 Ta 0.2 Ti 0.2 Zr 0.2 )B 2 exhibits the greatest recovery in hardness and modulus when irradiated to high ion fluences following initial changes at low fluence, indicating superior resistance to radiation-induced damage over its quaternary counterparts. Opportunities for designing HECs with superior hardness and modulus for enhanced radiation resistance (compared to their single constituent counterparts) by tailoring chemical disorder and bond character in the lattice are discussed.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Ion velocity effect governs damage annealing process in defective KTaO 3

Effects of electronic to nuclear energy losses (S e /S n ) ratio on damage evolution in defective KTaO 3 have been investigated by irradiating pre-damaged single crystal KTaO 3 with intermediate energy O ions (6 MeV, 8 MeV and 12 MeV) at 300 K. By exploring these processes in pre-damaged KTaO 3 containing a fractional disorder level of 0.35, the results demonstrate the occurrence of a precursory stage of damage production before the onset of damage annealing process in defective KTaO 3 that decreases with O ion energy. The observed ionization-induced annealing process by ion channeling analysis has been further mirrored by high resolution transmission electron microscopy analysis. In addition, the reduction of disorder level is accompanied by the broadening of the disorder profiles to greater depth with increasing ion fluence, and enhanced migration is observed with decreasing O ion energy. Since S e (~3.0 keV nm –1 ) is nearly constant for all 3 ion energies across the pre-damaged depth, the difference in behavior is due to the so-called 'velocity effect': the lower ion velocity below the Bragg peak yields a confined spread of the electron cascade and hence an increased energy deposition density. Here, the inelastic thermal spike calculation has further confirmed the existence of a velocity effect, not previously reported in KTaO 3 or very scarcely reported in other materials for which the existence of ionization-induced annealing has been reported. In other words, understanding of ionization-induced annealing has been advanced by pointing out that ion velocity effect governs the healing of pre-existing defects, which may have significant implication for the creation of new functionalities in KTaO 3 through atomic-level control of microstructural modifications, but may not be limited to KTaO 3 .

74 ATOMIC AND MOLECULAR PHYSICS↗
DOE OSTI2024

Microstructural evolution in doped high entropy alloys NiCoFeCr-3X (X=Pd/Al/Cu) under irradiation

Commonly studied equatomic single-phase FCC high entropy alloys based on 3d transition metals like NiCoFeCr do not provide adequate strength and radiation resistance at high doses for nuclear structural applications. In the current study, the major alloying effects like lattice distortion, ordering and clustering tendencies were investigated by adding low concentration of Pd, Al, or Cu respectively to study the doping effects on the ion irradiation response of NiCoFeCr alloy. The alloys were irradiated with 3 MeV Ni 2+ ions at 500 °C to a fluence of 1 × 10 17 /cm 2 at a beam flux of approximately 2.8 × 10 12 ions/cm 2 /s. The microstructural evolution upon irradiation i.e., formation of dislocation networks, radiation induced segregation and precipitation, and void formation were studied in detail. Further, post-irradiation characterization results showed that a Pd addition leads to a high void nucleation rate but controlled void growth, which may be attributed to increased lattice distortion. In Al added HEA, our microstructural analysis indicates that radiation induced ordered L1 2 precipitates do not affect void swelling significantly. Cu addition led to Cu precipitation that drastically suppressed dislocation density and void swelling of the alloy. Additionally, a model was developed to qualitatively describe the trend in void swelling of typical FCC alloys under ion irradiation. This model was able to qualitatively explain the suppression and reappearance of void swelling in ion irradiated alloys that generally occurs near the region with peak implanted ion concentration.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Unfaulting mechanisms of interstitial Frank loops in fluorite-structured ThO 2

Unfaulting of Frank loops in irradiated fluorite-structured oxides is of significance for understanding microstructural evolution. However, the mechanisms have not yet been directly observed. To this end, we utilize molecular dynamics to reveal the atomistic details related to the unfaulting process of interstitial Frank loops in ThO 2 , which involve a single pair or multiple pairs of co-propagating Shockley partials to annihilate the stacking faults. Here, we find that the unfaulting is achieved via a synchronous shear of the partial pairs to remove the extrinsic stacking fault in the cation sublattice and the intrinsic stacking fault in the anion sublattice. The high mobility of oxygen at the dislocation core may reduce the activation barriers of dislocation nucleation and migration. These findings provide a fundamental understanding of the transformation of faulted loops in irradiated ThO 2 , and could be transferable to other fluorite-structured oxides.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2023

Volume 6: Experiment Facility Spectrum Tailoring (HFIR Futures – Enhanced Capabilities Series)

In-core irradiation experiment research, such as materials and fuels irradiation research and radioisotope production, is one of the primary missions of Oak Ridge National Laboratory’s (ORNL) versatile High Flux Isotope Reactor (HFIR). In support of the HFIR-Sustaining and Enhancing Neutron Science (SENSe) Initiative, a technically diverse group of ORNL irradiation research subject matter experts formed the Spectrum Tailoring Working Group, with the goal of developing a compendium of experiment facility concepts to enhance irradiation experiment conditions via neutron spectrum tailoring capabilities. The purpose of this report is to document the concepts developed in FY22 and the associated scientific justifications, identify potential facility sponsors, and estimate costs and schedules for each concept. This report documents the efforts performed in FY22, which may continue in FY23 or later pending the direction of the HFIR-SENSe Initiative and the interested sponsors.

21 SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLANTS↗
DOE OSTI2023

Nanoprecipitates to Enhance Radiation Tolerance in High-Entropy Alloys

The growth of advanced energy technologies for power generation is enabled by the design, development, and integration of structural materials that can withstand extreme environments, such as high temperatures, radiation damage, and corrosion. High-entropy alloys (HEAs) are a class of structural materials in which suitable chemical elements in four or more numbers are mixed to typically produce single-phase concentrated solid solution alloys (CSAs). Many of these alloys exhibit good radiation tolerance like limited void swelling and hardening up to relatively medium radiation doses (tens of displacements per atom (dpa)); however, at higher radiation damage levels (>50 dpa), some HEAs suffer from considerable void swelling limiting their near-term acceptance for advanced nuclear reactor concepts. In this study, we developed a HEA containing a high density of Cu-rich nanoprecipitates distributed in the HEA matrix. The Cu-added HEA, NiCoFeCrCu 0.12 , shows excellent void swelling resistance and negligible radiation-induced hardening upon irradiation up to high radiation doses (i.e., higher than 100 dpa). The void swelling resistance of the alloy is measured to be significantly better than NiCoFeCr CSA and austenitic stainless steels. Density functional theory simulations predict lower vacancy and interstitial formation energies at the coherent interfaces between Cu-rich nanoprecipitates and the HEA matrix. The alloy maintained a high sink strength achieved via nanoprecipitates and the coherent interface with the matrix at a high radiation dose (~50 dpa). From our experiments and simulations, the effective recombination of radiation-produced vacancies and interstitials at the coherent interfaces of the nanoprecipitates is suggested to be the critical mechanism responsible for the radiation tolerance of the alloy. Furthermore, the materials design strategy based on incorporating a high density of interfaces can be applied to high-entropy alloy systems to improve their radiation tolerance.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Volume 9: Critical Facility with Add-On Ion Beam

Completion of the originally planned critical facility has been considered as part of the High Flux Isotope Reactor (HFIR) Sustaining and Enhancing Neutron Science Initiative at Oak Ridge National Laboratory (ORNL). A working group of ORNL staff members was formed to develop the idea and to recommend one or more configurations to best support future HFIR operations and scientific capacities. HFIR was designed with a critical pool in the reactor bay that was projected to be outfitted as a critical facility. The primary purpose of the planned critical facility was to measure the subcritical worth of fresh fuel elements to support startup requirements. However, the Y-12 National Security Complex already housed a critical facility that was used for this purpose. This report presents the working group’s efforts, including determination of the proposed critical facility’s high-impact benefits. A generic low-power critical facility would be employed for reactor physics measurements, code and data validation, reactor operator and staff training, and education. This facility would be instrumental in supporting current HFIR operations, conversion of HFIR to low-enriched uranium, existing light water reactor operations, and advanced reactor development and deployment.

21 SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLANTS↗
DOE OSTI2022

Understanding effects of chemical complexity on helium bubble formation in Ni-based concentrated solid solution alloys based on elemental segregation measurements

Here, helium bubble formation and swelling were systematically studied in Ni-based concentrated solid solution alloys containing different numbers and types of elements. Our microscopy analysis showed that although increasing the alloy chemical complexity helps suppress bubble formation in general, there is no monotonic relationship between the bubble growth rate and the number of alloying elements. Certain elements (e.g., Fe and Pd) are more effective in suppressing bubble growth than others (e.g., Cr and Mn). Atom probe tomography was applied to accurately measure elemental segregation around bubbles, revealing unique effects of certain alloying elements on vacancy migration towards bubbles. More specifically, the high vacancy mobility via Cr sites leads to a large vacancy flux and an increased bubble size, while the high degree of atomic size mismatch introduced by Pd helps deflect vacancy flow away from bubbles and decrease the amount of swelling. The effects identified in this study provide new strategies to design concentrated solid solutions with superior resistance to swelling.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Revealing two-stage phase transition process in defective KTaO 3 under inelastic interactions

Here, the interactions of ions with defective KTaO 3 has been studied by irradiating pre-damaged single crystal KTaO 3 with 5 MeV C, 7 MeV Si and 12 MeV O ions at 300 K. By exploring these processes in KTaO 3 , the results show that, for a pre-damaged fractional disorder level of 0.3 and inelastic electronic energy loss, S e , ≥ 4.65 keV/nm (7 MeV Si ions), the synergistic interaction of Se with defects enables amorphous ion track creation. At lower values of S e (5 MeV C and 12 MeV O), minor increases in disorder are observed initially over a region of depth at an ion fluence of 10 ions/nm 2 , which may be due to dissolution of pre-existing interstitial or amorphous clusters; however, with further increase in ion fluence, a transition from irradiation-induced disorder production to ionization-induced damage recovery processes, not previously reported in KTaO 3 , is observed.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Deformation mechanisms in single crystal Ni-based concentrated solid solution alloys by nanoindentation

Nanoindentation is a critical technique to probe mechanical properties at the micrometer and sub-micrometer scales, accompanied by challenges from indentation size effect, pile-up/sink-in effect, and strain rate sensitivity. In this work, different nanoindentation techniques have been employed to explore Ni-based concentrated solid solution alloys (CSAs) with the addition of 3d transition metal elements including Co, Cr, Mn, and Fe, including unique single-crystal Ni, NiCo, NiFe, Ni 80 Cr 20 , and NiCoFeCr samples with (100) surfaces. A procedure of nanoindentation tests and data analysis/correction have been developed, and a data set of hardness, elastic modulus, strain rate sensitivity, and activation volume for Ni-based CSAs are provided, including the less explored binary alloys such as Ni 80 Cr 20 and Ni 80 Mn 20 . The results show that the type of alloying elements is more critical than the number of elements in strengthening: Co does not provide strengthening in NiCo, while Cr, Mn, and Fe are effective strengthening elements. Cr is the most effective among all the 3d transition metal elements. Furthermore, atomic-level lattice distortion is responsible for the strengthening and the role of stacking fault energy is insignificant in Ni-based CSAs at room temperature. In summary, nanoindentation shows increasing promise as a reliable and fast tool to provide comprehensive mechanical information for new alloy design and development.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Dynamic substrate reactions during room temperature heavy ion irradiation of CoCrCuFeNi high entropy alloy thin films

Abstract High entropy alloys (HEAs) are promising materials for various applications including nuclear reactor environments. Thus, understanding their behavior under irradiation and exposure to different environments is important. Here, two sets of near-equiatomic CoCrCuFeNi thin films grown on either SiO 2 /Si or Si substrates were irradiated at room temperature with 11.5 MeV Au ions, providing similar behavior to exposure to inert versus corrosion environments. The film grown on SiO 2 had relatively minimal change up to peak damage levels above 500 dpa, while the film grown on Si began intermixing at the substrate–film interface at peak doses of 0.1 dpa before transforming into a multi-silicide film at higher doses, all at room temperature with minimal thermal diffusion. The primary mechanism is radiation-enhanced diffusion via the inverse Kirkendall and solute drag effects. The results highlight how composition and environmental exposure affect the stability of HEAs under radiation and give insights into controlling these behaviors.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Effects of Au2+ irradiation induced damage in a high-entropy pyrochlore oxide single crystal

Here, we report an ion-irradiation study of a compositionally complex (high-entropy) pyrochlore oxide. The damage produced from 4 MeV Au 2+ ion irradiation on single crystal (Yb 0.2 Tm 0.2 Lu 0.2 Ho 0.2 Er 0.2 ) 2 Ti 2 O 7 aligned along the [100] direction is investigated at room temperature by Rutherford backscattering spectrometry in channeling mode (RBS/C). Damage profiles based on RBS/C are presented and compared to single-component pyrochlore titanate oxides to evaluate the relative resistance to irradiation-induced amorphization. The results show that this high-entropy pyrochlore goes amorphous at a dose of 0.13 dpa, which is comparable to that of single-component pyrochlores previously studied. Transmission electron microscopy images unveil the damaged surface layer, which is consistent with the RBS/C results.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Role of chemical disorder on radiation-induced defect production and damage evolution in NiFeCoCr

Understanding chemical disorder in many concentrated solid solution alloys (CSAs) at the levels of electrons and atoms has attracted increasing attention as a path forward to reveal and identify underlying mechanisms for extraordinary mechanical properties and improved radiation tolerance. Single-phase NiFeCoCr CSA is a common base for many high-entropy alloys (HEAs) that have shown improved mechanical strength and radiation tolerance. In this study, defect production and damage evolution in NiFeCoCr under ion irradiation at room temperature to dose over 20 dpa are determined using ion channeling technique along both <100> and <110> directions utilizing multiple probing beam energies. The results obtained from the multi-axial and multi-energy channeling analysis are compared with those previously obtained for Ni crystals irradiated under similar conditions. The influence of chemical complexity on defect production and clustering at early-stage under room temperature irradiation up to dose of 1 dpa is discussed based on positron annihilation spectroscopy results. Defect structure evaluation in Ni and NiFeCoCr is also discussed based on transmission electron microscopy results over a prolonged irradiation at both room and elevated temperatures. Compared with chemically complex NiFeCoCr, larger dislocation loops thus less lattice strain are expected to form in pure Ni. Moreover, the role of chemical disorder in this CSA is also investigated based on ab initio calculations using large supercells. Finally, to understand the impact of chemical complexity effect on defect structure evolution, this integrated research effort attempts to link the relatively large charge redistribution due to difference in valence electron counts resulting from alloying different 3d transition metal elements, moderate lattice distortion arising from similar adaptable atomic size, and notable suppressed or delayed damage evolution in NiFeCoCr.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Reassembled nanoprecipitates resisting radiation

Outstanding resistance to destructive radiation damage in structural alloys is realized by ultra-high-density reversible nanoprecipitate inclusions, and the improvement is attributed to the reordering process of low-misfit superlattices in highly supersaturated matrices.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Role of electronic energy loss on defect production and interface stability: Comparison between ceramic materials and high-entropy alloys

High-entropy alloys (HEAs) and some complex alloys exhibit desirable properties and significant structural stability in harsh environments, including possible applications in advanced reactors. Energetic ion irradiation is often used as a surrogate for neutron irradiation; however, the impact of ion electronic energy deposition and dissipation is often neglected. Moreover, differences in recoil energy spectrum and density of cascade events on damage evolution must also be considered. In many chemically complex alloys, the mean free path of electrons is reduced significantly, thus their decreased thermal conductivity and slow dissipation of localized radiation energy can have noticeable effects on displacement cascade evolution that is greatly different from metals with high thermal conductivity. In this work, nanocrystalline HEAs of Ni 20 Fe 20 Co 20 Cr 20 Cu 20 and nonequiatomic (NiFeCoCr) 97 Cu 3 , both having much lower room-temperature thermal conductivity than pure Ni or Fe, are chosen as model HEAs to reveal the role that electronic energy loss during ion irradiation has in complex alloys. The response of nanocrystalline HEAs is investigated under irradiation at room temperature using MeV Ni and Au ions that have different ratios of electronic energy to damage energy, which is the energy dissipated in displacing atoms. Different from previously reported amorphization of nanocrystalline SiC, experimental results on these HEAs show that, similar to the process in nanocrystalline oxide materials, both inelastic thermal spikes via electron–phonon coupling and elastic thermal spikes via collisions among atomic nuclei contribute to the overall grain growth. The growth follows a power law dependence with the total deposited ion energy, and the derived value of the power-exponent suggests that the irradiation-induced instability at and near grain boundaries leads to local rapid atomic rearrangements and consequently grain growth. The high power-exponent value can be attributed to the sluggish diffusion and delayed defect evolution arising from the chemical complexity intrinsic to HEAs. Here, this work calls attention to quantified fundamental understanding of radiation damage processes beyond that of simplified displacement events, especially in simulating neutron environments.

36 MATERIALS SCIENCE↗