NASA NTRS1982

Zero-gravity growth of a sodium chloride-lithium fluoride eutectic mixture

Continuous and discontinuous lithium fluoride fibers embedded in a sodium chloride matrix were produced in space and on Earth, respectively. The production of continuous fibers in a eutectic mixture was attributed to the absence of convective current in the liquid during solidification in space. Image transmission and optical transmittance measurements of transverse sections of the space-grown and Earth-grown ingots were made with a light microscope and a spectrometer. It was found that better optical properties were obtained from samples grown in space. This was attributed to a better alignment of lithium fluoride fibers along the growth direction.

Yue, A. S.↗

NASA NTRS1977

Zero-gravity growth of NaCl-LiF eutectic. Experiment MA-131

Continuous and discontinuous lithium fluoride fibers embedded in a sodium chloride matrix were produced in space and on earth, respectively. The production of continuous fibers in an eutectic mixture was attributed to the absence of convection current in the liquid during solidification in space. Image transmission and optical transmittance measurements of transverse sections of the space-grown and earth-grown ingots were made with a light microscope and a spectrometer. It was found that better optical properties were obtained from samples grown in space. This was attributed to a better alignment of lithium fluoride fibers along the growth direction.

Yue, A. S.↗

NASA NTRS1976

Halide eutectic growth experiment MA-131

Fiberlike sodium chloride/lithium fluoride eutectic mixtures have been produced on earth and in space by the directional solidification technique. Macroscopic and microscopic examinations were made on longitudinal and transverse sections of Apollo Soyuz Test Project space grown and earth grown ingots. It was found that samples grown in space have a higher percentage of fibers alined with the growth axis. The enhanced alinement of fibers is attributed to the absence of convection currents in the liquid during solidification. Optical transmittance measurements of transverse sections of the space grown and earth grown ingots were performed with an infrared spectrometer. For a given sample thickness, the highest transmittance was obtained from ingots grown in space. For samples of different thicknesses, grown either in space or on earth, it was found that the thinner the sample, the higher the transmittance. This is in agreement with the general optical property of transparent materials.

Yue, A. S.↗