DOE OSTI2024

Multinonmetal-Doped V 2 O 5 Nanocomposites for Lithium-Ion Battery Cathodes

Lithium-ion batteries (LIBs) are critical for portable electronics and electric vehicles, demanding higher energy density to meet increasing energy storage needs. Current commercial cathode materials, such as LiFePO 4 and LiCoO 2 , are limited by a single electron transfer, restricting their energy density. Vanadium pentoxide (V 2 O 5 ) emerges as a promising high-capacity cathode due to its high theoretical capacity of 443 mA h g –1 with three Li storage capacities, significantly surpassing conventional materials. However, the practical application of V 2 O 5 is hindered by a large structural evolution and rapid capacity fading during full lithium intercalation. Here, this study introduces a multinonmetal doping (MNM) strategy to enhance V 2 O 5 cathodes by incorporating all-nonmetal dopants (B, P, and Si) and graphene (G). MNM-V 2 O 5 -G exhibits increased surface oxygen defects, improving charge transfer kinetics and thus enhancing the rate performance and cycling stability. Our results provide valuable insights into the role of surface oxygen defects in stabilizing V 2 O 5 with element doping. This research highlights the potential of multinonmetal doping to improve LIB cathode materials, offering a promising pathway for design of high-energy-density V 2 O 5 cathodes and advancing the development of next-generation energy storage solutions.

25 ENERGY STORAGE↗

DOE OSTI2024

Stabilizing Graphite Anode in Electrolytes with Nanoscale Anion Networking for High-Rate Lithium Storage

Graphite is the preferred anode material in commercial lithium-ion batteries (LIBs), but its limited compatibility with various organic molecules restricts the electrolyte solvent options. The primary challenge is solvent co-intercalation with Li ions, leading to graphite layer exfoliation. As a result, electrolyte selection often relies on ethylene carbonate (EC)-based solvents. Here, in this study, we introduce electrolytes featuring a nanoscale anion network ordering that hinders the liquid-phase exfoliation of graphite. This network, formed from concentrated long-chain lithium salts, traps free dioxolane (DOL) molecules, reducing the interactions between graphite particles and solvents during Li intercalation. Our findings reveal a mechanism that stabilizes graphite in otherwise unstable solvents with concentrated salts like LiTFSI, providing key insights for improving LIB performance by addressing electrolyte limitations on graphite anodes.

77 NANOSCIENCE AND NANOTECHNOLOGY↗

DOE OSTI2023

Boosting the Low-Temperature Performance of Graphite Anodes by Creating an Electrochemically Active Interface

Graphite is the major anode material used in commercial lithium-ion batteries (LIBs). However, the sluggish ion-transfer kinetics associated with graphite anodes significantly restrict the operation of LIBs over a wide temperature. This is primarily due to their low reversible capacity and the substantial overpotential exhibited under low-temperature conditions. To address this limitation, we demonstrate herein an approach that involves grafting an electrochemically active lithium benzenesulfonate layer onto a graphite surface through a typical reduction reaction of diazonium cations, followed by ion exchange process. This surface modification reduces the charge transfer resistance of graphite anodes, leading to an excellent reversible capacity of ~150 mAh g –1 at low-temperatures (-20 °C, 0.1C). Electrochemical impedance spectroscopy indicates that both desolvation of the lithium ions outside the graphite, and lithium diffusion within the solid electrolyte interphase and graphite lattice are two crucial rate-limiting steps during the Li (de)lithiation, with the latter dominating during the low-temperature operation. In conclusion, these findings demonstrate a facile method for enhancing the low-temperature performance of graphite through surface modification and provide valuable insights into fundamental understandings that can guide the future design of better -low-temperature graphite anodes.

25 ENERGY STORAGE↗

DOE OSTI2023

Kinetic pathways of fast lithium transport in solid electrolyte interphases with discrete inorganic components

The transport of lithium ions in the solid electrolyte interphase (SEI) has been previously accepted to proceed in two steps: a fast pore diffusion through the outer, porous organic layer followed by a slow knock-off or vacancy diffusion in the inner, dense inorganic layer. The second step is believed to be the rate-limiting step during fast-charging. In this study, we have intentionally constructed a thicker SEI (SEI-rich) structure on the surface of monoclinic Nb 2 O 5 (H-Nb 2 O 5 ) by adding LiNO 3 into a conventional ethylene carbonate based electrolyte. The electrochemical performance of two electrodes, one SEI-rich and one with few SEI (SEI-lean), was found to be almost the same, including their fast-charging capability and cycling stability, despite the significant difference in their SEI structure. Importantly, analysis using cryogenic scanning/transmission electron microscopy showed the discrete decoration of individual inorganic particles (e.g., Li 2 O) and amorphous species (LiN x O y /organic components) over the surface of H-Nb 2 O 5 . These discrete inorganic particles are in contradiction to the formation of dense inner inorganic layer, which has been commonly postulated. Based on these findings, we propose a new mechanism for Li ion transport through the SEI: one-step pore diffusion, without the second step slow diffusion. This one-step pore diffusion process provides an extremely fast Li ion transport, and effectively removes the kinetic limitation of Li ion transport in the SEI for fast charging. Finally, these results strongly suggest that the influence of SEI structure on the transport kinetics of lithium ions is much less significant than previously accepted. These results offer a new understanding of possible lithium ion transport pathway within SEI and may have implications for the future designs of fast-charging battery materials.

25 ENERGY STORAGE↗

DOE OSTI2023

Amino-tethering synthesis strategy toward highly accessible sub-3-nm L1 0 -PtM catalysts for high-power fuel cells

Because of the poor accessibility of embedded active sites, platinum (Pt)-based electrocatalysts suffer from insufficient Pt utilization and mass transport in membrane electrode assemblies (MEAs), limiting their performance in polymer electrolyte membrane fuel cells. Here, we report a simple and universal approach to depositing sub-3-nm L1 0 -PtM nanoparticles over external surfaces of carbon supports through pore-tailored amino (NH 2 )-modification, which enables not only excellent activity for the oxygen reduction reaction, but also enhanced Pt utilization and mass transport in MEAs. Using a low loading of 0.10 mg Pt ∙cm -2 , the MEA of PtCo/KB-NH 2 delivered an excellent mass activity of 0.691 A∙mgPt -1 , a record-high power density of 0.96 W∙cm -2 at 0.67 V, and only a 30-mV drop at 0.80 A∙cm -2 after 30,000 voltage cycles, which meets nearly all targets set by the Department of Energy. Finally, this work provides an efficient strategy for designing advanced Pt-based electrocatalysts and realizing high-power fuel cells.

32 ENERGY CONSERVATION, CONSUMPTION, AND UTILIZATI↗

DOE OSTI2023

Reversible Iron Oxyfluoride (FeOF)–Graphene Composites as Sustainable Cathodes for High Energy Density Lithium Batteries

Two large barriers are impeding the wide implementation of electric vehicles, namely driving-range and cost, primarily due to the low specific energy and high cost of mono-valence cathodes used in lithium-ion batteries. Iron is the ideal element for cathode materials considering its abundance, low cost and toxicity. However, the poor reversibility of (de)lithiation and low electronic conductivity prevent iron-based high specific energy multi-valence conversion cathodes from practical applications. In this work, a sustainable FeOF nanocomposite is developed with extraordinary performance. The specific capacity and energy reach 621 mAh g –1 and 1124 Wh kg –1 with more than 100 cycles, which triples the specific capacity, and doubles the specific energy of current mono-valence intercalation LiCoO 2 . This is the result of an effective approach, combing the nanostructured FeOF with graphene, realized by making the (de)lithiation reversible by immobilizing FeOF nanoparticles and the discharge products over the graphene surface and providing the interparticle electric conduction. Importantly, it demonstrates that introducing small amount of graphene can create new materials with desired properties, opening a new avenue for altering the (de)lithiation process. Finally, such extraordinary performance represents a significant breakthrough in developing sustainable conversion materials, eventually overcoming the driving range and cost barriers.

25 ENERGY STORAGE↗

DOE OSTI2022

Achieving SEI preformed graphite in flow cell to mitigate initial lithium loss

The irreversible lithium loss due to the formation of solid electrolyte interphase (SEI) in the initial cycle on the graphite anode greatly reduces the overall cell energy density of lithium ion batteries, that is, the lost Li ions from forming SEI lead to the decrease of Li ions for the intercalation. The method of cathode prelithiation has been widely explored to compensate this lithium loss. However, these cathode additives with high lithium contents inevitably lower the loading of the cathode active materials. In this work, we report a novel approach to solve this challenge, a facile graphite prelithiation method by preforming SEI layers on the surface of graphite powders (Pre-SEI graphite) utilizing a specially designed flow cell. The Li accommodation in the graphite anode can be controlled by the operating time and current density in the flow cell for the electrochemical SEI formation. As a result, we demonstrate a 10% initial Columbic efficiency increase of the LiFePO 4 electrode in a full cell configuration using the Pre-SEI graphite, compared with the pristine graphite anode. The electrochemical preformation of SEI on the graphite powders offers a complete solution to offset initial lithium loss without a sacrifice of active cathode material loading.

25 ENERGY STORAGE↗

DOE OSTI2022

Approaching theoretical specific capacity of iron-rich lithium iron silicate using graphene-incorporation and fluorine-doping

Lithium iron silicate, Li 2 FeSiO 4 , is a promising cathode material for lithium ion batteries due to its high theoretical specific capacity, earth abundance, low cost, and environmental friendliness. The challenges of Li 2 FeSiO 4 as a practical cathode material are (1) the low electronic and ionic conductivity and (2) the low discharge voltage. The approach of incorporating graphene sheets into the nanostructure of Li 2 FeSiO 4 is used for dealing with the low conductivities while fluorine doping is intended to increase the discharge voltage. The fluorine-doped and graphene-incorporated iron-rich lithium iron silicate F-LFSO/G nanomaterials were successfully synthesized using a facile/efficient hydrothermal method with excellent performance, 328.43 mA h g -1 at 0.1C rate, approaching their theoretical specific capacity, 99% of 331 mA h g -1 . This clearly reveals that the reversible (de)lithiation of 2 Li + ions per F-LFSO has been realized as a result of these approaches. The (de)lithiation process has been studied using in operando high energy synchrotron X-ray absorption near edge spectroscopy and X-ray photoelectron spectroscopy aided by theoretical modeling, which reveals that F doping deeply changes the O electron configuration in F-LFSO, and consequently makes the Li + ion transfer easier, while the reversible redox of oxygen can be utilized to achieve high specific capacity.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗