Structural Studies of Alloyed and Nanoparticle Transition Metal Dichalcogenides by Selenium-77 Solid-State Nuclear Magnetic Resonance Spectroscopy
Layered transition metal dichalcogenides (TMDCs) such as MoS 2 , MoSe 2 , and WSe 2 are under intense investigation because they are atomically thin semiconductors with photophysical properties that can be tuned by changing their composition or morphology. Mechanochemical processing has been proposed as a method to obtain alloyed TMDCs in the series Mo 1–x W x S y Se 2–y (x = 0–1; y = 0–2). However, elucidating the chemical transformations occurring at the atomic scale following mechanochemical processing can be challenging because the products are often amorphous or microcrystalline. To address this challenge, we probe TMDC mixing and alloying by using a combination of powder X-ray diffraction, Raman spectroscopy, diffuse reflectance spectroscopy, 77 Se solid-state nuclear magnetic resonance (SSNMR) spectroscopy, and planewave density functional theory (DFT) calculations. The nature of the milling material and reaction atmosphere are shown to be essential factors in limiting the formation of undesired oxide byproducts. We demonstrate acquisition of 77 Se SSNMR spectra using different combinations of Carr-Purcell Meiboom-Gill acquisition (CPMG) pulse sequences, magic angle spinning (MAS), and MAS dynamic nuclear polarization. Further, the combination of SSNMR with the other characterization methods clearly demonstrates that high energy impact ball milling induces molecular level alloying of Mo, W and chalcogen atoms in the family Mo 1–x W x S y Se 2–y . Gauge including projector augmented wave DFT calculations yield accurate 77 Se chemical shift (CS) tensor components. 77 Se SSNMR spectroscopy was also applied to study the structure of WSe 2 nanocrystals intercalated with ethylenediamine. The intercalated WSe 2 nanocrystals exhibit a more positive isotropic 77 Se CS as compared to bulk WSe 2 , however, the 77 Se CS anisotropy is the same, confirming the WSe 2 layers have a similar structure as in their bulk counterparts.