DOE OSTI2024

Electro-Chemo-Mechanical Evolution at the Garnet Solid Electrolyte–Cathode Interface

Solid-state batteries promise higher energy density and improved safety compared with lithium-ion batteries. However, electro-chemomechanical instabilities at the solid electrolyte interface with the cathode and the anode hinder their large scale implementation. Here, in this study, we focus on resolving electro-chemo-mechanical instability mechanisms and their onset conditions between a state-of-the-art cathode, LiNi 0.6 Mn 0.2 Co 0.2 O 2 (NMC622), and the garnet Li 7 La 3 Zr 2 O 12 (LLZO) solid electrolyte. We used thin-film NMC622 on LLZO pellets to place the interfacial region within the detection depth of the X-ray characterization techniques. The experimental probes of the near-interface region included in operando X-ray absorption spectroscopy and ex situ focused ion beam scanning electron microscopy. Electrochemical degradation was not observable during cycling at room temperature with 4.3 V versus Li/Li + charge voltage cutoff, or with stepwise potentiostatic hold up to 4.1 V versus Li/Li + . In contrast, secondary phases including reduced transition metal species (Ni 2+ , Co 2+ ) were found after cycling up to 4.3 V versus Li/Li + at 80 °C and during potentiostatic hold at 4.3 V versus Li/Li + (Ni 2+ ). Intergranular cracks between NMC622 grains and delamination at the NMC622|LLZO interface occurred readily after the first charge. These interface reaction products and mechanical failure lowered the capacity and cell efficiency due to partial loss of the NMC622 phase, partial loss of contact at the interface, and a higher polarization resistance. Electrochemical instability between delithiated NMC622 and LLZO could be mitigated by using a low charge voltage cutoff or cycling at lower temperature. Ways to engineer the mechanical properties to avoid crack deflection and delamination at the interface are also discussed for enhancing mechanical stability.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Uncovering fast solid-acid proton conductors based on dynamics of polyanion groups and proton bonding strength

Achieving high proton conductivity in inorganic solids is key for advancing many electrochemical technologies, including low-energy nano-electronics and energy-efficient fuel cells and electrolyzers. A quantitative understanding of the physical traits of a material that regulate proton diffusion is necessary for accelerating the discovery of fast proton conductors. In this work, we have mapped the structural, chemical and dynamic properties of solid acids to the elementary steps of the Grotthuss mechanism of proton diffusion. Our approach combines ab initio molecular dynamics simulations, analysis of phonon spectra and atomic structure calculations. We have identified the donor–hydrogen bond lengths and the acidity of polyanion groups as key descriptors of local proton transfer and the vibrational frequencies of the cation framework as the key descriptor of lattice flexibility. The latter facilitates rotations of polyanion groups and long-range proton migration in solid acid proton conductors. The calculated lattice flexibility also correlates with the experimentally reported superprotonic transition temperatures. Using these descriptors, we have screened the Materials Project database and identified potential solid acid proton conductors with monovalent, divalent and trivalent cations, including Ag + , Sr 2+ , Ba 2+ and Er 3+ cations, which go beyond the traditionally considered monovalent alkali cations (Cs + , Rb + , K + , and NH 4 + ) in solid acids.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2024

Hydrogen in energy and information sciences

Beyond its fascinating chemistry as the first element in the Periodic Table, hydrogen is of high societal importance in energy technologies and of growing importance in energy-efficient computing. In energy, hydrogen has reemerged as a potential solution to long-term energy storage and as a carbon-free input for materials manufacturing. Its utilization and production rely on the availability of proton-conducting electrolytes and mixed proton–electron conductors for the components in fuel cells and electrolyzers. In computing, proton mediation of electronic properties has garnered attention for electrochemically controlled energy-efficient neuromorphic computing. Incorporation of substitutional and interstitial hydride ions in oxides, though only recently established, enables tuning of electronic and magnetic properties, inviting a range of possible exotic applications. This article addresses common themes in the fundamental science of hydrogen incorporation and transport in oxides as relevant to pressing technological needs. The content covers (1) lattice (or bulk) mechanisms of hydrogen transport, primarily addressing proton transport, but also touching on hydride ion transport; (2) interfacial transport; (3) exploitation of extreme external drivers to achieve unusual response; and (4) advances in methods to probe the hydrogen environment and transport pathway. The snapshot of research activities in the field of hydrogen-laden materials described here underscores exciting recent breakthroughs, remaining open questions, and breathtaking experimental tools now available for unveiling the nature of hydrogen in solid-state matter.

08 HYDROGEN↗
DOE OSTI2023

Charge trapping at Al/Al 2 ⁢O 3 interface facilitates hydrogen-induced superabundant metal vacancy formation

Hydrogen is a ubiquitous impurity that deteriorates the metal/oxide interface, causing challenges such as current leakage and blistering. Here, in this work, we uncover the mechanisms behind hydrogen-induced damage at the prototypical Al/A⁢l 2 ⁢O 3 interface. The precursor that we identify is charge trapping at the interface, which facilitates hydrogen segregation to the interface plane as H – . Presence of hydrogen increases aluminum vacancy concentration at the interfacial metal and oxide planes. Each Al vacancy can trap multiple hydrogen atoms. As a result, the interfacial aluminum vacancy and hydrogen concentrations increase by orders of magnitude. Additionally, hydrogen behaves as an n-type dopant and increases electronic conductivity at the oxide layer adjacent to the interface by forming H + , and the [V Al –H] complex is the predominant defect at this layer. These findings provide the precursor mechanisms of hydrogen-induced damage at the metal-oxide interfaces and have implications for advancing Al/A⁢l 2 ⁢O 3 –based coatings and electronic devices.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2023

Roadmap on exsolution for energy applications

Over the last decade, exsolution has emerged as a powerful new method for decorating oxide supports with uniformly dispersed nanoparticles for energy and catalytic applications. Due to their exceptional anchorage, resilience to various degradation mechanisms, as well as numerous ways in which they can be produced, transformed and applied, exsolved nanoparticles have set new standards for nanoparticles in terms of activity, durability and functionality. In conjunction with multifunctional supports such as perovskite oxides, exsolution becomes a powerful platform for the design of advanced energy materials. In the following sections, we review the current status of the exsolution approach, seeking to facilitate transfer of ideas between different fields of application. We also explore future directions of research, particularly noting the multi-scale development required to take the concept forward, from fundamentals through operando studies to pilot scale demonstrations.

25 ENERGY STORAGE↗
DOE OSTI2023

Fast Surface Oxygen Release Kinetics Accelerate Nanoparticle Exsolution in Perovskite Oxides

Exsolution is a recent advancement for fabricating oxide-supported metal nanoparticle catalysts via phase precipitation out of a host oxide. A fundamental understanding and control of the exsolution kinetics are needed to engineer exsolved nanoparticles to obtain higher catalytic activity toward clean energy and fuel conversion. Since oxygen release via oxygen vacancy formation in the host oxide is behind oxide reduction and metal exsolution, we hypothesize that the kinetics of metal exsolution should depend on the kinetics of oxygen release, in addition to the kinetics of metal cation diffusion. In this report we probe the surface exsolution kinetics both experimentally and theoretically using thin-film perovskite SrTi 0.65 Fe 0.35 O 3 (STF) as a model system. We quantitatively demonstrated that in this system the surface oxygen release governs the metal nanoparticle exsolution kinetics. As a result, by increasing the oxygen release rate in STF, either by reducing the sample thickness or by increasing the surface reactivity, one can effectively accelerate the Fe 0 exsolution kinetics. Fast oxygen release kinetics in STF not only shortened the prereduction time prior to the exsolution onset, but also increased the total quantity of exsolved Fe 0 over time, which agrees well with the predictions from our analytical kinetic modeling. The consistency between the results obtained from in situ experiments and analytical modeling provides a predictive capability for tailoring exsolution, and highlights the importance of engineering host oxide surface oxygen release kinetics in designing exsolved nanocatalysts.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Degradation and recovery of solid oxide fuel cell performance by control of cathode surface acidity: Case study – Impact of Cr followed by Ca infiltration

Solid oxide fuel cells (SOFC) have attracted attention as clean and efficient energy conversion devices with low emissions. However, several degradation mechanisms limit the electrochemical performance of current SOFCs, with cathode degradation due to Cr-poisoning from metal interconnects particularly problematic. The acidity/basicity of binary additives has been found to be a sensitive descriptor of the oxygen exchange kinetics, indicating that acidic Cr-species/basic Ca-species can be expected to deactivate/activate the cathode surface, respectively. Inspired by recent advances, the feasibility of relative acidity as a tool for reviving degraded SOFCs is demonstrated by neutralizing Cr-poisoned SOFCs by subsequent serial infiltration of Ca-species. Furthermore, a model mixed ionic and electronic conducting oxide, Pr 0.1 Ce 0.9 O 2-δ (PCO), is selected as the cathode material. Area-specific resistances (ASR) of symmetric cells obtained by electrochemical impedance spectroscopy show that Cr-infiltration results in a seven-fold increase in ASR, while subsequent infiltration of Ca-species leads to complete recovery. Performance degradation and recovery are attributed to depressed/enhanced redox properties at the PCO surface, as supported by XPS analysis. Experiments using anode-supported fuel cells show a reduction in peak power density by 26% upon Cr-infiltration, reversed following Ca-infiltration, after which no degradation is observed during subsequent operation for 100 h.

(Pr,Ce)O2-δ↗
DOE OSTI2022

Electronegative metal dopants improve switching variability in Al 2 ⁢O 3 resistive switching devices

Resistive random-access memories are promising for nonvolatile memory and brain-inspired computing applications. High variability and low yield of these devices are key drawbacks hindering reliable training of physical neural networks. In this paper, we show that doping an oxide electrolyte, Al 2 ⁢O 3 , with electronegative metals makes resistive switching significantly more reproducible, surpassing the reproducibility requirements for obtaining reliable hardware neuromorphic circuits. Based on density functional theory calculations, the underlying mechanism is hypothesized to be the ease of creating oxygen vacancies in the vicinity of electronegative dopants due to the capture of the associated electrons by dopant midgap states and the weakening of Al-O bonds. These oxygen vacancies and vacancy clusters also bind significantly to the dopant, thereby serving as preferential sites and building blocks in the formation of conducting paths. Throughout this work, we validate this theory experimentally by implanting different dopants over a range of electronegativities in devices made of multiple alternating layers of Al 2 ⁢O 3 and WN and find superior repeatability and yield with highly electronegative metals, Au, Pt, and Pd. These devices also exhibit a gradual SET transition, enabling multibit switching that is desirable for analog computing.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Electrochemical pumping: An alternative solution for hydrogen embrittlement

Hydrogen embrittlement is a form of chemo-mechanical damage that is special in that it can be partially reversible. Here, in this paper, we propose a method for recovering structural alloys from hydrogen embrittlement at room temperature by electrochemically biased desorption of hydrogen. We demonstrate that the method can enable the reversion of hydrogen-induced degradation of mechanical properties, by comparing the mechanical behavior of commercial stainless steel specimens at different hydrogen charging and desorption states. These case studies also reveal the influence of electrochemical potential, H content and the characteristics of H trapping sites, on the effectiveness of this recovery approach. The limitations arising from the presence of unhealable forms of hydrogen damage, and the generic applicability of this electrochemically-assisted recovery method are also discussed.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Exsolution-Driven Surface Transformation in the Host Oxide

Exsolution synthesizes self-assembled metal nanoparticle catalysts via phase precipitation. An overlooked aspect in this method thus far is how exsolution affects the host oxide surface chemistry and structure. Such information is critical as the oxide itself can also contribute to the overall catalytic activity. Here, combining X-ray and electron probes, we investigated the surface transformation of thin-film SrTi 0.65 Fe 0.35 O 3 during Fe 0 exsolution. We found that exsolution generates a highly Fe-deficient near-surface layer of about 2 nm thick. Moreover, the originally single-crystalline oxide near-surface region became partially polycrystalline after exsolution. Such drastic transformations at the surface of the oxide are important because the exsolution-induced nonstoichiometry and grain boundaries can alter the oxide ion transport and oxygen exchange kinetics and, hence, the catalytic activity toward water splitting or hydrogen oxidation reactions. These findings highlight the need to consider the exsolved oxide surface, in addition to the metal nanoparticles, in designing the exsolved nanocatalysts.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Strain-Dependent Surface Defect Equilibria of Mixed Ionic-Electronic Conducting Perovskites

We report understanding the surface defect chemistry and its strain dependency is essential in developing next-generation electrochemical devices. However, due to their nanoscale dimensions, surface defects cannot be accessed by conventional techniques used in bulk defect studies. Here, we constructed the strain-dependent surface defect equilibria (i.e., the Brouwer diagram) of mixed ionic-electronic conducting perovskite oxides with near ambient pressure X-ray absorption spectroscopy. Using coherently strained thin-film La 0.6 Sr 0.4 Fe O3 (LSF) as model systems, we probed their surface defect equilibria at 400 °C in oxygen partial pressures between 1 to 10 -5 Torr. We found that the electron holes on the LSF surfaces have strong oxygen character, regardless of the strain states. Nevertheless, tensile strain makes the LSF surface more reducible than the compressed counterpart. These two observations were then validated using first-principles calculations. Finally, with the aid of thermodynamic analyses, we showed that the strain-dependent surface defect equilibria of LSF can be captured by bulk-like ideal solution defect models with shifted oxygen chemical potentials. The findings and methodology presented in this study enable quantitative determination of the surface defect chemistry, which is crucial to understanding and designing functional surfaces for efficient conversions of energy and fuels.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Anodic Shock-Triggered Exsolution of Metal Nanoparticles from Perovskite Oxide

Nanoparticles decorated electrodes (NDEs) are useful in fuel cells, electrolyzers, water treatment, and chemical synthesis. Here, in this study, we show that by rapidly bringing a mixed ionic-electronic conductor outside its electrochemical stability window, one can achieve uniform dispersion of metallic nanoparticles inside its bulk and at the surface and improve its electrocatalytic performance when back under normal functional conditions. Surprisingly, this can happen under anodic as well as cathodic current/voltage shocks in an ABO 3 perovskite oxide, La 0.4 Ca 0.4 Ti 0.88 Fe 0.06 Ni 0.06 O 3-δ (LCTFN), across a wide range of H 2 /O 2 gas environments at 800 °C. One possible mechanism for bulk Fe 0 /Ni 0 precipitation under anodic shock condition is the incomplete oxygen oxidation (O 2 – → O α– , 0 < α < 2), migration and escape of oxygen to interfaces, and “whiplash” transition-metal reduction due to low electronic conductivity. We show that both cathodic and anodic shocks can produce NDEs to enhance electrocatalytic performance, potentially improving the flexibility of this approach in practical devices.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Avoiding CO 2 Improves Thermal Stability at the Interface of Li 7 La 3 Zr 2 O 12 Electrolyte with Layered Oxide Cathodes

Abstract Solid‐state batteries promise higher energy densities and better safety than Li‐ion batteries with liquid electrolytes. However, the interface between solid electrolyte and cathode is unstable at the elevated temperatures that are needed while sintering to achieve good bonding between ceramic components. Here, the hypothesis is that, the gas environment, especially the presence of CO 2, is critical in determining the stability of the solid electrolyte–cathode interface. The effect of gas species on the interface is systematically probed, by a using Li 7 La 3 Zr 2 O 12 (LLZO) solid electrolyte with a thin film LiNi 0.6 Mn 0.2 Co 0.2 O 2 cathode as a model system to enable interface sensitivity. Detrimental phases formed at the interface and their onset conditions are identified by X‐ray absorption spectroscopy, X‐ray diffraction, and Gibbs free energy analysis. As a result, removing CO 2 and minimizing H 2 O(g) during sintering is necessary to obtain good contact at the LLZO|cathode interface without forming secondary phases. Sintering in O 2 is ideal, yielding excellent chemical stability and low interfacial resistance. Secondary phases also do not form in N 2, but oxygen loss occurs at elevated temperatures. The interfacial resistance obtained upon sintering in pure O 2 is comparable to the lowest values at LLZO interfaces with protective coatings, but here without the need for interface coatings.

25 ENERGY STORAGE↗