Artifact identification in X-ray diffraction data using machine learning methods
In situ synchrotron high-energy X-ray powder diffraction (XRD) is highly utilized by researchers to analyze the crystallographic structures of materials in functional devices ( e.g. battery materials) or in complex sample environments ( e.g. diamond anvil cells or syntheses reactors). An atomic structure of a material can be identified by its diffraction pattern along with a detailed analysis of the Rietveld refinement which yields rich information on the structure and the material, such as crystallite size, microstrain and defects. For in situ experiments, a series of XRD images is usually collected on the same sample under different conditions ( e.g. adiabatic conditions) yielding different states of matter, or is simply collected continuously as a function of time to track the change of a sample during a chemical or physical process. In situ experiments are usually performed with area detectors and collect images composed of diffraction patterns. For an ideal powder, the diffraction pattern should be a series of concentric Debye–Scherrer rings with evenly distributed intensities in each ring. For a realistic sample, one may observe different characteristics other than the typical ring pattern, such as textures or preferred orientations and single-crystal diffraction spots. Textures or preferred orientations usually have several parts of a ring that are more intense than the rest, whereas single-crystal diffraction spots are localized intense spots owing to diffraction of large crystals, typically >10 µm. In this work, an investigation of machine learning methods is presented for fast and reliable identification and separation of the single-crystal diffraction spots in XRD images. The exclusion of artifacts during an XRD image integration process allows a precise analysis of the powder diffraction rings of interest. When it is trained with small subsets of highly diverse datasets, the gradient boosting method can consistently produce high-accuracy results. The method dramatically decreases the amount of time spent identifying and separating single-crystal diffraction spots in comparison with the conventional method.