Engineering topics
Publications and source records attributed to Yang, Mengjin.
Although a harsher condition, degradation of perovskite solar cells in an open-circuit condition is related to the performance in a quasi-maximum power point condition. Further, shadow masks should be used during illuminated stability studies.
Metal halide perovskite photovoltaic performance required for commercial technology encompasses both efficiency and stability. Advances in both these parameters have recently been reported; however, these strategies are often difficult to directly compare due to differences in perovskite composition, device architecture, fabrication methods, and accelerated stressors applied in stability tests. In particular, it is found that there is a distinct lack of elevated temperature, operational (light and bias) stability data. Furthermore, significant testing is required to understand the interactions when combinations are used (e.g., additives used with posttreatments). Herein, individual and combined additive, posttreatment, and contact layer strategies from recent literature reports under standardized operational stability tests of p-i-n CsMAFA perovskites at 70 degrees C are evaluated. Through analysis of over 1000 devices, it is concluded that the hole-transport layer (HTL) is the most significant component impacting elevated temperature operational stability. This analysis motivates future development of high-performance HTLs.
Methods are described that include contacting an alkyl ammonium metal halide film with an alkyl ammonium halide, where the alkyl ammonium metal halide film includes a first halogen and a metal, the alkyl ammonium halide includes a second halogen, such that the contacting forms an alkyl ammonium metal mixed-halide film that interfaces with the alkyl ammonium metal halide film, where the alkyl ammonium metal mixed-halide film includes the first halogen, the second halogen, and the metal.
Abstract The rapidly increasing solar conversion efficiency (PCE) of hybrid organic–inorganic perovskite (HOIP) thin‐film semiconductors has triggered interest in their use for direct solar‐driven water splitting to produce hydrogen. However, application of these low‐cost, electronic‐structure‐tunable HOIP tandem photoabsorbers has been hindered by the instability of the photovoltaic‐catalyst‐electrolyte (PV+E) interfaces. Here, photolytic water splitting is demonstrated using an integrated configuration consisting of an HOIP/n + silicon single junction photoabsorber and a platinum (Pt) thin film catalyst. An extended electrochemical (EC) lifetime in alkaline media is achieved using titanium nitride on both sides of the Si support to eliminate formation of insulating silicon oxide, and as an effective diffusion barrier to allow high‐temperature annealing of the catalyst/TiO 2 ‐protected‐n + silicon interface necessary to retard electrolytic corrosion. Halide composition is examined in the (FA 1‐x Cs x )PbI 3 system with a bandgap suitable for tandem operation. A fill factor of 72.5% is achieved using a Spiro‐OMeTAD‐hole‐transport‐layer (HTL)‐based HOIP/n + Si solar cell, and a high photocurrent density of −15.9 mA cm −2 (at 0 V vs reversible hydrogen electrode) is attained for the HOIP/n + Si/Pt photocathode in 1 m NaOH under simulated 1‐sun illumination. While this thin‐film design creates stable interfaces, the intrinsic photo‐ and electro‐degradation of the HOIP photoabsorber remains the main obstacle for future HOIP/Si tandem PEC devices.
Metal halide perovskite solar cells have reached a critical point in their development. At a current certified record efficiency of 25.7% for a single-junction, research-scale cell, they now garner serious attention from the solar cell industry as a promising route to widespread, low-cost photovoltaics in single- or tandem-junction configurations. However, more work to demonstrate their durability under real-world outdoor test conditions is necessary to ensure the long-term success and deployment of the technology. Differences in chemistry, processes, and their combination result in unique performance limiters for both efficiency and stability. Further, as many active formulations and layer/cell stack combinations are sensitive to temperature, air, and moisture, it is important to separate intrinsic limitations to stability relative to these extrinsic sources. This presents a particular need for the development of an appropriate and reliable package for environmental (i.e., accelerated and outdoor) testing that will permit these different factors to be evaluated and understood.
An aspect of the present disclosure is a method that includes exchanging at least a portion of a first cation of a perovskite solid with a second cation, where the exchanging is performed by exposing the perovskite solid to a precursor of the second cation, such that the precursor of the second cation oxidizes to form the second cation and the first cation reduces to form a precursor of the first cation.
As lead halide perovskites (LHPs) continue to achieve success as a light-harvesting material in perovskite solar cells (PSCs), exploring and understanding other materials in the device stack become increasingly important. Particularly, selection of suitable hole transport materials (HTMs) that demonstrate high performance and stability is imperative in the design of P-I-N PSCs. Presented here are a family of 12 structurally related polymers based on either fluorene or carbazole main chains with select aromatic side groups that introduce tunable properties for use in PSCs. How properties such as the highest occupied molecular orbital energy level, conductivity, glass-transition temperature, and wettability of the HTM affect the PSC performance is explored. Devices that incorporate the polymer HTMs perform well relative to PTAA in benchmark P-I-N PSC architectures while exhibiting similar or superior stability under accelerated aging studies. The relative synthetic simplicity and resultant performance of the HTMs in PSCs coupled with the ability to customize properties with different functional groups demonstrates the potential of this family of HTMs for a variety of LHP materials.
All-perovskite tandem solar cells are promising for achieving photovoltaics with power conversion efficiencies above the detailed balance limit of single-junction cells, while retaining the low cost, light weight and other advantages associated with metal halide perovskite photovoltaics. However, the efficiency and stability of all-perovskite tandem cells are limited by the Sn-Pb-based narrow-bandgap perovskite cells. Here we show that the formation of quasi-two-dimensional (quasi-2D) structure (PEA) 2 GAPb 2 I 7 from additives based on mixed bulky organic cations phenethylammonium (PEA+) and guanidinium (GA+) provides critical defect control to substantially improve the structural and optoelectronic properties of the narrow-bandgap (1.25 eV) Sn-Pb perovskite thin films. Additionally, this 2D additive engineering results in Sn-Pb-based absorbers with low dark carrier density (~1.3 x 10 14 cm -3 ), long bulk carrier lifetime (~9.2 us) and low surface recombination velocity (~1.4 cm s -1 ), leading to 22.1%-efficient single-junction Sn-Pb perovskite cells and 25.5%-efficient all-perovskite two-terminal tandems with high photovoltage and long operational stability.