Various zinc anodes with increasing calcium zincate (0%, 30%, 70%, 100%) were cycled at 50% theoretical Zn utilization to investigate cycle life and estimated cost. Failure mechanisms of majority 70% Zn/30% CaZn anodes are compared with pure CaZn.
The relationship between structure and performance in alkaline Zn batteries is undeniable, where anode utilization, dendrite formation, shape change, and passivation issues are all addressable through anode morphology. While tailoring 3D hosts can improve the electrode performance, these practices are inherently limited by scaffolds that increase the mass or volume. Herein, a direct write strategy for producing template‐free metallic 3D Zn electrode architectures is discussed. Concentrated inks are customized to build designs with low electrical resistivity (5 × 10 −4 Ω cm), submillimeter sizes (200 μm filaments), and high mechanical stability (Young's modulus of 0.1–0.5 GPa at relative densities of 0.28–0.46). A printed Zn lattice anode versus NiOOH cathode with an alkaline polymer gel electrolyte is then demonstrated. This Zn||NiOOH cell operates for over 650 cycles at high rates of 25 mA cm −2 with an average areal capacity of 11.89 mAh cm −2 , a cumulative capacity of 7.8 Ah cm −2 , and a volumetric capacity of 23.78 mAh cm −3 . A thicker Zn anode achieves an ultrahigh areal capacity of 85.45 mAh cm −2 and a volumetric capacity of 81.45 mAh cm −3 without significant microstructural changes after 50 cycles.
A method of operating a battery comprises discharging a cathode comprising manganese dioxide to within a 2nd electron capacity of the manganese dioxide at a C-rate of equal to or slower than C/10, recharging the battery, and cycling the battery during use a plurality of times. The cathode is in a battery, and the battery comprises the cathode, an anode, a separator disposed between the anode and the cathode, and an electrolyte. The cathode comprises the manganese dioxide and a conductive carbon. The anode comprises: a metal component and a conductive carbon. The metal component can be a metal, metal oxide, or metal hydroxide, and the metal of the metal component can be zinc, lithium, aluminum, magnesium, iron, cadmium and a combination thereof.
Abstract not provided.
Abstract not provided.
Abstract not provided.