DOE OSTI2022

Role of chemical disorder on radiation-induced defect production and damage evolution in NiFeCoCr

Understanding chemical disorder in many concentrated solid solution alloys (CSAs) at the levels of electrons and atoms has attracted increasing attention as a path forward to reveal and identify underlying mechanisms for extraordinary mechanical properties and improved radiation tolerance. Single-phase NiFeCoCr CSA is a common base for many high-entropy alloys (HEAs) that have shown improved mechanical strength and radiation tolerance. In this study, defect production and damage evolution in NiFeCoCr under ion irradiation at room temperature to dose over 20 dpa are determined using ion channeling technique along both <100> and <110> directions utilizing multiple probing beam energies. The results obtained from the multi-axial and multi-energy channeling analysis are compared with those previously obtained for Ni crystals irradiated under similar conditions. The influence of chemical complexity on defect production and clustering at early-stage under room temperature irradiation up to dose of 1 dpa is discussed based on positron annihilation spectroscopy results. Defect structure evaluation in Ni and NiFeCoCr is also discussed based on transmission electron microscopy results over a prolonged irradiation at both room and elevated temperatures. Compared with chemically complex NiFeCoCr, larger dislocation loops thus less lattice strain are expected to form in pure Ni. Moreover, the role of chemical disorder in this CSA is also investigated based on ab initio calculations using large supercells. Finally, to understand the impact of chemical complexity effect on defect structure evolution, this integrated research effort attempts to link the relatively large charge redistribution due to difference in valence electron counts resulting from alloying different 3d transition metal elements, moderate lattice distortion arising from similar adaptable atomic size, and notable suppressed or delayed damage evolution in NiFeCoCr.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Phase stability, mechanical properties, and ion irradiation effects in face-centered cubic CrFeMnNi compositionally complex solid-solution alloys at high temperatures

We report two CrFeMnNi face-centered cubic complex concentrated solid-solution alloys (CSA) have been evaluated for phase stability, mechanical properties, and radiation damage effects from heavy ions. Cr 18 Fe 27 Mn 27 Ni 28 and Cr 15 Fe 35 Mn 15 Ni 35 were predicted by thermodynamic calculations to phase separate and maintain a single phase at 700 °C, respectively. Aging experiments at this temperature confirmed varying degrees of precipitation of a body-centered cubic phase in both Cr 18 Fe 27 Mn 27 Ni 28 and Cr 15 Fe 35 Mn 15 Ni 35 . The alloys showed promising strength in tensile deformation at room temperature, with yield strengths of 155 MPa and 151 MPa for Cr 18 Fe 27 Mn 27 Ni 28 and Cr 15 Fe3 5 Mn 15 Ni 35 , respectively. At 500 °C, the yield strength of Cr 18 Fe 27 Mn 27 Ni 28 fell to 93 MPa, and to 100 MPa in Cr 15 Fe3 5 Mn 15 Ni 35 . Unlike Cr 18 Fe 27 Mn 27 Ni 28 , Cr 15 Fe 35 Mn 15 Ni 35 gained some ductility at 500 °C compared to room temperature. The two CSAs were irradiated to 75 dpa at 500 °C in the plateau region of the displacement curve using 3.7 MeV Ni 2+ ions, alongside model alloy 709 as a reference. Irradiation results produced similar densities and sizes of dislocations loops in the two CSAs compared to the reference. However, while large voids form in the plateau region of Cr 18 Fe 27 Mn 27 Ni 28 , small voids form just beyond the displacement peak of Cr 15 Fe 35 Mn 15 Ni 35 . Atom probe tomography and energy dispersive X-ray spectroscopy-equipped scanning transmission electron microscopes were used to characterize the alloys for changes in chemical distribution.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2021

Microchemical evolution of irradiated additive-manufactured HT9

The microstructural responses under 5 MeV Fe2 + single-ion-beam irradiation of three conditions of additive-manufactured (AM) HT9 steel using a powder-based directed energy deposition (DED) technique with and without postbuild heat treatments were investigated. Besides the observed dislocation loop formation and the absence of cavities at the irradiation condition of 50 dpa at 460 °C, Ni/Si/Mn-rich precipitates are found to form in all three conditions of AM-HT9, whereas Cu-rich clusters that arise from Cu uptake from the DED process are only observed in the heat-treated conditions, and not in the as-built (ASB) condition. Coprecipitation of the Cu- and Ni/Si/Mn-rich clusters occur near defect sinks such as line dislocations and grain boundaries in the heat-treated AM-HT9. The variation in microchemical evolution can be directly linked to the starting sink strength of the three AM-HT9 conditions, and the ASB condition with higher sink strength suppressed the responses observed in the postbuild heat-treated specimens.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2021

High radiation tolerance of an ultrastrong nanostructured NiCoCr alloy with stable dispersed nanooxides and fine grain structure

The present paper reports the irradiation behavior of nanostructured NiCoCr medium entropy alloy enhanced by Y-Hf-O nanooxides and fine grains produced by powder metallurgy. Ion beam irradiation to a peak dose of 130 dpa at 580°C produced neither detectable void swelling nor irradiation-induced hardening, in contrast to significant void swelling and property degradation of single phase NiCoCr concentrated solid-solution alloy under the similar irradiation condition. The dispersed nanooxides and high density of grain boundaries act as defect sinks that effectively annihilate irradiation-induced interstitials and vacancies. Furthermore, high-density nanooxides maintain their crystalline structures and stabilize the grain boundaries during irradiation.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Dislocation Loops in Proton Irradiated Uranium-Nitrogen-Oxygen System

Here in this study, we investigated the dislocation loop types formed in the proton-irradiated uranium-nitrogen-oxygen (U-N-O) system, which involves uranium mononitride (UN), uranium sesquinitride (a-U2N3), and uranium dioxide (UO2) phases. The dislocation loop formation is examined using specimens irradiated at 400°C and 710°C. Based on the detailed transmission-based electron microscopy characterization with i) the morphology-based on-zone and ii) the invisibility-criterion based two-beam condition imaging techniques, only a single type of dislocation loop in each phase is found: a/2?110?, a/2?111?, or a/3?111? dislocation loops in UN, a-U2N3, and UO2 phases, respectively. Molecular statics calculations for the formation energy of perfect and faulted dislocation loops in UN phases indicate a critical loop size of ~ 6 nm, above which perfect loops are energetically favorable. This could explain the absence of faulted loops in the experimental observation of the irradiated UN phase at two temperatures. This work will enhance the understanding of irradiation induced microstructural evolution for uranium nitrides as advanced nuclear fuels for the next-generation nuclear reactors.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2020

STEM Characterization of Dislocation Loops in Irradiated FCC Alloys

In this study, we demonstrate the methodology systematically developed for dislocation loop (perfect and faulted loops) imaging and analysis in irradiated face-centered-cubic (FCC) alloys using scanning transmission electron microscopy (STEM). On-zone [001] STEM imaging was identified as the preferred choice for its accuracy and effectiveness based on the comparison with other dislocation loop imaging techniques including: (i) on-zone STEM imaging using other major low-index zone axes, (ii) kinematic two-beam conditions bright field imaging near the [001] zone axis in conventional TEM (CTEM) mode, and (iii) Rel-Rod CTEM dark-field (DF) imaging near the [011] zone axis. The effect of STEM collection angle on the contrast formation of dislocation loops was also investigated. The developed method was confirmed by imaging all populations of perfect and faulted loops of types a/2$\langle$110$\rangle${110} and a/3$\langle$111$\rangle${111} found in an ion irradiated Ni40Fe40Cr20 alloy. The proposed STEM-based technique can easily identify said loops with a size greater than 10 nm without any assumptions such as those commonly made using the conventional Rel-Rod CTEM-DF technique. The recommended methodology in this study is developed as a quick and convenient tool that can be generally applied to irradiated FCC-based materials due to their common crystallography.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2020

Dislocation loop evolution and radiation hardening in nickel-based concentrated solid solution alloys

Effects of chemical composition, ion irradiation dose and temperature on unfaulting of irradiation induced Frank dislocation loops to perfect loops in two nickel based single-phase solid solution alloys, Ni–20Fe and NiFe–20Cr, have been studied. The fraction of Frank loops decreases with irradiation dose from 7.2 to 38.4 dpa at 500°C, but with more Frank loops remaining in the ternary alloy. However, perfect loops and dislocation networks become the dominant features of defects at 580°C in both alloys. The results indicate a thermally assisted loop unfaulting process that may be hindered by more sluggish defect motion in the alloy with more chemical components. Nano-indentation with both continuous stiffness method and single indentation method are used to measure radiation hardening. Loop unfaulting in both alloys irradiated at 580°C reduced radiation hardening while significant hardening is observed after irradiation at 500°C. The quasi-static single indentation method exhibits lower hardness results compared to continuous stiffness method, because dislocations induced from the cyclic loading in the latter method get relaxed and stabilized, resulting in higher resistance to the indenter.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Irradiation-Induced Extremes Create Hierarchical Face-/Body-Centered-Cubic Phases in Nanostructured High Entropy Alloys

A nanoscale hierarchical dual-phase structure is reported to form in a nanocrystalline NiFeCoCrCu high-entropy-alloy (HEA) film via ion irradiation. Under the extreme energy deposition and consequent thermal energy dissipation induced by energetic particles, a fundamentally new phenomenon is revealed, in which the original single-phase face-centered-cubic (FCC) structure partially transforms into alternating nanometer layers of a body-centered-cubic (BCC) structure. The orientation relationship follows the Nishiyama–Wasser-man relationship, that is, (011) BCC || (1¯1¯1) FCC and [100] BCC || [11¯0] FCC . Simulation results indicate that Cr, as a BCC stabilizing element, exhibits a tendency to segregate to the stacking faults (SFs). Furthermore, the high densities of SFs and twin boundaries in each nanocrystalline grain serve to accelerate the nucleation and growth of the BCC phase during irradiation. By adjusting the irradiation parameters, desired thicknesses of the FCC and BCC phases in the laminates can be achieved. Finally, this work demonstrates the controlled formation of an attractive dual-phase nanolaminate structure under ion irradiation and provides a strategy for designing new derivate structures of HEAs.

36 MATERIALS SCIENCE↗