NASA NTRS2005

Electroformed Nickel-Graphite Composite

Future x-ray astronomy will demand larger optics than Chandra, currently in orbit. Ways must be devised to produce cheaper and lighter x-ray mirrors to save the cost of manufacturing and launching this future telescope. One technique, being developed at Marshall Space Flight Center and elsewhere, is electroformed nickel replication technique, wherein mirror shells are electroformed (using pure nickel or a nickel alloy) onto super-polished and figured aluminum mandrels and are subsequently released by cooling. This technique can produce relatively inexpensive mirrors, but is hampered by the high density of nickel (8.9 g / cm3). An alternative is to develop a composite, with lower mass density and compatible mechanical properties to the nickel cobalt alloy, as the mirror shell material.

Xiong-Skiba, Pei↗

NASA NTRS2004

Electrocomposite of Alumina in Nickel Matrix

Nickel/aluminum oxide composite was electroformed in a sulfamate bath with 50 g/L of 0.05-micron aluminum oxide powder. Different plating methods including direct current plating, periodic pulse plating, and periodic reverse pulse plating were used. With conventional direct current plating, the maximum particle inclusion in the nickel matrix remains about 2% (wt). However, much higher percentile particle inclusions were achieved when a specific pulse reversal plating technique was applied. The particle incorporation approaches theoretical maximum when the deposit thickness per cycle approaches the particle diameter size at lower duty cycle. The highest particle incorporation achieved is 23% (by weight). Conceptual models interpreting the dramatic differences in the results of these plating methods were also proposed.

Xiong-Skiba, Pei↗