DOE OSTI2021

Morphology engineering of iridium electrodes via modifying titanium substrates with controllable pillar structures for highly efficient oxygen evolution reaction

Nowadays, Ti is the well-chosen anode substrate material for proton exchange membrane electrolyzer cells (PEMECs) and modifications of the substrate surfaces are essential for the fabrication of highly efficient electrodes. Herein, we introduce the morphology engineering of Ir/Ti electrodes with different acid treatments of hydrochloric acid (HCl) and oxalic acid (OA), and the comparative benefits of these two acid treatment methods are studied from the aspects of their impacts on the morphology, interfacial contact resistance (ICR), and oxygen evolution reaction (OER) performances of resultant electrodes. Notably, compared to the flat surface from OA treatment, Ti substrates with the pillar structure could be successfully achieved via HCl etching. Further, the HCl and the oxalic acid (OA) treatments would reduce the interfacial contact resistance (ICR) to 15.2% and 5.5% of the pristine Ti substrate at 1.38 MPa, respectively. By iridium electrodeposition on Ti substrates, Ir/Ti electrodes with different catalyst loadings are fabricated. With similar low-loadings of about 0.05 mgIr cm –2 , an Ir/Ti electrode with HCl treated substrate exhibits a lower overpotential of ~283 mV at 10 mA cm –2 current density than 305 mV from OA treatment, due to the boosted reaction areas from HCl treatment.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2021

An open-access database and analysis tool for perovskite solar cells based on the FAIR data principles

Large datasets are now ubiquitous as technology enables higher-throughput experiments, but rarely can a research field truly benefit from the research data generated due to inconsistent formatting, undocumented storage or improper dissemination. Here we extract all the meaningful device data from peer-reviewed papers on metal-halide perovskite solar cells published so far and make them available in a database. We collect data from over 42,400 photovoltaic devices with up to 100 parameters per device. We then develop open-source and accessible procedures to analyse the data, providing examples of insights that can be gleaned from the analysis of a large dataset. The database, graphics and analysis tools are made available to the community and will continue to evolve as an open-source initiative. This approach of extensively capturing the progress of an entire field, including sorting, interactive exploration and graphical representation of the data, will be applicable to many fields in materials science, engineering and biosciences.

14 SOLAR ENERGY↗

DOE OSTI2021

Insights into the rapid two-phase transport dynamics in different structured porous transport layers of water electrolyzers through high-speed visualization

In proton exchange membrane electrolyzer cells (PEMECs), maintaining efficient two-phase transport is one of the most important functions of porous transport layers (PTLs). To enhance the two-phase transport in PTLs, thin/titanium liquid/gas diffusion layers (TT-LGDLs) are introduced in PEMECs, and their difference from the conventional Ti felt PTLs are analyzed in-situ through high-speed and microscale visualization and electrochemical characterizations. The visualization results show that unfavorable large slugs can be greatly reduced in the PEMEC with a TT-LGDL compared to the PEMEC with a Ti felt PTL. More importantly, the recovery capability of water starvation with different PTLs is studied. After water starvation, the PEMEC with the TT-LGDL can recover the water starvation much more rapidly than the Ti felt cell, benefiting from its short and straight-through flow paths. Furthermore, the TT-LGDL tends to generate oxygen bubbles that are almost six times smaller and 236 times more frequently than the Ti felt PTL, indicating significantly boosted removal efficiency of produced oxygen and PEMEC performance. Finally, this study offers new insights into the dynamic processes of two-phase transport and the recovery capability of water starvation for different PTLs, which will provide valuable guidance for further optimization of PTLs and performance enhancement of PEMECs.

08 HYDROGEN↗

DOE OSTI2021

Engineered Thin Diffusion Layers for Anion-Exchange Membrane Electrolyzer Cells with Outstanding Performance

Anion-exchange membrane electrolyzer cells (AEMECs) are one of the most promising technologies for carbon-neutral hydrogen production. Over the past few years, the performance and durability of AEMECs have substantially improved. Herein, we report an engineered liquid/gas diffusion layer (LGDL) with tunable pore morphologies that enables the high performance of AEMECs. The comparison with a commercial titanium foam in the electrolyzer indicated that the engineered LGDL with thin-flat and straight-pore structures significantly improved the interfacial contacts, mass transport, and activation of more reaction sites, leading to outstanding performance. We obtained a current density of 2.0 A/cm 2 at 1.80 V with an efficiency of up to 81.9% at 60 °C under 0.1 M NaOH-fed conditions. The as-achieved high performance in this study provides insight to design advanced LGDLs for the production of low-cost and high-efficiency AEMECs.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2021

All-in-one bipolar electrode: A new concept for compact and efficient water electrolyzers

Highly compact and efficient proton exchange membrane electrolyzer cells (PEMECs) are strongly desired for commercializing hydrogen production. Here, a novel concept of all-in-one bipolar electrode (AIOBE) is proposed for high-efficiency and compact PEMECs with the help of 3D printing and sputtering coating. AIOBE ideally integrated catalyst layer (CL)/gas diffusion layer/bipolar plate/current distributor/gasket, which significantly reduced component quantity on the cathode side of PEMECs from 5 to 1, cut down on part weight and volume, and drastically accelerated the fabrication and maintenance processes. Moreover, AIOBE with the micro-scale flat surface and nano-scale rough CL provided an ultralow ohmic resistance (~100 mOhm cm 2 ) and a high catalyst utilization. Finally, AIOBE delivered a practical voltage of 1.62 V and a high energy efficiency of 91% at 1000 mA/cm 2 , and its mass activity (4.48 A/mg Pt ) was 14 times higher than conventional PEMECs. In conclusion, this work provides a new route for developing highly compact electrochemical devices, such as fuel cells, electrolyzers for N 2 reduction and CO 2 conversion, and many more.

3D printing↗

DOE OSTI2021

W-induced morphological modification of NiFe layered double hydroxides as efficient electrocatalysts for overall water splitting

Layered double hydroxides (LDHs) are one of the most efficient electrocatalysts for water splitting due to their nanosheet features and compositional flexibilities. This work explored the impact of W precursor concentration (0 ~ 10 mM) on LDH morphologies and performance in hydrogen production. Using an electrodeposition W-doping process, W-induced NiFe LDHs (NiFeW-LDHs) were in-situ grown on carbon fiber papers for water splitting. A performance peak was found at a W doping of 5 mM with well-aligned nanosheets, which not only boosted the charge transfer ability and gas evolution but also offered more than a four-fold electrochemical surface area increase compared to film-like NiFe hydroxides. The NiFeW-LDHs exhibited remarkable performance compared to NiFe hydroxides, showing decreased overpotentials of 31 mV and 114 mV for the oxygen evolution reactions (OERs) and hydrogen evolution reactions (HERs) at 10 mA/cm 2 and -10 mA/cm 2 , respectively, in alkaline media. The performance enhancement at 5 mM W-doping was linked to the well-aligned NiFeW-LDH nanosheets; smaller, less-textured nanosheets were observed with lower or higher W precursor concentrations (2.5 mM or >7.5 mM), leading to inferior OER and HER performances. Hence, an appropriate W doping is crucial to generating the morphologies that contribute to the higher performance of NiFeW-LDHs.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2021

Constructing Ultrathin W-Doped NiFe Nanosheets via Facile Electrosynthesis as Bifunctional Electrocatalysts for Efficient Water Splitting

Exploring cost-effective and efficient bifunctional electrocatalysts via simple fabrication strategies is strongly desired for practical water splitting. Herein, an easy and fast one-step electrodeposition process is developed to fabricate W-doped NiFe (NiFeW)-layered double hydroxides with ultrathin nanosheet features at room temperature and ambient pressure as bifunctional catalysts for water splitting. Notably, the NiFeW nanosheets require overpotentials of only 239 and 115 mV for the oxygen evolution reaction (OER) and hydrogen evolution reaction (HER), respectively, to reach a current density of 10 mA/cm 2 in alkaline media. Their exceptional performance is further demonstrated in a full electrolyzer configuration with the NiFeW as both anode and cathode catalysts, which achieves a low cell voltage of 1.59 V at 10 mA/cm 2 , 110 mV lower than that of the commercial IrO 2 (anode) and Pt (cathode) catalysts. Moreover, the NiFeW nanosheets are superior to various recently reported bifunctional electrocatalysts. Such remarkable performances mainly ascribe to W doping, which not only effectively modulates the electrocatalyst morphology but also engineers the electronic structure of NiFe hydroxides to boost charge-transfer kinetics for both the OER and HER. Hence, the ultrathin NiFeW nanosheets with an efficient fabrication strategy are promising as bifunctional electrodes for alkaline water electrolyzers.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2021

Favorable morphology and electronic conductivity of functional sublayers for highly efficient water splitting electrodes

Low electronic conductivities and improper morphologies of anode electrodes greatly limit the reaction area, catalyst utilization and efficiency in proton exchange membrane water electrolyzers. In this study, conductive sublayers with different conductivities and morphologies were introduced into anode electrodes in membrane-based water electrolyzers. In-situ and ex-situ investigation results showed that conductive sublayers (Au mesh and carbon nanotube (CNT) film) augmented the sheet conductivity of anode electrodes by up to 4000 times (from 2000 to 0.5 ohm square -1 ), and the ohmic resistance of water electrolyzers was reduced to 1/3 when inserting conductive sublayers. In addition, CNT film provided a higher electrochemical active area than Au mesh, because of favorable morphologies (large porosity and surface area) of CNT fibers on CNT films. Therefore, the current density of water splitting was increased by 3 times (from 4.55 mA cm -2 to 14.83 mA cm -2 ) at 2.5 V compared to a conventional anode electrode. Visualizations on bubble dynamics showed improved performances with conductive sublayers; this was mainly due to greatly increased number of reaction sites, highly spread reaction area (from 50 to 1000 um), and reduced activation overpotential. Therefore, a balance between high electronic conductivity and nanoporous morphology is essential to the anode electrode for larger reaction sites and areas in highly efficient water electrolyzers.

25 ENERGY STORAGE↗

DOE OSTI2021

High-speed characterization of two-phase flow and bubble dynamics in titanium felt porous media for hydrogen production

Bubble dynamics and two-phase flow phenomena are closely related to the performance of proton exchange membrane electrolyzer cells (PEMECs). This paper reports an in-situ study of the oxygen bubble behavior and associated multiphase evolutions in the anode side of PEMECs with titanium (Ti) felt liquid gas diffusion layers (LGDLs) by a high-speed visualization system. The micro oxygen bubble dynamics was captured and analyzed at different locations and virous operating conditions. The results show that the bubble detachment frequency and detachment diameter greatly increase with the operating current density. Additionally, they are significantly impacted by the local pore structure and morphology of Ti felt LGDLs. In the flow channels, there exist only several discrete micro bubbles at a low current density (0.04 A/cm 2 ) and a large flow velocity (133 mm/s). At a current density (0.2 A/cm 2 ) and a flow velocity (67 mm/s), a number of gas slugs are formed in the follow channels, in addition to discrete micro bubbles. At a high current density (1 A/cm 2 ) and a flow velocity (67 mm/s), more bubbles appear in the channel, and the flow field is dominated by slug or annular flows. These investigations can help to better understand the two-phase flow and bubble detachment mechanism, and provide a foundation for electrochemical reaction, multiphase flow studies and optimize the design of gas diffusion layers and flow fields for PEMECs in the future.

08 HYDROGEN↗

DOE OSTI2021

A simple convertible electrolyzer in membraneless and membrane-based modes for understanding water splitting mechanism

State-of-the-art membrane-based electrolyzers such as proton exchange membrane electrolyzer cells, are costly, susceptible to degradation, and time-consuming for electrode evaluation and triple-phase boundary electrochemical reaction studies. Here, a simple convertible electrolyzer in membraneless and membrane-based modes is proposed. For the first time, this enables comprehensive investigations of water splitting with pure water, acidic and alkaline electrolytes in one cell. With the simple electrolyzer and high-speed visualization system, the influences of flow rate, electrolytes, concentration, and Nafion membrane on the oxygen evolution reactions (OERs), hydrogen evolution reactions (HERs) and electrolyzer performance are comprehensively investigated. Visualization results reveal that water splitting only occurred at the edge between the electrode and the Nafion membrane in pure water. However, they occurred on the whole electrode surface in alkaline and acidic electrolytes, indicating easily tunable reaction sites with the convertible electrolyzer. This demonstrates the feasibility of using the simple convertible electrolyzer for understanding the water splitting mechanism. The relation between electrolyte thickness and resistances with different electrolytes is also quantified. This research provides an insight for optimizing electrochemical devices while delivering an inexpensive and fast way for electrode evaluations and electrochemical reaction studies.

25 ENERGY STORAGE↗

DOE OSTI2021

Ultrathin platinum nanowire based electrodes for high-efficiency hydrogen generation in practical electrolyzer cells

Significant reduction of noble metal catalyst loading and simplification of electrode fabrication are urgently needed in order to lower the cost of proton exchange membrane electrolyzer cells (PEMECs) for large-scale hydrogen production. Herein, we report an integrated electrode design comprising in-situ grown platinum nanowires (PtNW) on ultrathin titanium liquid/gas diffusion layers (LGDLs) via a cost-effective and green chemical synthesis approach. The ultrathin integrated PtNW electrodes showed a low cell voltage of 1.643 V and high efficiency of 90.08% at 1000 mA cm -2 using about 15 times lower catalyst loadings than a conventional catalyst-coated membrane in PEMEC tests. Ex-situ electrochemical characterizations and microscale visualizations further reveal that PtNW electrodes display highly efficient hydrogen evolution reactions and excellent electrode durability due to high active surface area, favorable bubble detachment, and structural stability. This work provides new insights into catalyst layer design and facile ultrathin electrode fabrication for more compact and low-cost PEM electrolyzers, fuel cells and other systems.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2020

Optimization of catalyst-coated membranes for enhancing performance in proton exchange membrane electrolyzer cells

To achieve large-scale application of proton exchange membrane electrolyzer cells (PEMECs) for hydrogen production, it is highly desirable to reduce the manufacturing cost while enhancing cell performance. In the PEMPECs, a catalyst-coated membrane (CCM) is the vital component where electrochemical reactions and mass transport mainly occur. The fabrication methods and catalyst layer (CL) structure can significantly affect the cell performance. Herein, for the first time, a comparative study of CCM fabrications with decal transfer and direct spray deposition methods have been conducted by both ex-situ materials characterization and in-situ performance testing in PEMECs. It is found CCMs that are fabricated with a direct spray deposition method display enhanced cell performance compared to CCMs fabricated with a decal transfer method, mainly due to the largely reduced ohmic resistance and improved mass transport. More importantly, cell performance can be greatly enhanced by simply regulating the Nafion ionomer content at the anode CL. The optimal Nafion ionomer content of 10 wt% gives the best cell performance at 80 °C with a low cell voltage of 1.887 V at 2 A cm -2 , outperforming the commercial CCM and most other previous publications. Our study provides a valuable guidance for fabrication and optimization of CCMs with significantly enhanced performance and reduced cost for practical application of the PEMECs.

08 HYDROGEN↗

DOE OSTI2020

Role of electron pathway in dimensionally increasing water splitting reaction sites in liquid electrolytes

Hydrogen from water splitting is one of the most promising alternatives for fossil fuels in solving the global energy crisis, while its electrochemical reaction mechanism, especially in liquid electrolytes, remains unclear. Herein, how the electrode conductivity affects the reaction sites of oxygen evolution reactions (OERs) in acidic and alkaline solutions was investigated by employing visualization system and electrochemical testing. Inserting Au nanolayers greatly increased electrode conductivities, improved OER kinetics and reduced cell ohmic resistance, leading to excellent water splitting performances in both acidic and alkaline electrolytes. Furthermore, the in-situ visualization results showed more reaction sites and higher catalyst utilizations were achieved by augmenting the electrode conductivity, and reaction sites increased from 1-dimension to 2-dimension. Additionally, it was discovered that electrical conductivities of acidic and alkaline solutions are insufficient to overcome the sharp drop of potential in the electrical double layer for activating OER uniformly on low-conductivity catalysts, indicating the importance of electrical conductivity of the electrode in acidic and alkaline water electrolyzers. This study provided a guidance on how to develop efficient and compact electrodes for acidic and alkaline water electrolyzer stacks and other electrochemical devices, such as fuel cell, N2 reduction, CO 2 conversion, etc.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗