Water-soluble polymer membrane insolubilized by transition-metal salt. Thin layer of lower permeability material joined with thicker layer of highpermeability material. Two layers chemically identical or chemically distinct. They differ in density, compactness or other respects. Used to purify or desalinate seawater, brackish water, or industrial or domestic wastewater.
The individual and combined effects of pasteurization temperature (347 K) and surfactants (anionic, cationic, and neutral) on a poly(ether/urea) thin-film hyperfiltration membrane were studied. Performance of this positively charged membrane was measured in terms of sodium chloride rejection and water flux. The observed effect was mostly on water flux and minimal on salt rejection. Pasteurization temperature caused an irreversible flux decline (flux decline slope of 0.09). The gradual flux reduction caused by neutral and cationic surfactants was reversible, whereas the flux reduction caused by anionic surfactant was irreversible and of similar magnitude to flux reduction caused by pasteurization temperature. The effects of anionic surfactant and pasteurization temperature were additive. Because of flux decline at elevated temperatures the poly(ether/urea) membrane is not very attractive for long-term spaceflight use.
A method for preparing water insoluble asymmetric membranes from water soluble polymers is discussed. The process involves casting a film of the polymer, partially drying it, and then contacting it with a concentrated solution of a transition metal salt. The transition metal ions render the polymer insoluable and are believed to form a complex with it. Optionally, the polymer is crosslinked with heat or radiation. The most preferred polymer is poly(vinyl alcohol). The most preferred complexing salt is copper sulfate. The process and the metal ion linked membranes are discussed. The membranes are reverse osmosis membranes.
A model waste based on a modest vegetarian diet is given, including composition and elemental analysis. Its use is recommended for evaluation of candidate waste treatment processes for a Controlled Ecological Life Support System (CELSS).
Polymeric membranes suitable for use in reverse osmosis water purification because of their high urea and salt rejection properties are prepared by generating a plasma of an unsaturated hydrocarbon monomer and nitrogen gas from an electrical source. A polymeric membrane is formed by depositing a polymer of the unsaturated monomer from the plasma onto a substrate, so that nitrogen from the nitrogen gas is incorporated within the polymer in a chemically combined form.
The abrasion resistance of plastic surfaces coated with polymerized organosilanes can be significantly improved by post-treatment of the polymerized silane in an oxygen plasma. For optical purposes, the advantages of this post-treatment are developed with a transparent polycarbonate resin substrate coated with plasma polymerized vinyltrimethoxysilane.
Plasma reaction chamber removes trace contaminants from spacecraft, submarines, and other closed environments by oxidizing contaminants to produce carbon dioxide and water. Contaminants are alcohols, esters, hydrogen sulfide, and ammonia. Others are lubricant solvents such as Freons, aromatics, and Ketones. Contaminants are removed from chamber by scrubber.
A radio frequency glow discharge reactor is described for removing trace oxidizable contaminants from an oxygen bearing atmosphere. The reaction chamber is defined by an inner metal electrode facing a dielectric backed by an outer conductive electrode. In one embodiment, a conductive liquid forms the conductor of an outer electrode and cools the dielectric. A resonator coupled to a variable radio frequency source generates the high voltages for creating a glow discharge in the chamber at a predetermined pressure whereby the trace contaminants are oxidized into a few simple non-toxic products that may be easily recovered. The corresponding process for removal of trace contaminants from an oxygen-bearing atmosphere with high efficiency independent of the concentration level is also disclosed.
Pressure and temperature are controlled precisely and water is rapidly removed to inhibit back reaction in process.
Calcium superoxide is prepared in high yields by spreading a quantity of calcium peroxide diperoxyhydrate on the surface of a container, positioning said container in a vacuum chamber on a support structure through which a coolant fluid can be circulated, partially evacuating said vacuum chamber, allowing the temperature of the diperoxyhydrate to reach the range of about 0 to about 40 C; maintaining the temperature selected for a period of time sufficient to complete the disproproriation of the diperoxyhydrate to calcium superoxide, calcium hydroxide, oxygen, and water; constantly and systematically removing the water as it is formed by sweeping the reacting material with a current of dry inert gas and/or by condensation of said water on a cold surface; backfilling the chamber with a dry inert gas; and finally, recovering the calcium superoxide produced.
Following plasma-polymerization technique, treatment in oxygen glow discharge further enhances abrasion resistance and transmission. Improvement in abrasion resistance was shown by measuring percentage of haze resulting from abrasion. Coating samples were analyzed for abrasion using standard fresh rubber eraser. Other tests included spectra measurements and elemental analysis with spectrometers and spectrophotometers.
The radiofrequency discharge, previously shown to oxidize trace levels of methane in oxygen, was studied with contaminated air at 50, 600, and 760 torr. As with oxygen, the concentration of methane traces could be reduced by several orders of magnitude, and no organic reaction products were detected in the effluent; however, substantial concentrations of NOx (0.1-6%) were formed during treatment. The concentration of NOx was decreased by using a large diameter electrode. There is evidence that the process will oxidize N2 and NO as well as organic impurities in oxygen or oxygen/inert gas atmospheres.
Low-temperature plasma polymerized coating improves light transmission through plastic lenses.