Structural and Optical Properties of High Entropy (La,Lu,Y,Gd,Ce)AlO 3 Perovskite Thin Films

Mixtures of Ce-doped rare-earth aluminum perovskites are drawing a significant amount of attention as potential scintillating devices. However, the synthesis of complex perovskite systems leads to many challenges. Designing the A-site cations with an equiatomic ratio allows for the stabilization of a single-crystal phase driven by an entropic regime. This work describes the synthesis of a highly epitaxial thin film of configurationally disordered rare-earth aluminum perovskite oxide (La 0.2 Lu 0.2 Y 0.2 Gd 0.2 Ce 0.2 )AlO 3 and characterizes the structural and optical properties. The thin films exhibit three equivalent epitaxial domains having an orthorhombic structure resulting from monoclinic distortion of the perovskite cubic cell. An excitation of 286.5 nm from Gd 3+ and energy transfer to Ce 3+ with 405 nm emission are observed, which represents the potential for high-energy conversion. These experimental results also offer the pathway to tunable optical properties of high-entropy rare-earth epitaxial perovskite films for a range of applications.

36 MATERIALS SCIENCE↗

DOE OSTI2022

3D-printed electrically conductive silicon carbide

The development of electrically conductive ceramics could achieve robust mechanical strength as well as practically high conductivity, offering applications in structural electrodes, conductors, catalyst supports, etc. However, its operating temperature is limited due to the intrinsic dense structures inevitably hindering the thermal management capability, thus resulting in a temperature-dependent electrical behavior in high-temperature environments. In this work, we report an additive manufacturing protocol through vat photopolymerization 3D printing to fabricate the architectured conductive silicon carbide (SiC) ceramics that simultaneously possess high electrical conductivity as well as low thermal conductivity, and demonstrate electric reliability under high-temperature environments above 600°C. The percolation of graphene into the ceramic scaffold establishes a uniform conductive network, exhibiting its electrical conductivity up to 1000 S m –1 . The bulk density of the 3D-printed ceramic is measured from 0.366 g cm –3 to 0.897 g cm –3 , with thermal conductivity ranging from 62 mW m –1 K –1 to 88 mW m –1 K –1 . Furthermore, the mechanical performance of conductive ceramic can be effectively reinforced by densifying the microstructures via spark plasma sintering treatment. The proposed additive manufacturing strategy widens the potential of ceramics as a structural and functional material, offering a promising pathway toward high-temperature electronics applications.

36 MATERIALS SCIENCE↗