Windes, William E. [Idaho National Laboratory (INL), Idaho Falls, ID (United States)] (ORCID:0000000188030885)

Publications and source records attributed to Windes, William E. [Idaho National Laboratory (INL), Idaho Falls, ID (United States)] (ORCID:0000000188030885).

4 records

All sources NASA NTRS DOE OSTI

DOE OSTI2025

Physical and thermal property changes under uniform oxidation in nuclear graphite

Material property changes of fine- and medium-grain nuclear graphite grades were measured after subjection to uniform oxidation. The cores of high temperature reactors are composed of large nuclear graphite block components. Here, these large core components are designed to provide neutron moderation and reflection, create a large thermal sink to assist in operational control, and form the solid core structure containing the nuclear fuel, coolant channels, and the safety critical channels for control rod insertion. Oxidation is a principle degradation mechanism affecting all aspects of the nuclear graphite component functions. This study addresses the underlying physical property changes of nuclear-graphite components for oxidized mass loss ranges beyond the current recommended ASME code rule limits to ensure structural integrity within the graphite components (a maximum mass loss = 10%).

11 - NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2025

Through-thickness fracture behavior of neutron-irradiated nuclear graphite NBG-17 Using X-ray micro-CT

Achieving precise control over crack propagation in nuclear graphite and conducting quantitative analysis remain challenging. In this study, the through-thickness fracture behavior of pristine and neutron-irradiated (700 °C, ∼7 dpa) NBG-17 nuclear graphite was investigated using split-disc testing coupled with micro-computed tomography (micro-CT). A notably lower number of micropores was observed in the neutron-irradiated specimen. The fracture toughness of neutron-irradiated NBG-17 was measured to be 1.45 MPa√m, compared to 1.17 ± 0.05 MPa√m for the pristine specimen. In both materials, cracks were found to initiate at the filler–binder interface, and often correlated with microstructural features such as pores and thermal cracks. Crack bridging and deflections emerged as the primary toughening mechanisms in both unirradiated and irradiated NBG-17. However, compared with the pristine specimen, the cracks in the neutron-irradiated specimen were more likely to grow trans granularly, resulting in less deflected crack paths. The reduced micro-porosity and strengthened filler–binder boundaries were considered to be the cause of the observed differences in crack morphologies. In conclusion, this study provides a qualitative analysis of the fracture behavior of neutron-irradiated nuclear graphite in the absence of radiolytic oxidation.

36 - MATERIALS SCIENCE↗

DOE OSTI2025

Graphite Oxidation Rate Study on ET-10 and ETU-10 Grades - Task 4: QA Support and Testing for Structural Graphite Oxidation

INL performed targeted oxidation tests to measure oxidation rates for samples of ET-10 and ETU-10 graphite under CRADA No. 21CRA22 Mod. 3, Annex A, “Tritium Testing to Support Kairos Power Advanced Reactor Demonstration” (04/02/2024). All testing was conducted within INL’s Carbon Characterization Laboratory (CCL) using test standard ASTM D7542-21 "Standard Test Method for Air Oxidation of Carbon and Graphite in the Kinetic Regime" [ASTM International, 2021]. Kairos Power provided all test specimens through its graphite vendor Ibiden, Inc. to INL and ASTM specimen specified dimensions. Information within this report only provides the Arrhenius oxidation rate plots as a function of temperature for each graphite grade tested. The raw mass loss per time data will be provided on the Nuclear Data Management and Analysis System (NDMAS) portal located on the INL information system.

36 MATERIALS SCIENCE↗

DOE OSTI2025

Influence of pre-existing defects on thermal transport in nuclear graphite

Nuclear graphite is a critical material in high-temperature nuclear reactors due to its superior thermal and mechanical properties. The manufacturing process leaves multi-scale ‘pre-existing’ defects that can affect thermal transport characteristics. Because these defects are remnant of graphitization temperature, they cannot be thermally annealed. This study employs a non-thermal electron wind force (EWF) annealing technique to avoid this obstacle. 2 min of EWF treatment of the as-received graphite IG-110 at temperatures below 100 °C led up to 67% increase in thermal diffusivity and ~ 35% decrease in electrical resistivity in average. Differential scanning calorimetry also showed similar outcome for specific heat. X-ray diffraction characterization was performed by fitting a bi-modal crystallite size distribution model to reveal the enhancement in crystallinity after the EWF treatment. The findings emphasize the potential of EWF annealing for optimizing thermal performance in nuclear graphite and its implications for reactor efficiency and safety.

Annealing↗