DOE OSTI2023

Determining the oxidation behavior of matrix graphite

This work presents the oxidation behavior of matrix graphite in air. Matrix graphite, graphite powder/flakes bonded by a small amount of non-graphitic carbon, surrounds coated fuel particles in order to form cylindrical fuel compacts (in prismatic core designs) or spheres (in pebble-bed reactor designs). This work focuses on oxidation tests conducted on two matrix graphite materials, one provided by Kairos Power and the other A3 matrix graphite. Some of the tests followed American Society for Testing and Materials (ASTM) oxidation testing standards using a vertical furnace system and others were performed in a thermogravimetric analyzer (TGA). It was determined that, at temperatures of 450 °C–700 °C, the oxidation rate of the Kairos matrix graphite follows the Arrhenius equation. In comparison with A3 matrix graphite, the Kairos matrix graphite shows better oxidation resistance at high temperatures (≥550 °C), but also a higher oxidation rate at low temperatures. Both the A3 matrix graphite and the Kairos matrix graphite materials may experience preferential oxidation of the partially graphitized binder. An oxygen penetration gradient was also observed when using the three characterization methods (i.e., optical microscope, x-ray tomography [XCT], and density profile by the lathe) enlisted in this research. In conclusion, the oxygen penetration depth increases with decreasing isothermal oxidation temperature, while the center of the oxidized samples (10% weight loss) remains almost untouched even at 500 °C.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2023

Summary of Vendor Irradiation Capsule Workshop Hosted at Oak Ridge National Laboratory, October 3-4, 2022

The Department of Energy office of Nuclear Energy, Advanced Reactor Technology office tasked Idaho National Laboratory (INL), and Oak Ridge National Laboratory (ORNL) with hosting a set of two workshops. The primary purpose of these workshops was to convince the commercial high temperature reactor community, specifically the graphite and composite experts, to collaborate with the building and operation of a graphite/ceramic composite irradiation capsule(s). The workshops were designed to first instruct the attendees on the technical and scheduling challenges in conducting such an experiment by providing information on different technical areas in scheduling, designing, building, operating, and disassembling such irradiation capsules. A secondary purpose was to determine the individual irradiation requirements (including the desired irradiated material properties) to understand what the remaining technical needs for gas-cooled and salt-cooled advanced nuclear reactors. The first workshop was held at ORNL October 3-4, 2022. This report summarizes the discussions held during this workshop. The second workshop was hosted at INL April 4-6, 2023 and will have a separate summary report.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗

DOE OSTI2023

GRAPHITE–MOLTEN SALT CONSIDERATIONS FOR COMPONENTS IN NUCLEAR APPLICATIONS

The new High Temperature Reactor (HTR) designs being considered for future Gen IV nuclear reactor deployment include designs utilizing molten salt as the primary coolant. These molten-salt cooled, graphite core designs pose new material compatibility challenges that are not considered within the gas-cooled HTR designs that have been previously built and operated. While the Molten Salt Reactor Experiment (MSRE) demonstrated that the molten salt can be considered chemically inert to graphite the novel physical and thermal interactions that the molten salt poses may be just as impactful as the chemical reactivity. Specifically, molten salt intrusion into the open pore structure of nuclear graphite grades can provide additional internal stresses within the microstructure exacerbating the stress buildup from irradiation induced dimensional change. Additionally, designs using a molten salt containing liquid fuel could provide “hot spots” within graphite structural components causing local thermal stresses. Abrasion and erosion concerns are magnified with molten salt due to the extremely high density of the salts (some have higher densities than the structural graphite components). Finally, the graphite-graphite and fuel pebble-graphite tribological behavior are distinctly difference within the molten salt from the inert gas environments and must be investigated. These topics and others are currently under investigation within the DOE Advanced Reactor Technologies (ART) graphite program and will be discussed in depth.

Gallego, Nidia↗