Atmosphere Effects in Laser Powder Bed Fusion: A Review

The use of components fabricated by laser powder bed fusion (LPBF) requires the development of processing parameters that can produce high-quality material. Manipulating the most commonly identified critical build parameters (e.g., laser power, laser scan speed, and layer thickness) on LPBF equipment can generate acceptable parts for established materials and moderately intricate part geometries. The need to fabricate increasingly complex parts from unique materials drives the limited research into LPBF process control using underutilized parameters, such as atmosphere composition and pressure. As presented in this review, manipulating atmosphere composition and pressure in laser beam welding has been shown to expand processing windows and produce higher-quality welds. The similarities between laser beam welding and laser-based AM processes suggest that this atmosphere control research could be effectively adapted for LPBF, an area that has not been widely explored. Tailoring this research for LPBF has significant potential to reveal novel processing regimes. This review presents the current state of the art in atmosphere research for laser beam welding and LPBF, with a focus on studies exploring cover gas composition and pressure, and concludes with an outlook on future LPBF atmosphere control systems.

70 PLASMA PHYSICS AND FUSION TECHNOLOGY↗
DOE OSTI2023

Investigation of the Effect of Chrome and Nickel Concentrations During Two-Piston Splat Quenching of Austenitic Stainless Steels

For solidification rates at or near equilibrium solidification conditions the effects of chrome (Cr) and nickel (Ni) on stainless steel solidification modes and microstructures are well detailed. However, fusion-based additive manufacturing (FBAM) processes that rely on faster, more rapid solidification rates call for a more in-depth understanding of the effects of rapid solidification on the solidification behavior and how these change with variations in alloy composition. Eleven custom stainless steel (SS) alloys with unique compositions based on 316L were made using targeted alloying element additions to generate feedstock with Cr/Ni eq ratios ranging from 0.9 to 2.1. Two-piston splat quenching (SQ) was used to produce rapid solidification conditions similar to those achieved in powder bed fusion processes in a fraction of the time and cost of traditional methods. Employing heat transfer simulations, SEM, TEM, and STEM characterization techniques, the SQ process was found to consistently produce solidification rates estimated to be between ~ 0.4 and 1.6 m/s. Five unique solidification microstructures were identified within the rapidly solidified SQ samples (primary austenite, massively transformed ferrite to austenite, primary austenite and massively transformed ferrite to austenite, primary ferrite, and primary ferrite and massively transformed ferrite to austenite). Both the primary ferrite solidification mode and primary ferrite phase were found to form at lower Cr/Ni eq values than previously predicted. SQ samples with compositions that were within the compositional specifications for 316L SS, an alloy which is commonly used in FBAM processes, demonstrated a wider range of potential solidification modes and microstructures that could form at rapid solidification rates than expected. Finally, by using SQ as a means to simulate rapid solidification conditions similar to those observed in FBAM processes, potential new alloy compositions can be screened faster and more cost effectively than purchasing and running test batches of the metallic powder.

36 MATERIALS SCIENCE↗
DOE OSTI2023

A Comparison of Solidification Structures and Submicroscale Cellular Segregation in Rapidly Solidified Stainless Steels Produced via Two-Piston Splat Quenching and Laser Powder Bed Fusion

Fusion-based additive manufacturing techniques leverage rapid solidification (RS) conditions to create parts with complex geometries, unique microscale/nanoscale morphological features, and elemental segregation. Three custom composition stainless steel alloys with varying chromium equivalence to nickel equivalence ratio (Cr eq /Ni eq ) between 1.53 and 1.95 were processed using laser powder bed fusion (LPBF) and/or two-piston splat quenching (SQ) to produce solidification rates estimated between 0.4 and 0.8 m/s. Both scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were utilized to collect high-resolution images, electron backscatter diffraction (EBSD) phase identification, and measure cellular segregation. Similar features were observed in both LPBF and SQ samples including phase and microstructure, nanoscale oxide particles, cell size, and segregation behavior. However, dislocation pileup was observed along the cell boundaries only in the LPBF austenite solidified microstructure. Targeted adjustment of the SQ feedstock Cr and Ni concentrations, within the ASTM A240 specification for 316L resulted in no observable impact on the cell size, oxide particle size, or magnitude of segregation. Also, the amount of Ni segregation in the ferrite solidified microstructures did not significantly differ, regardless of Cr/Ni eq or processing technique. Here, SQ is demonstrated as capable of simulating RS rates and microstructures similar to LPBF for use as an alternative screening tool for new RS alloy compositions.