Williams, Dustin

Publications and source records attributed to Williams, Dustin.

5 records

DOE OSTI2024

High Temperature Copper Metallization: Demand, Hurdles and Reliability

As newer cells structures come online, the pressing need to replace silver in the metallization pastes has renewed interest in alternative technologies employing base metals. Copper typically leads the charge with its abundance and lower cost but has faced numerous obstacles from relatively higher oxidation and diffusion rates which can damage the lifetime of the devices. In this study, a low-cost alternative to silver metallization pastes has been shown on PERC cells. The screen printable copper paste can be fired in air at temperatures >500 degrees C, and the impact of processing conditions and equipment on the performance and reliability of 274 cm2 cells have been evaluated. Through damp heat testing of micro-modules using 16 cm2 cells, routes that can lead to both the failure and success of durable contacts have been demonstrated.

copper↗

DOE OSTI2024

Exploring the Performance and Reliability of Screen-Printable Fire-Through Copper Paste on PERC Solar Cells

In this work, we present the performance and reliability of a fire-through copper (Cu) paste which has been screen printed on c-Si solar cell with passivated emitter rear contact (PERC). The Cu paste is fired through silicon nitride (SiN) anti-reflection coating at a peak temperature of 630 degrees C . SEM images of the Cu paste show a Cu core with ~200 nm oxide shell around the particles. This conductive oxide layer acts as a diffusion barrier between Cu and Si and prevents the degradation of cell performance during accelerated aging conditions. An efficiency of 19.250% has been achieved with Voc=654mV,FF= 76.68%, Jsc=38.40 m.A/cm 2 for champion PERC cells. Accelerated testing of the PERC mini-modules in damp heat chamber with 85 degrees C and 85% humidity have demonstrated that the devices are operational even after 1,500 hours. Devices with screen printed Ag contacts on the front side have been studied in parallel to the Cu contacts for comparison.

copper↗

DOE OSTI2024

Evaluating the Performance and Reliability of Screen-Printable Fire-Through Copper Paste on PERC Solar Cells

A bifacial silicon heterojunction solar cell demands approximately 210 mg usage of silver paste (9 busbars, 24.5%, bifacial, M6 size wafer). Copper is an excellent alternative to silver: 100x cheaper, similar elecvtrical resistivities, and 1000x more abundant. Successful demonstration of large area selective emitter PERC solar cells using Cu fire-through paste with FF approximately 75% and approximately 19%. Paste chemistry results in oxide-based Cu diffusion barrier, leading to good reliability of the devices: 1000h DHT giving a 3.5% efficiency drop. The additional series resistance still needs to be lowered. Printed and fired cell performance is governed mostly by pFF, especially J02 ; same for DHT degradation. Further improvement in printing and firing optimization for lower series resistance and higher FF.

Ag↗

DOE OSTI2024

Exploring the Performance and Reliability of Screen-Printable Fire-Through Copper Paste on PERC Solar Cells

For 40 TW of PV required to transition our planet to 100% renewables, the silver (Ag) should disappear from PV production. Advantages of copper (Cu) over silver (Ag) include 1) bulk Cu has a similar conductivity to Ag (1.7 mu O-cm for Cu, 1.6 mu O-cm for Ag) and 2) Cu is approximately 100 times cheaper than Ag, making it an excellent potential replacement. Problems associated with copper (Cu) contacts include 1) easy oxidation and 2) diffusion into the Si cell and recombination activity.

copper paste↗

DOE OSTI2024

Development and Reliability of Screen-Printable Fire-Through Cu Paste for Passivated Contact Solar Cells

We present the development of copper (Cu) paste which has been screen printed on Selective Emitter-Passivated Emitter Rear Contact (SE-PERC) solar cells. This paste can also be applied to Tunnel Oxide Passivated Contact (TOPCON) solar cells due to its fire-through nature. Champion PERC cells have achieved ....efficiency with ...parameters . Accelerated testing to investigate reliability performance of the SE- PERC mini-modules were carried out in damp heat chamber with 85oC and 85% humidity. The devices were found to be operational even after 1,500 hours. Devices with screen printed Ag contacts on the front side have been studied in parallel to the Cu contacts for comparison.

copper paste↗