Diffusional creep and creep degradation in the dispersion-strengthened alloy TD-NiCr

Dispersoid-free regions were observed in TD-NiCr (Ni-20Cr-2ThO2) after slow strain rate testing in air from 1145 to 1590 K. Formation of the dispersoid-free regions appears to be the result of diffusional creep. The net effect of this creep is the degradation of TD-NiCr to a duplex microstructure. Degradation is further enhanced by the formation of voids and integranular oxidation in the thoria-free regions. These regions apparently provided sites for void formation and oxide growth since the strength and oxidation resistance of Ni-20Cr is much less than Ni-20Cr-2ThO2. This localized oxidation does not appear to reduce the static load bearing capacity of TD-NiCr since long stress rupture lives were observed even with heavily oxidized microstructures. But this oxidation does significantly reduce the ductility and impact resistance of the material. Dispersoid-free bands and voids were also observed for two other dispersion strengthened alloys, TD-NiCrAl and IN-853. Thus, it appears that diffusional creep is charactertistic of dispersion-strengthened alloys and can play a major role in the creep degradation of these materials.

Whittenberger, J. D.↗
NASA NTRS1972

An observation of the effect of grain structure on the appearance of Kirkendall porosity.

Study of substitutional diffusion in thoriated and nonthoriated nickel alloys, particularly in several nominally Ni-20Cr-2ThO2:Ni type diffusion couples diffused at 1530 K. Upon metallographic examination, one DS-NiCr:Ni couple had negligible Kirkendall pore formation while the other couples contained significant porosity. It is believed that the difference in Kirkendall porosity is related to the unique grain structure of the particular lot of DS-NiCr used in this diffusion couple.

Whittenberger, J. D.↗
NASA NTRS1972

Diffusion in thoriated and nonthoriated nickel and nickel-chromium alloys at 1260 C

Various solid-solid diffusion couples were assembled from thoriated and nonthoriated nickel-base alloys, welded, and diffusion annealed at 1260 C. Concentration profiles indicated that a thoria dispersion does not affect diffusion in Cr(alloy):Ni and Ni-4.8Al:Ni types of couples unless a fine grain structure is retained by the thoria particles. Metallography revealed the presence of thoria-free bands in the thoriated-Ni side of the diffusion zone. The bands contained grain boundaries and, in some cases, non-Kirkendall porosity. A mechanism based on the operation of vacancy sources is proposed to explain the thoria-free bands. In addition, a particular DS-NiCr:Ni couple had negligible Kirkendall porosity. This behavior was related to the grain structure of the particular lot of DS-NiCr.

Whittenberger, J. D.↗