Cone formation as a result of whisker growth on ion bombarded metal surfaces

It is shown experimentally that the seed metals which can cause cone development on ion bombarded metal targets need not to have a lower sputtering yield as widely believed but rather a higher melting point. By lowering the bombarding ion energy to near sputtering threshold values (less than 100 eV) the growth of genuine single crystal whiskers which point in all directions not related to the direction of ion incidence is observed. It is concluded that (intentional or unintentional) seed cones are the result of an interplay among whisker growth, surface movement of atoms, and the effects of sputtering.

Wehner, G. K.↗
NASA NTRS1979

Mass effects on angular distribution of sputtered atoms

Sputtering metal targets at low ion energies (Hg or Ar at less than 300 eV) under normal ion incidence causes the lighter atoms (lighter isotopes or lighter elements of alloys) to be preferentially ejected in a direction normal to the target surface. Experimental results are shown for several elements and alloys at various bombardment energies. The amount of enrichment of the lighter species normal to the target surface decreases quite rapidly with increasing ion energy. The phenomenon is a result of reflective collisions because lighter atoms can be backscattered from heavier ones underneath but not vice versa. The effect provides an explanation of why solar-wind-exposed lunar material is enriched in the heavier isotopes, since sputtered lower-mass elements have a higher chance of achieving the lunar escape velocity.

Olson, R. R.↗
NASA NTRS1979

Whiskers, cones and pyramids created in sputtering by ion bombardment

A thorough study of the role which foreign atoms play in cone formation during sputtering of metals revealed many experimental facts. Two types of cone formation were distinquished, deposit cones and seed cones. Twenty-six combinations of metals for seed cone formation were tested. The sputtering yield variations with composition for combinations which form seed cones were measured. It was demonstrated that whisker growth becomes a common occurrence when low melting point material is sputter deposited on a hot nonsputtered high melting point electrode.

Wehner, G. K.↗