NASA NTRS2005

Atomic Oxygen Effects on Coated Tether Materials

The University of Alabama in Huntsville s Propulsion Research Center has teamed with NASA's Marshall Space Flight Center (MSFC) to research the effects of atomic oxygen (AO) bombardment on coated tether materials. Tethers Unlimited Inc. has provided several candidate tether materials with various coatings for (AO) exposure in MSFC's Atomic Oxygen Beam Facility. Additional samples were exposed to ultraviolet (UV) radiation at MSFC. AO erodes most organic materials, and ultraviolet radiation embrittles polymers. This test series was performed to determine the effect of AO and UV on the mechanical integrity of tether materials that were treated with AO-protective coatings, such as Photosil or metallization. Both TUI's Multi-Application Survivable Tether (MAST) Experiment and Marshall Space Flight Center's Momentum Exchange Electrodynamic Reboost (MXER) programs will benefit from this research by helping to determine tether materials and coatings that give the longest life with the lowest mass penalty.

Gittemeier, Keith A.↗

NASA NTRS2005

Simulated Space Environment Effects on Tether Materials with Protective Coatings

Atomic oxygen (AO) erodes most organic materials. and ultraviolet radiation embrittles polymers. A previous study indicated untreated polymers such as ultra-high molecular weight polyethylene (UHMWPE) are severely degraded when exposed to AO. This test series was performed to determine the effect of AO and UV on the mechanical integrity of tether materials that were treated with AO-protective coatings. Three coating systems were evaluated for their ability to protect the underlying material from AO erosion. The first coating system is the Photosil surface modification process which incorporates silicon-containing functional groups into the top micron of an organic material. The Photosil process has had favorable results with polyurethane- and epoxy-based thermal control coatings . The second coating system is metallization, in this case nickel. The third coating system is silsesquioxane. The Marshall Space Flight Center Atomic Oxygen Beam Facility (AOBF) was used to simulate low Earth orbit AO of 5 eV energy. In addition, some tether samples were exposed to ultraviolet radiation then evaluated for any changes in mechanical strength. Tether missions, such as a momentum-exchange/electrodynamic reboost (MXER) tether, may benefit from this research.

Finckenor, Miria M.↗

NASA NTRS2005

Space Environmental Effects on Coated Tether Materials

The University of Alabama in Huntsville s Propulsion Research Center has teamed with NASA's Marshall Space Flight Center (MSFC) to research the effects of atomic oxygen (AO) bombardment on coated tether materials. Tethers Unlimited Inc. has provided several candidate tether materials with various coatings for AO exposure in MSFC s Atomic Oxygen Beam Facility. Additional samples were exposed to ultraviolet (UV) radiation at MSFC. AO erodes most organic materials, and ultraviolet radiation embrittles polymers. This test series was performed to determine the effect of AO and UV on the mechanical integrity of tether materials that were treated with AO-protective coatings, such as polyhedral oligomeric silsesquioxane (POSS) or metallization. Both TUI's Multi-Application Survivable Tether (MAST) Experiment and Marshall Space Flight Center s Momentum Exchange Electrodynamic Reboost (MXER) programs will benefit from this research by helping to determine tether materials and coatings that give the longest life with the lowest mass penalty.

Gittemeier, Keith A.↗

NASA NTRS2005

Low Earth Orbit Environmental Effects on Space Tether Materials

Atomic oxygen (AO) and ultraviolet (UV) radiation erode and embrittle most polymeric materials. This research was designed to test several different materials and coatings under consideration for their application to space tethers, for resistance to these effects. The samples were vacuum dehydrated, weighed and then exposed to various levels of AO or UV radiation at the NASA Marshall Space Flight Center. They were then re-weighed to determine mass loss due to atomic oxygen erosion, inspected for damage and tensile tested to determine strength loss. The experiments determined that the Photosil coating process, while affording some protection, damaged the tether materials worse than the AO exposure. TOR-LM also failed to fully protect the materials, especially from UV radiation. The POSS and nickel coatings did provide some protection to the tethers, which survived the entire test regime. M5 was tested, uncoated, and survived AO exposure, though its brittleness prevented any tensile testing.

Finckernor, Miria M.↗