Au assisted smooth ultrathin epitaxial ZnO film grown by pulsed laser deposition on sapphire(0001)
High quality ZnO has applications in photonics and electronics. Literature has shown that continuous, but rough ZnO film can be grown on sapphire substrate by pulsed laser deposition (PLD). In this work, ZnO and Au were co-deposited by PLD on sapphire(0001) substrates from a single ZnO target overlaid with an Au strip that serves as a catalyst. The reflection high-energy electron diffraction (RHEED) patterns show paired double stripes from sample of ZnO-Au where the difference of in-plane lattice parameters between ZnO and Au is 11.4 %. The two-dimensional (2D) reciprocal space maps constructed from azimuthal RHEED (ARHEED) patterns reveal parallel epitaxial relationship between ZnO and Au in the continuous ZnO-Au film on sapphire substrate. Transmission electron microscopy (TEM) cross section images and energy dispersive spectroscopy maps show a minute amount of Au nanocrystals distributed in the entire ultrathin ZnO film. Atomic force microscopy shows the root-mean-square roughness of the surface of ultrathin ZnO film with Au is in the sub-nm range. The ARHEED and TEM results show that a couple of atomic percentages of Au co-deposited with ZnO catalyzes the growth of smooth ultrathin epitaxial ZnO film.