Engineering PapersSearch

Engineering topics

Wan, Liwen F. [Lawrence Livermore National Laboratory (LLNL), Livermore, CA (United States)]

Publications and source records attributed to Wan, Liwen F. [Lawrence Livermore National Laboratory (LLNL), Livermore, CA (United States)].

Atomic-scale vacancy engineering unlocks basal-plane catalytic activity in metallic WSe 2 for reversible oxygen electrocatalysis

Two-dimensional metallic transition metal dichalcogenides offer high electrical conductivity and large surface areas for electrocatalysis, yet their inherent basal planes are catalytically inert. Here, we present an atomic-scale vacancy engineering strategy to activate the basal surfaces of metallic WSe 2 for reversible oxygen electrocatalysis. This approach, based on intentionally designed substitutional metal doping, promotes the spontaneous formation of selenium vacancies while preserving the metallic 1 T′ phase, thereby creating highly reactive and oxygen-affinitive sites. Density functional theory calculations reveal that these vacancy-mediated metal complexes dramatically lower the energy barriers for initial oxygen adsorption, enabling dissociative oxygen adsorption. Operando and ex-situ spectroscopic analyses confirm that vacancy-mediated metal complexes transform into dynamic Se/W-oxide intermediates under operating conditions. Se/W-oxides on the surface experimentally and theoretically prove electrocatalytic activity and reversibility. Applying this strategy in lithium–oxygen batteries, the basal-plane activated WSe 2 shows high discharge capacities (9868 mA h g −1 , corresponding to 3947 mA h g$^{-1}_{cathode}$), impressive cycle retention over 550 cycles at 1000 mA h g −1 , and outstanding rate–capability over a wide current–density range (100–3000 mA g −1 ) during 256 cycles.

2D materials

Microstructure‐Dependent Sodium Storage Mechanisms in Hard Carbon Anodes

Sustainable energy storage is essential to support the transition to renewables and meet the increasing demand for energy. Sodium‐ion batteries (NIBs) are attractive for grid‐scale energy storage due to the abundance and low cost of sodium, sustainability of other battery components, and electrochemical performance. Hard carbon (HC) is a leading anode material for NIBs, but its complex microstructure complicates the understanding of sodium storage mechanisms. Using X‐ray total scattering and density functional theory calculations, this study clarifies how HC's microstructural variations influence sodium storage across the slope (high potential) and plateau (low potential) regions of the potential capacity curve. In the slope region, sodium initially adsorbs at high‐binding energy defect sites and subsequently intercalates between graphene layers, adsorbing at low‐binding energy defect sites, correlating with different slopes observed during initial sodiation. Initial irreversibility arises from sodium trapping at surface defects and solid electrolyte interface formation. In the plateau region, sodium simultaneously intercalates and fills pores, influenced by pore size, interlayer spacing, and defect concentration. HCs with larger pore sizes form larger sodium clusters. In conclusion, the proposed mechanism underscores the role of microstructure engineering in enhancing HC performance and advancing NIBs for grid‐scale energy storage.

36 MATERIALS SCIENCE