In-Situ Visualization of a Growing Brittle Crack in Aluminum Oxynitride Using Synchrotron X-Rays and the Double-Cleavage Drilled Compression Geometry

Brittle fracture is difficult to study in situ due to the speed of a growing crack and the often-catastrophic nature of failure in brittle materials. As a result, the influence of microstructural considerations, such as orientation, grain boundary locations, and strain field, on the crack path remains poorly understood. Presented in this study is a method addressing this knowledge gap, which utilizes the double-cleavage drilled compression geometry to achieve quasi-stable fracture in aluminum oxynitride (AlON). Synchrotron X-ray micro-computed tomography is used to characterize the crack shape and length, while high-energy diffraction microscopy provides information on the strains, orientations, and shapes of grains in the microstructure surrounding the crack tip. During testing, the crack grew in discrete and irregular jumps while the fracture toughness falls within reported ranges. The crack in AlON is found to have no greater tendency to crack intergranularly as compared to transgranularly, and grains which are cracked transgranularly do not display a trend in orientation or stress when compared to those around which the crack followed a grain boundary. The high resolution of the crack path and microstructural data provides a path forward for modeling and understanding 3D brittle fracture.

Gorske, Sara F.↗
DOE OSTI2022

Segmentation of tomography datasets using 3D convolutional neural networks

Dendritic microstructures are ubiquitous in nature and are the primary solidification morphologies in metallic materials. Techniques such as X-ray computed tomography (XCT) have provided new insights into dendritic phase transformation phenomena. However, manual identification of dendritic morphologies in microscopy data can be both labor intensive and potentially ambiguous. The analysis of 3D datasets is particularly challenging due to their large sizes (terabytes) and the presence of artifacts scattered within the imaged volumes. Here, in this study, we trained 3D convolutional neural networks (CNNs) to segment 3D datasets. Three CNN architectures were investigated, including a new version of FCDenseNet which we extended to 3D. We show that using hyperparameter optimization (HPO) and fine-tuning techniques, both 2D and 3D CNN architectures outperform the previous state of the art. The 3D U-Net architecture trained in this study produced the best segmentations according to quantitative metrics (intersection-over-union of 95.56% and a boundary displacement error of 0.58 pixels), while 3D FCDense produced the smoothest boundaries and best segmentations according to visual inspection. The trained 3D CNNs are able to segment entire 852 × 852 × 250 voxel 3D volumes in only ~60 s, thus hastening the progress towards a deeper understanding of phase transformation phenomena such as dendritic solidification.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Characterization and Accelerated Life Testing of a New Solid Oxide Electrolysis Cell

The project aims to develop mechanistic degradation models that realistically predict long-term Solid Oxide Electrolysis Cell (SOEC) durability, using input data from accelerated electrochemical life testing combined with quantitative microstructural and microchemical evaluation. A promising SOEC type will be further developed. The understanding achieved by combining experimental results and theory will be used to guide improvements in long-term SOEC durability, and validate that this technology can reach DOE H 2 production cost and durability targets. Planned outcomes include: (1) new experimental accelerated testing data on SOEC degradation at the oxygen electrode, fuel electrode, and electrolyte; (2) predictive theory of degradation developed based on the accelerated test data; (3) new electrode materials and processing methods that minimize degradation rate; (4) determination of the impact of SOEC electrolyte thickness and electrode composition/microstructure on performance and degradation; (5) determination of the operating conditions where degradation is minimized; and (6) validation of degradation models for extrapolating accelerated test data to predict long-term durability.

08 HYDROGEN↗
DOE OSTI2021

Migration of inclusions in a matrix due to a spatially varying interface energy

An interfacial energy can be a function of a bulk field such as temperature or electric field. Here we find that in a system with a gradient in temperature or electric potential, the resulting variation in interfacial energy can induce a particle to migrate by either surface or bulk diffusion. For a circular particle under a constant unidirectional gradient in the bulk field, the field dependence of the interfacial energy induces a circular particle to move as a circle at a constant velocity along the direction from higher to lower interfacial energy. A linear stability analysis of this steady state migration suggests that perturbations will damp out as time evolves, and thus under these conditions a migrating circular particle is morphologically stable. Other spatial distributions of interface energy can lead to the distortion of an initially circular shaped particle during migration. A phase field model is developed that captures these distortions and verifies the theoretical results mentioned above.

36 MATERIALS SCIENCE↗
DOE OSTI2020

On the role of the zirconia/ceria interface in the degradation of solid oxide electrolysis cells

Gd-doped Ceria (GDC) barrier layers are widely used in solid oxide electrolysis cells to prevent reactions between the Y-stabilized Zirconia (YSZ) electrolyte and oxygen electrode. In some cases, electrolysis operation causes fracture near the GDC/YSZ interface. Here, we explain this effect using a numerical calculation, showing that a peak oxygen pressure is observed near the GDC/YSZ interface during electrolysis operation. Moreover, GDC/YSZ interdiffusion and possible zirconate phase formation occurring during electrode firing yield a low oxygen ion conductivity region that introduces a much higher peak oxygen partial pressure at the interdiffusion layer/YSZ interface, thereby exacerbating degradation. The results indicate that the peak pressure can be reduced and, thereby, damage can be mitigated by altering processing in order to minimize interdiffusion, decreasing the GDC layer thickness, and reducing oxygen electrode polarization resistance or altering electrolyte transport properties, e.g., changing the Gd doping level of GDC to increase the oxygen vacancy diffusivity.