Hydrogen uptake in graphite matrix at high temperature
Tritium management is a critical challenge for the next generation of nuclear reactors, such as Fluoride Salt Cooled High Temperature Reactors (FHRs) and High Temperature Gas-cooled Reactors (HTGRs), due to the higher production rate (up to 10,000 times) than conventional Light Water Reactors (LWRs). Graphitic materials employed as moderator, reflector, and fuel pebbles offer a potential pathway for tritium recovery by serving as a sink for tritium. Prediction of uptake capacity under reactor relevant conditions remains a challenge due to a lack of low partial pressure data and significant inter-grade variability of graphite. This study addresses these gaps by providing a comprehensive characterization of hydrogen (as a tritium surrogate) uptake and release behavior in the A3-3 graphite matrix (GM) used in fuel pebbles. Uptake measurements are performed at reactor relevant temperatures of 600- 800 °C, 1-200 Torr hydrogen pressure, and 15-120 min equilibration time, followed by thermal desorption spectroscopy up to 1100 °C. Uptake experiments at different equilibration times demonstrate the role of kinetics in hydrogen uptake, which can be modeled as a diffusion-with-trapping process. In the thermodynamics limit, the Sips adsorption model is shown to capture the uptake in A3-3 GM well. Our campaign provides a set of new results for hydrogen uptake in A3-3, including limiting uptake capacity at 600 °C, apparent diffusion coefficient at 600 °C, and the first estimates of the FHR/HTGR relevant (600 °C, 20 Pa partial pressure) equilibrium uptake capacity and time to saturation. Desorption data highlights a new site for hydrogen uptake, not observed in nuclear graphite, which we attribute to the non-graphitized binder. Using the Kissinger method, we estimate activation energy for release from the desorption peaks, confirming the activation energy for release from the basal planes and providing the first estimate for the activation energy of release from the binder.